Question 4. A tensile test is carried out on a bar of mild steel of diameter 2 cm. The bar yields under a load of 80 Kn. It reaches a maximum load of 150 kN, and breaks finally at a load of 70 kN. Estimate: a)the tensile stress at the yield point b)the ultimate tensile stress c)the average stress at the breaking point if the diameter of the fractured neck is 1 cm.

Question 4. A tensile test is carried out on a bar of mild steel of diameter 2 cm. The bar yields under a load of 80 Kn. It reaches a maximum load of 150 kN, and breaks finally at a load of 70 kN. Estimate: a)the tensile stress at the yield point b)the ultimate tensile stress c)the average stress at the breaking point if the diameter of the fractured neck is 1 cm.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: A punch of 20 mm diameter is used to punch a hole in 8 mm thick plate. If the force required to…

A: Here, We need to calculate the average shear stress on the plate. diameter = 20 mm thickness = 8 mm…

Q: 2. A metal plate is .125 inch thick. What force is required to punch out a square piece 1" x 1"? Th…

A: Thickness of metal plate is 0.125 inch Size of square piece is 1''×1'' The ultimate shear stress of…

Q: For a specimen of a steel alloy with a plane strain fracture toughness of 80 MPa√m, fracture results…

A: Given KIC=80MPamσ=510MPaa=6mm Consider the formula KIC=Yσπa80=Y×5103.14×6Y=0.036

Q: Determine : 1. Soil classification of soil A using AASHTO method. 2. Soil classification of soil B…

A: 1. Soil A according to AASHTO: The AASHTO classification chart is shown below: Given data, Passing…

Q: A tension test for a steel alloy results in the stress-strain diagram shown in Figure. Calculate the…

A: Consider the graph,

Q: The stress field in a loaded aluminum plate was determined as [-2x² + 3y² 3x + y+ 5] O = F[3x + y+5…

Q: Determine the following: a. Young's modulus within the linear portion b. Tangent modulus at a stress…

A: a).Young's Modulus : At the proportional limit, stress is directly proportional to strain stress α…

Q: 2. The Goodman diagram relates oa and om for fatigue failure after a specific number of cycles N₁,…

A: Given, Fatigue strength under zero mean stress , σa(0) = 0.45 σTS Tensile strength, σTS = 375…

Q: A 3m-long, thin-walled section (thickness t = 4 mm, for all elements) is used as a cantilever to…

A: “Since you have asked multiple questions, we will solve the first question for you. If you want any…

Q: A tensile test specimen of stainless steel alloy having a diameter of 0.550 in. and a gage length of…

Q: A hole is to be punched through a steel plate of 8 mm thickness. What is the least diameter of hole…

A: given steel plate thickness=8 mmcompressive stress=800 N/mm2ultimate shear strength=300 N/mm2

Q: Prob- In a tensile test carried out in the laboratory on a steel specimen for 5 minutes. The strain…

A: given- strain=0.30time=5 mintues

Q: A very large, steel plate of yield stress 200 MPa and Poisson's ratio 0.3 has a crack at the centre…

A: To determine the extent of plastic region at Crack tip : For plastic region we have,…

Concept explainers

Material Properties

Construction in civil engineering demands high strength, durability, and longevity. These targets can be achieved by better design and analysis, along with the correct choice of materials. Different materials have different properties and hence, they respond and performs differently under the various condition of external loadings. It is therefore a critical task of an engineer to select the right material based on the property that the material is supposed to function in real-time. When speaking about the property, there are different categories of material properties like chemical property, physical property, mechanical property, electrical property, magnetic property, thermal property, etc. These material properties form the basis of material selection in various applications.

Question

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Calculate the stress and strain at each force interval. Plot a graph of the stress-strain curve. Estimate the yield point of the steel and note its location on the curve. Estimate the ultimate strength of the steel and note its location on the curve.
th
A 13 mm diameter tensile specimen has 50 mm gauge length. If the load corresponding to the 0.2% offset is 6800 kg, the yield stress will be nearly 1. 31 kg/mm² 2. 43 kg/mm² 3. 51 kg/mm² 4. 63 kg/mm² X
(c) A piece of material is subjected to tensile stress of 70 N/mm² in one direction and a compressive stress of 50 N/mm² in a direction at right angles to the previous one. Find fully the stresses on a plane the normal of which makes an angle of 40 degree with the 70 N/mm² stress.
The aluminum bar ACDB is rigidly connected to a steel tube in CD. The data is presented in the table. If the load P is equal to 125 kN, determine: The stress of aluminum in segment AC. Answ: 63.66 MPa The stress of aluminum in segment CD. Answ: 13.93 MPa The stress in steel in segment CD. Answ: 39.79 MPa The total deformation of the bar. Answ: 0.29273 mm
A certain steel has proportionality limit of 300 N/mm² in simple tension. Under a Three Dimensional Stress System, the principal stresses are 150 N/mm² (Tensile), 75 N/mm² (Tensile) and 30 N/mm² (Compressive), μ = 0.3. The factor of safety according to maximum shear stress theory would be
A hollow steel cylinder 3.5m which has an inside diameter and outside diameter of 55mm and 35mm. If the steel carry a load (Your Registration Number ie 1 to 63) KN find the stress in the cylinder also find the deformation in the cylinder if the Modulus of Elasticity is 90 GPA.
As shown, an aluminium alloy construction BCD with a circular cross section is fixed at end B and affected by a force of 150 N at the free end D. The diameter of the cross-section a-a is 20 mm. The yield strength of the material is 80 MPa: a) Determine the stresses at point A of the a-a cross-section. As indicated in the picture, draw the stress element in Cartesian coordinates and specify the stress values.(b) Calculate the factor of safety, n for Tresca, and the von Mises yield criterion to see if the structure would yield based on the stresses at point A.(c) In the major stress area, draw the yield loci of both criteria and indicate the operational stress state & why is the Rankine failure criterion inappropriate for aluminium alloys?
Calculate true strain ASAP
A very large, steel plate of yield stress 200 MPa has a crack at the centre of length 18 mm, orientated along the x-axis. If the plate is subjected to far field tensile loading of magnitude 179 MPa and is assumed to be in a state of plane strain, determine the extent of the plastic region at the crack tip, along the x-axis. You may assume Poisson's ratio is (1/3). Express your answer as an integer value of mm.
A brass specimen of the circular cross-section is fractured at 151 kN force and the final length of the specimen at fracture is 48 mm. The fracture strength of the specimen is found to be 72 kN/mm?. The percentage of elongation of the specimen is 44 %. Determine the following (i) Diameter of the specimen, ii) Initial length of the specimen, iii) Stress under an elastic load of 15 kN, iv) Young's Modulus if the elongation is 1.5 mm at 15 kN (v) Final diameter if the percentage of reduction in area is 21 %. ( Initial Cross-sectional Area (in mm?) The Diameter of the Specimen (in mm) Initial Length of the Specimen (in mm) Stress under the elastic load (in N/mm?) Young's Modulus of the Specimen (in N/mm2) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)
A steel specimen is tested in tension. The specimen is 1" wide by 0.5" thick in the test region. By monitoring the stresses from the testing machine, it was found that the specimen yielded at a stress of 72 ksi and fractured at 96 ksi. (a). Determine the tensile loads at yield and at fracture