The following creep data were taken on an aluminum alloy at 480 °C and a constant stress of 2.75 MPa. Plot the data as strain versus time, then determine the steady-state or minimum creep rate. Note: The initial and instantaneous strain is not included. Time (min): 0 2 4 10 12 14 16 18 20 22 24 26 28 30 32 34 Strain: 0 0.22 0.34 0.41 0.48 0.55 0.62 0.68 0.75 0.82 0.88 0.95 1.03 1.12 1.22 1.36 1.53 1.77

The following creep data were taken on an aluminum alloy at 480 °C and a constant stress of 2.75 MPa. Plot the data as strain versus time, then determine the steady-state or minimum creep rate. Note: The initial and instantaneous strain is not included. Time (min): 0 2 4 10 12 14 16 18 20 22 24 26 28 30 32 34 Strain: 0 0.22 0.34 0.41 0.48 0.55 0.62 0.68 0.75 0.82 0.88 0.95 1.03 1.12 1.22 1.36 1.53 1.77

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resilience
The creep data have been taken on an ahuminum alloy at 400°C and constant stress of 25MPA are shown in below Table, Find the steady state or minimum creep rate. Time (min) strain Time (min) 16 strain 0.135 0.0 0.0 2 0.025 18 0.153 4 0.043 0.065 20 0.172 0.193 0.218 22 0.078 24 10 0.092 26 0.255 12 0.109 28 0.307 14 0.120 30 0.368
4) In the temperature range from 600°C to 750°C, a steel wire with 100 mm length shows the steady state creep behavior. The wire was exposed to 600°C under 300 MPa for ten years, how long the specimen would be? ( TH Trung Trong Stress (MPa) 1000 FTTinh Tru Trung Trung Trong th 800 600 400 200 100 80 60 40 815 C 20 d 10-6 104 10-5 650 C 730 C 925°C d d d d d 10-3 10-2 10-1 1 10 10² Steady-state creep rate (h-¹) 10³
Determine the percentage of ductility of a metal alloy having the following tensile stress-strain diagram. Tensile stress-strain diagram 450 400 350 300 250 200 150 100 NO 50 0.05 0.1 0.15 0.2 0.25 0.3 0 35 0.4 Strain 300 EN Stress (Mpa)
Question 2 Figure 2 shows the dependence of fatigue strength on testing cycles (S-N curve) of an acetal polymer. 60 50 40 30 20 10 104 105 106 107 108 Number of cycles to failure Figure 2 The S-N fatigue curve for an acetal polymer a. What is the fatigue strength, or maximum stress amplitude, at one million cycles of loading? b. An acetal polymer 30-cm-long bar with a diameter of 20 mm is designed to survive one million cycles of loading, what is the maximum allowable axial load that can be applied on one end of the bar? Magnitude of stress Reversal, MPa
1. Suppose that you have measured the strain aging kinetics of a high-strength low-alloy (HSLA) steel and obtained the following results: Aging Temperature (°C) Aging Time (min) ΔΥ (MPa) 150 240 40 130 1800 40 Determine (using a mathematical rather than graphical approach) the time necessary to obtain a strengthening increment, AY, of 40 MPa at an ageing temperature of 120°C. State any assumptions made in order to arrive at your approximation.
8.35 Steady-state creep data taken for a stainless steel at a stress level of 70 MPa (10,000 psi) are given as follows: T(K) 10x 10 2.5 x 10 977 1089 If it is known that the value of the stress exponent n for this alloy is 7.0, compute the steady-state creep rate at 1250 K and a stress level of 50 MPa (7250 pst).
3. A cylindrical specimen of cold-worked copper has a ductility, %EL. If its cold-worked radius is d, what was its radius before deformation? Use %EL=25%; d = 10mm Ductility (%EL) 70 60 50 40 30 20 Brass 1040 Steel 10 Copper 0 0 10 110 20 30 40 50 60 70 Percent cold work