1. Determine the amount andcomposition of a and 3 phase in 100g of a lead-tin alloy of eutecticcomposition immediately after theeutectic reaction has beencompleted.a161.9BaTemperature (°C)4003002001000Pbαa+L20a+B161.9%4060Weight percent tin80B+LB-Sn

Given: The total mass of the lead tin alloy: →m=100 g At eutectic point: The weight percentage of…

Answered: 1. Determine the amount and composition…

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

2. Determine the amount of liquid phase in the a Cu-50% Ni alloy at 1300°C, % L 1500 1400 L. C +L 58 1300 1200 1100 1000 Cu 20 40 60 80 Ni Weight percent nickel Temperature (°C)
What is the composition, in wt% Cr2O3, of the liquid phase in an alloy containing 71 wt% Cr2O3 at 2200C?
Question One (Compulsory) Composition (atk Sn) 100 20 40 60 80 327C B00 300 Liquid 500 232C 400 200 183C 07.8 18.3 61.9 300 100- H200 100 BO 100 20 40 60 Pb) Compesition (wt% Sn) Figure 1: Lead -tin phase diagram Figure I above shows a lead-tin (alloy) phase diagram. Consider an alloy composition of 55 wt% Sn - 45 wt% Pb. Answer the following questions: (i) Name the phases present and their compositions in the alloy at 150°C. (ii) Describe the structural and composition changes in the alloy when it is cooled from 190°C to 20°C. (iii) What are the compositions of phases at the eutectic point and why is this point important for the alloy? (iv) Given that the average density of a phase is determined as Pa = 100 ,calculate the PA PB volume fractions of the phases at the given compositions and at 150°C. Take the densities of lead and tin as 11.34 g/cm' and 7.36 g/cm' while the mass fraction of a is 0.21. (v) Name and describe four industrial applications of lead-tin alloys. ta aroundu (3.)…
Q2/ For a 97.5 wt% Fe-2.5 wt% C at a temperature 700 oC, determine the following: a) The Number and types of The Phases Present. b) The Amount of Phases Present in Grams That forms per 100 G. c) Draw The Microstructure Of Phases Present At This Point And What is The React called? 1600 1538°C 1493°C L 1400 8 1394°C Y+L 1200 y, Austenite 1000 Temperature (°C) 912°C 800a Y 600 400 0 (Fe) 0.76 0.022 a, Ferrite 1 2.14 1147°C 4.30 y + Fe C رقم الصفحة 1/ 1 727°C a + Fe3C 2 4 3 Composition (wt% C) Iron- Carbon Phase Diagrams Cementite (Fe3C) 5 6 6.7
For an alloy containing 20 wt % Ag, refer to the Cu-Ag phase diagram given in the Figure: What is the melting point of Cu in °C? What are the relative amounts(in %) of the existing phases at 900°C? Define the Eutectic point in terms of °C and the composition % of Ag.
Q/ The phase present for a 30 wt% sn, 7O wt% pb of alloy at 200°c is (a+ L) Determine: Composition of (a) and (L) for both (sn) and (pb). * 327°C 300E Liquid 232°C a +L 200E B + L 183°C 18.3 61.9 97.8 100 a +B 20 40 60 80 100 (Pb) Composition (wt% Sn) (Sn) Ca =18 Wt% pb, CL=58 Wt% pb and Ca =82 Wt% Sn, CL=42 Wt% Sn. Ca =20 Wt% pb, CL=60 Wt% pb and Ca =80 Wt% Sn, CL=40 Wt% Sn. Ca =22 Wt% pb, CL=65 Wt% pb and Ca =78 Wt% Sn, CL=35 Wt% Sn. Ca =15 Wt% pb, CL=63 Wt% pb and Ca =85 Wt% Sn, CL=73 Wt% Sn. Temperature ("C)
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Should correct
For the lead-tin system:(a) Determine the proportions of liquid and solid phases for the 40% Sn composition ofthe lead-tin system at temperatures 2500?, 2000?, ??? 1500?. (b) Draw the development of microstructure along the dashed line at points A,B,C, andD.
Please tell me statements in the question is true or false with small reason of your answer Part 2
In this Sn-Pb alloy system, what is the relative percentage of proeutectic alpha phase after alloy 2 is cooled down from 300 °C to room temperature? Alloy 2 Alloy I 327 Solidus Liquidus 300 Liquid Liquidus 250 a + liquid Solidus 200 B+ liquid 183 Eutectic point 150 Solvus +B 100 Solvus 50 19.2 40.0 61.9 97.5 li 60 10 20 30 40 50 70 80 90 100% 100% Weight percent tin Sn Pb O1. 73% O II. 51% O II. 49% O IV. 27% Temperature (C),
*About the Pb/Sn binary system, find the percentages of phases at room temperature for each of the following alloys. Alloy Chemical composition Percentages of phases at room temperature no. 20%Sn,80% Pb 40% Sn,60% Pb 3 62% Sn,38% Pb 70%Sn,30% Pb 90% Sn, 10% Pb 4

Recommended textbooks for you

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Elements Of Electromagnetics

Mechanical Engineering

ISBN:

9780190698614

Author:

Sadiku, Matthew N. O.

Publisher:

Oxford University Press

Mechanics of Materials (10th Edition)

Mechanical Engineering

ISBN:

9780134319650

Author:

Russell C. Hibbeler

Publisher:

PEARSON

Thermodynamics: An Engineering Approach

Mechanical Engineering

ISBN:

9781259822674

Author:

Yunus A. Cengel Dr., Michael A. Boles

Publisher:

McGraw-Hill Education

Control Systems Engineering

Mechanical Engineering

ISBN:

9781118170519

Author:

Norman S. Nise

Publisher:

WILEY

Mechanics of Materials (MindTap Course List)

Mechanical Engineering

ISBN:

9781337093347

Author:

Barry J. Goodno, James M. Gere

Publisher:

Cengage Learning

Engineering Mechanics: Statics

Mechanical Engineering

ISBN:

9781118807330

Author:

James L. Meriam, L. G. Kraige, J. N. Bolton

Publisher:

WILEY

SEE MORE TEXTBOOKS

1. Determine the amount and composition of a and 3 phase in 100 g of a lead-tin alloy of eutectic composition immediately after the eutectic reaction has been completed. 9 L61.9 Temperature (°C) 400 300 200 100 a+L 20 61.99 40 60 Weight percent tin 80 B+L Sn