It is intended to determine what type of white pigment has been used as a colorant in a thermoplastic. A pulverized sample is examined with RX diffraction, Cu Kα radiation was used from λ = 1.541A°. A diffraction spectrum with 3 reflections was obtained at 2θ = 31.72Ao, 57.73Ao and 39.12Ao. Ao: Angstrom Determine the type of pigment used

It is intended to determine what type of white pigment has been used as a colorant in a thermoplastic. A pulverized sample is examined with RX diffraction, Cu Kα radiation was used from λ = 1.541A°. A diffraction spectrum with 3 reflections was obtained at 2θ = 31.72Ao, 57.73Ao and 39.12Ao. Ao: Angstrom Determine the type of pigment used

Similar questions

Problem 3. A 1mm filament produces a 1mm × 1mm electron beam incident on an anode disk with anode angle = 13°.The center of the focal spot is 1 m away from a detector which is centered at the center of the focal spot on the anode disk and is 50 cm wide. Determine the effective focal spot dimensions on the disk and the dimensions of the focal spot in the center of the detector, at the far anode edge of the detector, and at the far cathode edge of the detector (see figure below which is definitely not to scale). 1 m աալ 0 40 cm
Tungsten is a very high density, high melting point, and hard metal. These properties are partially due to its body centered cubic (BCC) crystal structure. Tungsten has an atomic number of 74 and an average mass of 183.8u. (1u = 1.661x10-27 kg). X-ray diffraction experiments determine that the Bravais lattice has a characteristic length of 3.155 Å (This means each side of the cube shown below has a length of 0.3155 nm.) How many complete tungsten atoms are there in each BCC unit cell?
Atomic sodium produces two prominent spectral lines at 588.995 nm and 589.592 nm. Find the angular separation between these lines when observed in third order using a spectrometer with 2100 lines per cm. Include proper units.
A ray of white light traveling through air enters a triangular prism that has an index of refraction of 1.319 for the red end of the spectrum and 1.34 for the violet end and an apex angle of 69 degrees. If the ray has an angle of incidence of 55degrees with respect to the normal of the interface boundary, what is the angular separation between the red and violet ends of the spectrum within the prism? Measure this in degrees to 3 decimal places.
8) (a) Show that if the crystal undergoes volume expansion, then the reflected beam is rotated by the angle: 80 =-.tan0.8T, where ß is the volume coefficient of expansion, T is the temperature and the Bragg angle. (b) The Bragg angle for a certain reflection from a powder specimen of Cu is 47.75° at a temperature of 293 K and 46.60° at 1273 K. Calculate the coefficient of linear thermal expansion of Cu (Use the angle in radian).
The index of refraction of silicate flint glass for red light is 1.620 and for violet light is 1.660 A beam of white light in this glass strikes the glass-air interface at a 20.10° angle of incidence and refracts out into the air. What is the angular separation between the red and violet components of the spectrum that emerges from the glass? angular separation: 0.2995 Incorrect
1. A helium-neon laser, radiating at 632.8 nm, has a power output of 3.0 mW. The beam diverges at angle 0.17 mrad as in fig 1. (a) What is the intensity of the beam 40m from the laser? (b) What is the power of a point source providing that intensity at that distance? Laser Figure 1: Helium neon laser
A ray of white light traveling through air enters a triangular prism that has an index of refraction of 1.512 for the red end of the spectrum and 1.539 for the violet end and an apex angle of 64.1 degrees. If the ray has an angle of incidence of 49.8 degrees with respect to the normal of the interface boundary, what is the angular separation between the red and violet ends of the spectrum upon exiting the prism? Measure this in degrees to 2 decimal places.
Question A4 The mineral schreibersite is often found in iron-nickel meteorites. One sample was found to have a body-centred tetragonal structure with a = 9.0168 Å and c = 4.4491 Å. Calculate the scattering angle and the multiplicity for the first (lowest 0) diffraction peak, using Cu Ka radiation of wavelength X = 1.5406 Å.
The dispersion curve of glass is the curve that describes how the index of refraction of glass changes as a function of the wavelength. This curve can be represented approximately by Cauchy's empirical equation, n = A + B/2² where for a specific glass in question A = 1.40 and B = 2.5 × 10 nm² (yes, those units are nanometer squared). Find the phase and group velocities for light of 500nm wavelength in that glass.
Please help me answer the following. The laser = 759 nm, and the diffraction grating is 4.5 cm
PROBLEM For a given x-ray diffraction test (n = 1) on a cubic crystal structure, the recorded diffraction peaks (20) were 24.09°, 34.33°, 42.37°, 49.33°, 55.62°, and 61.48°. The x-ray wavelength used in the test was 0.15418 nm. For this test, determine the crystal structure of the element, the lattice constant, and identify the element.