3. A copper-silver alloy is heated to 900°C (Figure Q1) and is found to consist of a andliquid phases. If the mass fraction of the liquid phase is 0.68, determine(a) the composition of both phases, in both weight percent and atom percent, and(b) the composition of the alloy, in both weight percent and atom percentTemperature (°C)1200A100080060040020000aC(Cu)B8.0(Cap)-SolidusSolvus2020a + LComposition (at% Ag)-Liquidus779°C (TB)I4040a + B1TLiquid16060E71.9(CE)IComposition (wt% Ag)Figure Q1: Copper-silver phase diagramT8080B+L91.2(CBE)IG100L220020001800F1600140012001000800→600H400100(Ag)Temperature (°F)

Answered: Image /qna-images/answer/a707f4ea-bed5-4505-8159-066d4f7106f0.jpg

3. A copper-silver alloy is heated to 900°C (Figure Q1) and is found to consist of a and liquid phases. If the mass fraction of the liquid phase is 0.68, determine (a) the composition of both phases, in both weight percent and atom percent, and (b) the composition of the alloy, in both weight percent and atom percent Temperature (°C) 1200 1000 800 600 400 2000 a (Cu) B 8.0 (Ca) -Solidus Solvus 20 20 a + L Composition (at % Ag) 40 -Liquidus 779°C (TE) 40 a + B Liquid 60 E 71.9 (CE) 60 Composition (wt% Ag) Figure Q1: Copper-silver phase diagram 80 80 B+L 91.2 (C₁E) G 22₂ 100 H 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 (Ag) Temperature (°F)

3. A copper-silver alloy is heated to 900°C (Figure Q1) and is found to consist of a and liquid phases. If the mass fraction of the liquid phase is 0.68, determine (a) the composition of both phases, in both weight percent and atom percent, and (b) the composition of the alloy, in both weight percent and atom percent Temperature (°C) 1200 1000 800 600 400 2000 a (Cu) B 8.0 (Ca) -Solidus Solvus 20 20 a + L Composition (at % Ag) 40 -Liquidus 779°C (TE) 40 a + B Liquid 60 E 71.9 (CE) 60 Composition (wt% Ag) Figure Q1: Copper-silver phase diagram 80 80 B+L 91.2 (C₁E) G 22₂ 100 H 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 (Ag) Temperature (°F)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Temperature, °C 10 -10 -20 -30 NaCl 0 Ice + liquid (brine) Liquid (brine) 10 Ice + salt 20 Salt +…

Q: For a hypothetical material, experiments show that a sample containing 1 billion atoms has 40…

A: Given; Number of atoms (N) @600° C is 1 billion (1×109 ) Numbers of vacancies (Nv) @600° C is 40…

Q: In an electrochemical cell, a metal anode lost 0.227 g while a total volume of 0.08149 L of hydrogen…

Q: What is the composition in weight percent of an alloy that contains 98 g tin and 65 g lead? What is…

A: weight of the alloy (98+65)=163g weight percentage of Tin=(98/163)x100=60.12 %…

Q: answer all the parts from a-c

Q: Copper (Cu) and silver (Ag) alloys form a binary alloy system that dissolves each other completely…

A: Please find the solution below

Q: How many kilograms of nickel must be added to 1.75kg of copper to yield a liquidus temperature of…

A: In the given figure, Copper - Nickel equilibrium diagram is given. It is required to determine…

Q: For a hypothetical material, experiments show that a sample containing 1 billion atoms has 40…

A: Given Data T=6000c = T=600+273=873k N=number of atomic sites per cubic meter = 1x109 atoms/m3…

Q: The microstructure of eutectic alloys is always heterogeneous. true or false.

A: This question is based on the concept of eutectic alloys.

Q: What is the solubility limit of Cr2O3 in the solid at 2025C? Al,03-Cr,O3 Phase Diagram 2300 2250…

A: Al2O3Cr2O3 - This is the isomorphous system, in this alloy elements are completely soluble in both…

Q: Coal has the following analysis: carbon = 75%, hydrogen = 5%, oxygen = 6%, nitrogen = 1.5%, sulfur =…

Q: (2) Sketch the microstructure of Pb-Sn alloy at (A) and (B). (s Composition (at% Sn)

A: Microstructure in metallic materials consists of the distribution and topological arrangement of…

Q: B/ Aluminum (Tm=660 OC) and Silicon (Tm=1410 OC) were fully dissolved in each other in the liquid…

A: Given: The melting point of pure Al with 0% Si, Tal = 660°C The melting point of pure with 0% Al,…

Q: How would I... Determine the composition of aluminum and silicon (%Al/%Si) to melt the Al-Si…

A: what you are looking for is the eutectic point in a eutectic reaction a liquid phase transforms into…

Q: If our alloy has a composition of 10% i and has a temperature of 1100C, determim Si. a) What…

Q: 1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After…

A: Given: Mass of steel=1000 grams Weight % of carbon=1.5 % To find: The amount of pure iron or pure…

Q: For alloys of two hypothetical metals A and B, there exist an a, A-rich phase, and a B, B-rich…

Q: The composition of the α in an 42 wt% griffinium alloy at 662 degrees centigrade is (enter the wt%…

