5. A specimen with cylindrical shape was subjected to tensile test. Please plot the stress vs. strain curve for the specimen and calculate Young's modulus. Diameter of test specimen, do 11.600 mm Length of test specimen, lo 50.500 mm Load vs. elongation data for the test specimen Load (N) Length (mm) 7.150 50.594 14.840 50.768 22.760 50.942 30.220 51.116 33.980 51.290 37.900 51.464 41.120 51.892 44.220 52.320 45.540 52.748 47.120 53.684 46.760 54.620 45.280 55.550 44.620 56.238 41.700 56.920 36.220 57.602

5. A specimen with cylindrical shape was subjected to tensile test. Please plot the stress vs. strain curve for the specimen and calculate Young's modulus. Diameter of test specimen, do 11.600 mm Length of test specimen, lo 50.500 mm Load vs. elongation data for the test specimen Load (N) Length (mm) 7.150 50.594 14.840 50.768 22.760 50.942 30.220 51.116 33.980 51.290 37.900 51.464 41.120 51.892 44.220 52.320 45.540 52.748 47.120 53.684 46.760 54.620 45.280 55.550 44.620 56.238 41.700 56.920 36.220 57.602

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Using the stress-strain curve in Figure 3, please answer questions: iv) If the specimen is loaded to stress of 65 Mpa and then unloaded, determine the residual plastic strain v) If the diameter of the unloaded specimen is 1cm and the Poisson's ratio of the material is v=0.3, what is the specimen diameter just prior of yield of the tensile specimen
Consider a bar with a rectangular cross-section area with a thickness of t = 0.5 in. and height of h = 3.5 in. When force P = 19 kips is applied to the bar, the strain gages attached to the surface of the bar reads εx = 740 µε along the direction of the force and εy = -170 µε in the perpendicular direction. Determine Poisson's ratio for this specimen? Determine the modulus of elasticity for this specimen?in Ksi
A “twisting” torque (i.e. torsion) of 80 Nm is applied to a hollow bone with an outside radius of 2 cm and an inside radius of 0.9 cm. What is the maximum shear stress of this bone? Report your answer in N/cm². Report to the nearest 0.1 unit (e.g. 100.1 N/cm²). You are allowed an error of +-10%.
Q-The longitudinal strain of cylindrical bar of 25 mm diameter and 1.5 m length is found to be 3 times its lateral strain in a tensile test. What is the value of Bulk Modulus by assuming SES E = 1x 10³ N/mm²?
Q. No .3 On the free surface of an aluminum [E = 10,000 ksi; v = 0.33] component, the strain rosette shown in the figure was used to obtain the following normal strain data: = -500 µɛ, E = -220 µe, and &e = +600 µɛ. Determine the normal stress that acts along an axis that is rotated at an angle of 0= 45° coun- terclockwise from the positive x axis. 60 60 60
In the diagram of a tensile sample: IEMIJOO TITia grinsigni pist -40 mm 4 mm (1 1998 AMIN 6.5 mm -20 mm- a) compute the magnitude of the stress at point P, when the externally applied stress is 140 MPa. b) how much would the radius of curvature at the point P need to be increased to reduce the stress by 25%
Given the torque-angle deformation curve below, estimate the shear modulus in GPa?. Where the length of the specimen is 273mm and the diameter is 19.3mm (Round your answer to nearest integer, e.g. 100, do not add units, use exact value of pi not 3.14) SC.O 45.0 35.0 25.0 20.0 5.0 0.20 040 050 0.60 0.70 0.80 0.90 Angle (") A S en eta ine f Your Answer: Answer Torque (N-m)
I. Problem Solving: Answer what is being required. Show you complete solution. 1. Compute the tensile stress from the value acquired from the experiment if the breaking load is 105KN. The diameter of the specimen is 150mm and the height is 300mm. 2. Compute the flexural stress of the sample specimen if its dimension is 150mm x 150mm x 500mm in a 3 point loading. The effective length is 400mm. The specimen failed at 44,300N in the middle third. 3. Compression test was applied to a certain type of wood. Compute the stress based on the following dimensions. The grains are parallel with the length. а. Compression Test Dimension (mm) Load (N) Compressive stress (МРa)
Can you please answer the following question in the picture and show all of your work in, please.
The strain rosette shown in the figure was used to obtain normal strain data at a point on the free surface of a machine component. ɛa= -250 µm/m, ɛb= -35 µm/m, and ɛc= 390 µm/m.[E= 29000 ksi, G= 10900 ksi, a= 40 °] y X a Determine the maximum absolute shear stress. 8660 psi 4190 psi 9810 psi 7020 psi 15000 psi O0000
Sketch the stress-strain curve of the following tension test??? In the tension test of a metal fracture occurs at maximum load. The conditions at fracture were: A = 100 mm and L, = 60 mm, the initial values were: A = 150 mm and L. 40 mm.
Calculate the stress from a 0.3498 in. diameter tensile specimen yielding at 4.407 kips 46.0 ksi 30.6 ksi 33.4 ksi 45.9 ksi