Question A4 The mineral schreibersite is often found in iron-nickel meteorites. One sample was found to have a body-centred tetragonal structure with a = 9.0168 Å and c = 4.4491 Å. Calculate the scattering angle and the multiplicity for the first (lowest 0) diffraction peak, using Cu Ka radiation of wavelength X = 1.5406 Å.

Question A4 The mineral schreibersite is often found in iron-nickel meteorites. One sample was found to have a body-centred tetragonal structure with a = 9.0168 Å and c = 4.4491 Å. Calculate the scattering angle and the multiplicity for the first (lowest 0) diffraction peak, using Cu Ka radiation of wavelength X = 1.5406 Å.

Similar questions

X-rays of wavelength 0.0628 nm are scattered from a crystal with a grazing angle of 11.3°. Assume m = 1 for this process. Calculate the spacing between the crystal planes. d = nm
The vanadium crystallizes in the body centered cubic lattice with a lattice parameter a. The X-ray diffraction data were collected from this compound and the following first four Bragg positions 20 (degrees): 21.06, 30.17, 37.03 and 43.10 were registered. The wavelength of the used X-ray radiation is 2 = 1.54Á. 1- Give the Bragg's Law. 2- Determine the inter-planer spacing d of the family of lattice planes (hke) of the cubic system. hkt 3 - Using the structure factor, determine the allowed reflections of the body centered cubic. 4- Index the four Bragg angles given above and calculate the cell parameter a.