A certain steel has proportionality limit of 300 N/mm² in simple tension. Under a Three Dimensional Stress System, the principal stresses are 150 N/mm² (Tensile), 75 N/mm² (Tensile) and 30 N/mm² (Compressive), μ = 0.3. The factor of safety according to maximum shear stress theory would be

A certain steel has proportionality limit of 300 N/mm² in simple tension. Under a Three Dimensional Stress System, the principal stresses are 150 N/mm² (Tensile), 75 N/mm² (Tensile) and 30 N/mm² (Compressive), μ = 0.3. The factor of safety according to maximum shear stress theory would be

Materials Science And Engineering Properties

1st Edition

ISBN:9781111988609

Author:Charles Gilmore

Publisher:Charles Gilmore

Chapter6: Introduction To Mechanical Properties

Section: Chapter Questions

Problem 5CQ

See similar textbooks

Related questions

Q: A 30m long aluminum bar is subjected to a tensile stress of 172 MPa. Find the elongation in mm if E…

Q: A plate in equilibrium is subjected to uniform stresses along its edges with magnitude Oxx= 30 MPa…

A: Given data- A plate in equilibrium under uniform stress- σxx=30 MPa,σyy=30 MPa,σzz=0 MPa, Young's…

Q: An aluminum alloy [E = 70 GPa; v = 0.33; a = 23.0×10-6/°C] bar is subjected to a tensile load P. The…

Q: An extruded polymer beam is subjected to a bending moment M. The length of the beam is L-760 mm. The…

A: Give Data: Length of beam=760 mm b1=102 mm b2=20mm d2=20mm a=6.5 mm tensile stress=10 Mpa…

Q: A bronze rod is rigidly attached between an aluminum rod and a steel rod as shown in the figure…

Q: 2. A steel with E = 29 000 ksi with a rectangular cross-section is bent over a rigid mandrel with R…

Q: An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 680 mm.…

A: FIND NA :y=36×95(952)-22×22(95-7-222)36×95-22×22y=22.637mmFIND MOI…

Q: An aluminum alloy [E = 72 GPa; v = 0.33; a= 23.0 x 10-6/°C] plate is subjected to a tensile load P.…

Q: An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 500 mm.…

A: Given data: Length of beam=L=500 mm b1=33 mm, d1=109 mm b2=20 mm, d2=20 mm a=6.5 mm Allowable…

Q: An extruded polymer beam is subjected to a bending moment M. The length of the beam is L = 800 mm.…

Q: If the material is machine steel having a yield stress of sY = 500 MPa, determine the factor of…

A: Given: The yield stress is 500 MPa. Consider the figure,

Q: . Calculate the strain at the centroid of the tension steel in single layer if the effective depth…

Concept explainers

Pressure and Stress

Question

A certain steel has proportionality limit of
300 N/mm² in simple tension. Under a Three
Dimensional Stress System, the principal stresses
are 150 N/mm² (Tensile), 75 N/mm² (Tensile) and
30 N/mm² (Compressive), μ = 0.3. The factor of
safety according to maximum shear stress theory
would be

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Given data

VIEW

Step 2: Calculate the factor of safety

VIEW

Solution

VIEW

Step by step

Solved in 3 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Compare the engineering and true secant elastic moduli for the natural rubber in Example Problem 6.2 at an engineering strain of 6.0. Assume that the deformation is all elastic.
A steel component is subjected to alternate cyclical loading. The steel follows Basquin's law for high cycle fatigue, o, x N = C, (where the stress amplitude is in MPa). Ignore the geometric detail and assume that Marin's modifying factors are all equal to 1. You are given the minimum stress ain = -213 MPa, the maximum stress omax = 213 MPa. The material data are Tensile strength oUTS = 539 MPa, Basquin's constant c, = 875 MPa, Basquin's exponent a = 0.085. a) Calculate the stress ratio R, the stress amplitude o, in MPa and the mean stress am in MPa. The answers are acceptable with a tolerance of 0.01 for R and of 1 MPa the stresses. R: MPa MPа b) Calculate the corresponding life, in 10° cycles, (tolerance of 0.1 106 cycles) N :
Solve please
For a given steel cube section subjected to three dimensional state of principal stress. 75N/mm² ŠI 150 N/mm 30 N/mm² Consider yield stress = 250 N/mm², and µ = 0.3 The value of factor of safety according to maximum strain energy theory. -X
A mild steel bar of square cross-section 40 mm x 40 mm is 400 mm long it is subjected to a longitudinal tensile stress of 440 N/mm² and lateral compressive stress is 200 N/mm² in perpendicular directions. E = 2 x 105 N/mm², μ = 0.3. What is the approximate elongation of the bar in the longitudinal direction?
A steel 0.6 inch×1.2 inch steel 90 m long is subjected to a 45 KN tensile load along its lenght.If poison's ratio is 0.3 Find: A. The deformation along its lenght. B. The deformation along its thickness. C. The defirmation along uts width. D. The lateral strain.
The stresses in a flat steel plate in a condition of plane stress are: o, = 10000 N/mm2 o = 6000 N/mm? = 8000 N/mm2 Find the magnitude and orientation of the principal stresses in the plane of the plate.
As shown, an aluminium alloy construction BCD with a circular cross section is fixed at end B and affected by a force of 150 N at the free end D. The diameter of the cross-section a-a is 20 mm. The yield strength of the material is 80 MPa: a) Determine the stresses at point A of the a-a cross-section. As indicated in the picture, draw the stress element in Cartesian coordinates and specify the stress values.(b) Calculate the factor of safety, n for Tresca, and the von Mises yield criterion to see if the structure would yield based on the stresses at point A.(c) In the major stress area, draw the yield loci of both criteria and indicate the operational stress state & why is the Rankine failure criterion inappropriate for aluminium alloys?
The state of plane stress shown occurs at a critical point of a steel machine component. As a result of several tensile tests, it has been found that the tensile yield strength is o, = 250 MPa for the grade of steel used. Determine the factor of safety with respect to yield using (a) the maximum shearing stress criterion, and (b) the maximum distortion energy criterion. ↑y 40 40 MPa 80 MPa 25 MPa ➜X
An aluminum alloy [E = 69 GPa; v = 0.33; a = 23.0 x 10-6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 215 mm, a cross-sectional area of A = 5100 mm2, and a length of L = 3.9 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by AT = 53°C, the longitudinal normal strain in the plate is found to be 2320 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Ad. L Answer: (a) P = i (b) Δd = = i d KN mm
PROBLEM 1) An aluminum bar carries the axial loads at the positions shown. If E=70GPA, compute the total deformation of the bar. Assume that the bar is suitably braced to prevent buckling. 0.4m D What is the axial stress o Ag in Pa? 10KN 0.8m 0.4m B 5KN 0.6m 20KN A=800 mm? A=1,200 mm²
An aluminum alloy [E = 74 GPa; v = 0.33; a = 23.0 x 10-6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 265 mm, a cross-sectional area of A = 5300 mm², and a length of L= 4.2 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by AT = 57°C, the longitudinal normal strain in the plate is found to be 2920 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Ad. L P Answer: (a) P = i (b) Δd = i kN mm