Metal A melts at 1400°C, Metal B melts at 600C. Thermal arrest data is obtained from cooling curves for the alloy of AB and is shown below %A O 10 20 30 50 60 80 90 100 1st Point 600 700 860 960 1140 1220 1320 1370 1400 2nd Point 600 630 690 760 910 1000 1160 1280 0 Determine (i) plot and label the equilibrium diagram(ii) for an alloy containing 50% of A and 50% B state(a) solidification commencing temperature(b) solidification ending temperature(c) percentage of solid &liquid

Metal A melts at 1400°C, Metal B melts at 600C. Thermal arrest data is obtained from cooling curves for the alloy of AB and is shown below %A O 10 20 30 50 60 80 90 100 1st Point 600 700 860 960 1140 1220 1320 1370 1400 2nd Point 600 630 690 760 910 1000 1160 1280 0 Determine (i) plot and label the equilibrium diagram(ii) for an alloy containing 50% of A and 50% B state(a) solidification commencing temperature(b) solidification ending temperature(c) percentage of solid &liquid

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

(a) Sketch a Pressure-Temperature phase diagram for a pure substance X where liquid X is less dense than solid X. Insert an isobar at 1 atm and an isotherm at 300 K. Clearly label all physical states, triple point, critical temperature and any normal transition temperatures.
In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.
An FCC iron-carbon alloy initially containing 0.15 wt% C is carburized at an elevated temperature and in an atmosphere wherein the surface carbon concentration is maintained at 1.0 wt% C. If after 49.5 h the concentration of carbon is 0.35 wt% C at a position 4.0 mm below the surface, determine the temperature in degree Celsius (°C) at which the treatment was carried out. O 1303 C 1094 C 1050 C 1388 C O 1022 C O 1700 C
For alloys of two hypothetical metals A and B, there exist an α, A-rich phase and a β, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Alloy Composition Fractionα Phase Fractionβ Phase 60 wt% A - 40 wt% B 0.57 0.43 30 wt% A - 70 wt% B 0.12 0.88 (a) α phase ________ wt% A (b) β phase ________ wt% A
Q/ The phase present for a 30 wt% sn, 7O wt% pb of alloy at 200°c is (a+ L) Determine: Composition of (a) and (L) for both (sn) and (pb). * 327°C 300E Liquid 232°C a +L 200E B + L 183°C 18.3 61.9 97.8 100 a +B 20 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Ca =18 Wt% pb, CL=58 Wt% pb and Ca =82 Wt% Sn, CL=42 Wt% Sn. Ca =20 Wt% pb, CL=60 Wt% pb and Ca =80 Wt% Sn, CL=40 Wt% Sn. Ca =22 Wt% pb, CL=65 Wt% pb and Ca =78 Wt% Sn, CL=35 Wt% Sn. Ca =15 Wt% pb, CL=63 Wt% pb and Ca =85 Wt% Sn, CL=73 Wt% Sn. Temperature ("C)
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Consider the binary alloy phase diagram shown schematically below. The left-hand side denotes phase a, and the right-hand side the phase ß. The intermediate region is a coexistence regime with both a and ß phases. The three points 1, 2 and 3 in the coexistence region are at 22.8 wt% A, 28.2 wt% A, and 33.7 wt % A respectively. If the points on the phase boundaries L and R are at 20 wt% A and 39 wt % A, respectively, what is the fraction of a phase at 1, 2 and 3? (This question has only one correct answer) T(°C) A-B binary alloy 1400 Coexistence region 3 1 2 1100 B 20 % 40 % Weight % A
16. (Solution Needed) An unknown compound is at 200°C and 1 MPa. What is the maximum number of phases that could be present? d. not possible to specify both temperature and pressure а. b. 1 е. 3 с. 4
Calculate the work done (in J/mol) for mechanically reversible, isothermalcompression if 1 mol of methyl chloride undergoes a pressure change from 1 bar to 60 bar at 125 ℃. The species follows the virial equation of state ? = 1 +??b. Determine the molar volume (in cm3/mol) of n-heptane at 535 K and 25 bar basedon the generalized compressibility factor correlation. c. Estimate the density (in g/cm3) of saturated liquid ammonia at 320 K.
Q.4) For 30 wt% Sn - 70 wr% Pb alloy at 125 °C, (a) what phases are present? (b) What are the compositions of the phases? (c) Calculate the relative mass fraction of each phase present. Composition (at% Br 100 80 60 40 20 A 3270 Temperature (C) 300 200 100 0 0. (Pb) Solvus Solidu a+L B 18.3 20 liquidus Liquid 183 C 61.9 40 60 Composition (wt% Sn) 80 L 232 C G 97.8 1 600 500 P 400 (3) angesadway 300 200 H 100 100 (Sn)
A diffusion process has reached equilibrium. This means that MARK ALL CORRECT ANSWERS the flow is equal in both directions. O the entropy has decreased. all flow has stopped. O the concentration gradient is zero.
In this Sn-Pb alloy system, what is the relative percentage of proeutectic alpha phase after alloy 2 is cooled down from 300 °C to room temperature? Alloy 2 Alloy I 327 Solidus Liquidus 300 Liquid Liquidus 250 a + liquid Solidus 200 B+ liquid 183 Eutectic point 150 Solvus +B 100 Solvus 50 19.2 40.0 61.9 97.5 li 60 10 20 30 40 50 70 80 90 100% 100% Weight percent tin Sn Pb O1. 73% O II. 51% O II. 49% O IV. 27% Temperature (C),