A cylindrical rod with a length of 380 mm and a diameter of 10 mm is to be subjected to a tensile load. The rod mus not experience plastic deformation or an increase in the length of more than 0.9 mm when a load of 24.5 kN is applied. Which of the four materials listed in the table below are possible candidates? Justify your answer.

A cylindrical rod with a length of 380 mm and a diameter of 10 mm is to be subjected to a tensile load. The rod mus not experience plastic deformation or an increase in the length of more than 0.9 mm when a load of 24.5 kN is applied. Which of the four materials listed in the table below are possible candidates? Justify your answer.

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

A cylindrical specimen of aluminum having a diameter of 12.8 mm and a gauge length of 50.800 mm is pulled in tension by a 7330 N. The stress applied to the aluminum is?
A 3003-H14 aluminum alloy rod with 0.5 in. diameter is subjected to a 2000- lb tensile load. Calculate the resulting diameter of the rod. If the rod is sub- jected to a compressive load of 2000 lb, what will be the diameter of the rod? Assume that the modulus of elasticity is 10,000 ksi, Poisson’s ratio is 0.33, and the yield strength is 21 ksi.
A cylindrical specimen of brass that has a diameter of 20 mm, a tensile modulus of 110 GPa, and a Poisson's ratio of 0.35 is pulled in tension with force of 40,000 N. If the deformation is totally elastic, what is the strain experienced by the specimen? O 0.00463 O 0.00116 O 0.0029 O 0.01350
STRENGTH OF MATERIALS Answer: Maximum tensile 38 MN/m2, maximum compressive 46 MN/m2 Please show the solution to get the answer.
A round steel alloy bar with a diameter of 19mm and a gauge length of 76mm was subjected to tension, with the results shown in Table. Using a computer spreadsheet program, plot the stress–strain relationship. From the graph, determine the Young’s modulus of the steel alloy and the deformation corresponding to a 37kN load.
A cylindrical rod 500 mm long, having a diameter of 12.7 mm, is subjected to a tensile load of 30,000 N. The rod is to experience an elongation not more than 1.3 mm and FOS ≥ 1.5 setting yield strength as a criteria. Additional constraints to be met are max specific stiffness and %EL not more than 0.15. Which of the below listed materials are possible candidates? Justify your choice(s) by making a table of constraints.
A piece of Aluminum originally 213 mm long is pulled in tension with a stress of 844 MPa. If the deformation is entirely elastic, what will be the resultant elongation in mm? The modulus of elasticity of aluminum is 69 GPa. Round your answer to 2 significant figures.
A steel bar with a length of 3 m, diameter of 25 mm, modulus of elasticity of 207 GPa, and linear coefficient of thermal expansion of 0.000009 m/m/°C is fixed at both ends when the ambient temperature is 40°C. If the ambient temperature is decreased to 15°C, what internal stress will develop due to this temperature change? Is this stress tension or compression? Why?
A cylindrical rod with a length of 380 mm and a diameter of 10 mm is to be subjected to a tensile load. The rod must not experience plastic deformation or an increase in length of more than 0.9 mm when a load of 24.5 kN is applied. Which of the four materials listed in table are possible candidates? Justify your answer. Material Elastic Modulus, GPa Yield Strength, MPa Tensile Strength, MPa 110 ETT 70 207 101 Copper Aluminum alloy Steel Brass alloy 248 255 448 345 289 420 551 420 * Plastic deformation is defined as a process in which the object due to applied force changes its size or shape in a way that is not reversible
A cylindrical rod 360 mm long, having a diameter of 10.0 mm, is to be subjected to a tensile load. If the rodis to experience neither plastic deformation nor an elongation of more than 0.9 mm when the applied load is22500 N, which of the four metals or alloys listed below are possible candidates? Justify your choice(s).Material Modulus ofElasticity (GPa)Yield Strength(MPa)TensileStrength (MPa)Aluminum alloy 70 255 420Brass alloy 100 345 420Copper 110 210 290Steel alloy 207 450 550
A cylindrical piece of steel, with a diameter of 60mm and length 100 mm, is subjected to an axial compressive force of 40,000 kg. If bulk modulus is 1.7 x 106 kg/cm² and poison's ratio is 0.25 than the change in volume of the cylindrical piece is?
A cylindrical rod 600 mm long and having a diameter 13.2 mm is to be subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 1.4 mm when the applied load is 30 KN. Which of the four metals or alloys listed below are possible candidates. Justify the answer with calculations Material modulus of elasticity(gpa) yield strength(mpa) tensile strength(mpa) Aluminium alloy 70 255 420 Brass alloy 100 345 420 Copper 110 210 275 Steel alloy 207 450 550