A: Givengriffinium alloy Gr=42 wt% at 662oC

Q: It's not even that Idk how to do it, I'm very confused at that what parameters I should use to even…

Q: Which of the following statements are true about the following phase diagram? Group of answer…

A: At atmospheric pressure three allotropic forms of iron exist: alpha iron (α-Fe), gamma iron and…

Q: 7. Consider 1.5 kg of a 99.6 wt% Fe-0.4 wt% C steel that is cooled to a temperature just below the…

A: In this problem we are asked to consider 2.0 kg of a 99.6 wt% Fe-0.4 wt% C alloy that is cooled to a…

Q: At what temperature does the first liquid phase form at 90% Ni? T(°C) 1600 1500 1400 1300 1200 1100…

Q: 1 Al-Li Aerospace Alloys When a small amount of Li is added into Al to create an Al-Li alloy, the…

Q: 13) If you have an alloy with a composition of 22 wt% Ag at a temperature of 779.1° C, identify: a)…

Q: Hi i keep getting these wrong

A: 13.1 Bi-65at%Sb means 65% Sb and 35% Bi. See the image I attached, it would be ~375oC. So your…

Question

3. A copper-silver alloy is heated to 900°C (Figure Q1) and is found to consist of a and
liquid phases. If the mass fraction of the liquid phase is 0.68, determine
(a) the composition of both phases, in both weight percent and atom percent, and
(b) the composition of the alloy, in both weight percent and atom percent
Temperature (°C)
1200
A
1000
800
600
400
200
0
0
a
C
(Cu)
B
8.0
(Cap)
-Solidus
Solvus
20
20
a + L
Composition (at% Ag)
-Liquidus
779°C (TB)
I
40
40
a + B
1
T
Liquid
1
60
60
E
71.9
(CE)
I
Composition (wt% Ag)
Figure Q1: Copper-silver phase diagram
T
80
80
B+L
91.2
(CBE)
I
G
100
L
2200
2000
1800
F
1600
1400
1200
1000
800
→600
H
400
100
(Ag)
Temperature (°F)

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step 5

Trending now

This is a popular solution!

Step by step

Solved in 5 steps with 5 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Phase Diagrams and Its Applications in Metallurgy

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Determine the composition and fraction with 50% Ni and 1300 ° C
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
An alloy system consists of two metals A&B which are soluble in each other in all proportions in the liquid state, but completely insoluble in the solid state. The melting point of metal A is 425°C and B is 375°C. The lowest melting point (Eutectic) is 230°C at 40%B. Choose the correct answers for the following sentences: the phases present in the equilibrium diagram are: OL& A & B O A & B O A&L B& L
Solve correctly please.
An aluminum alloy contains 0.091 mol aluminum and 0.038 mol of magnesium. Determine the mass percentage of magnesium in the alloy. а. 22.7 с. 31.5 b. 27.3 d. 39.2
For the lead-tin system:(a) Determine the proportions of liquid and solid phases for the 40% Sn composition ofthe lead-tin system at temperatures 2500?, 2000?, ??? 1500?. (b) Draw the development of microstructure along the dashed line at points A,B,C, andD.
Material science Assuming this system forms a laminar type eutectic, determine the volume proportion of phases for an equilibrium solidified 50% Pb alloy. Sketch the expected microstructure.
A hypothetical eutectic phase diagram for metals A and B shows that cooling a liquid melt with a concentration of 50 wt% A-50 wt% B to just below 625 °C (eutectic isotherm temperature) results in simultaneous formation of alpha and beta phases. The phase diagram also shows that alpha (A rich) and beta (B rich) phases exist at left and right extremes of the phase diagram, respectively. At the eutectic isotherm temperature, the maximum solubility of B in A and A in B is 10 wt% and 5 wt%, respectively. The phase diagram does not have any intermetallic compounds. A new solid alloy is made by melting together 86 gr of a 40 wt% A-60 wt% B alloy with 136 gr of 65 wt% A-35 wt% B alloy followed by cooling the melt to 400 °C. If the new alloy is heated up from 400 °C to just below 625 °C, answer the following questions: a. Calculate the overall alloy composition. b. Determine phases present and calculate their respective masses. Calculate the masses of the primary phase, eutectic phase, and…
700 L 600 M a + L Mg, Pb 500 P 465 400 L Mg Pb 300 200 a + Mg Pb B+ Mg Pb 100 20 40 60 80 100 Mg Composition (wt% Pb) Pb Mg,Pb Using the above figure, sketch neatly the microstructure of the alloys (given in the below table) and determine the amount of each phase presented. Structure of the alloys at different compositions 田 Compositions &temperature 10%Pb,90%Mg Structure Structure Compositions &temperature 20%Pb, 80%Mg @400°C @0°C My.Pb 50%Pb,50%Mg 67%Pb, 33%Mg @0°C Mgz PB @0°C 81%Pb,19%Mg 90%Pb,10%Mg @200°C @0°C Temperature ("C)
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite
*About the Pb/Sn binary system, find the percentages of phases at room temperature for each of the following alloys. Alloy Chemical composition Percentages of phases at room temperature no. 20%Sn,80% Pb 40% Sn,60% Pb 3 62% Sn,38% Pb 70%Sn,30% Pb 90% Sn, 10% Pb 4