Textbook Question
Chapter 19, Problem 42QTP
Estimate the die-clamping force required for injection molding five identical 8-in.-diameter disks in one die. Include the runners of appropriate length and diameter.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
3. A dimension of 225.00 mm is specified for a particular injection moulded component manufactured
in ABS. Calculate the corresponding dimension to which the mould cavity should be machined, using
the value of shrinkage given in the table below.
Typical values of shrinkage for moldings of selected thermoplastics.
Shrinkage,
mm/mm (in/in)
Shrinkage,
Plastic
Plastic
mm/mm (in/in)
ABS
Polyethylene
Polystyrene
0.006
0.025
Nylon-6,6
Polycarbonate
0.020
0.004
0.007
PVC
0.005
8
An extrusion operation is used to produce a parison whose mean diameter = 27 mm. The inside and outside diameters of the die that produced the parison are 18 mm and 22 mm, respectively. If the minimum wall thickness of the blow-molded container is to be 0.40 mm, what is the maximum possible diameter of the blow mold?
Chapter 19 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 19 - What are the forms of raw materials for processing...Ch. 19 - What is extrusion? What products are produced by...Ch. 19 - Describe the features of an extruder screw and...Ch. 19 - How are injection-molding machines rated?Ch. 19 - What is (a) a parison, (b) a plastisol, and (c) a...Ch. 19 - How is thin plastic film produced?Ch. 19 - List several common products that can be made by...Ch. 19 - What similarities and differences are there...Ch. 19 - Explain the difference between potting and...Ch. 19 - What is thermoforming?
Ch. 19 - Describe runner, gate, sprue, and well.Ch. 19 - Describe the advantages of cold-forming plastics...Ch. 19 - What are the characteristics of filament-wound...Ch. 19 - Describe the methods that can be used to make...Ch. 19 - What is pultrusion? Pulforming?Ch. 19 - How are very thin plastic film produced?Ch. 19 - What process is used to make foam drinking cups?Ch. 19 - If a polymer is in the form of a thin sheet, is it...Ch. 19 - How are polymer fibers made? Why are they much...Ch. 19 - What are the advantages of coextrusion?Ch. 19 - Explain how latex rubber gloves are made.Ch. 19 - Describe the features of a screw extruder...Ch. 19 - Explain why injection molding is capable of...Ch. 19 - Prob. 24QLPCh. 19 - Explain the reasons that some plastic-forming...Ch. 19 - Describe the problems involved in recycling...Ch. 19 - Can thermosetting plastics be used in injection...Ch. 19 - Inspect some plastic containers, such as those...Ch. 19 - An injection-molded nylon gear is found to contain...Ch. 19 - Explain why operations such as blow molding and...Ch. 19 - Prob. 31QLPCh. 19 - Typical production rates are given in Table 19.2....Ch. 19 - What determines the cycle time for (a) injection...Ch. 19 - Does the pull-in defect (sink marks) shown in Fig....Ch. 19 - What determines the intervals at which the...Ch. 19 - Identify processes that would be suitable for...Ch. 19 - Identify processes that are capable of producing...Ch. 19 - Inspect several electrical components, such as...Ch. 19 - Inspect several similar products that are made of...Ch. 19 - What are the advantages of using whiskers a...Ch. 19 - Construct a table that lists the main...Ch. 19 - Estimate the die-clamping force required for...Ch. 19 - A 2-Iitcr plastic beverage bottle is made by blow...Ch. 19 - Consider a Styrofoam drinking cup. Measure the...Ch. 19 - In Fig. 19.2, what flight angle, , should be used...Ch. 19 - Make a survey of a variety of sports equipment,...Ch. 19 - Explain the design considerations involved in...Ch. 19 - Give examples of several parts suitable for insert...Ch. 19 - Give other examples of design modifications in...Ch. 19 - With specific examples, discuss the design issues...Ch. 19 - Die swell in extrusion is radially uniform for...Ch. 19 - Inspect various plastic components in a typical...Ch. 19 - It is well known that plastic forks, spoons, and...Ch. 19 - Prob. 55SDPCh. 19 - Make a survey of the technical literature, and...Ch. 19 - Prob. 57SDPCh. 19 - Prob. 58SDPCh. 19 - Prob. 59SDPCh. 19 - Examine some common and colorful plastic poker...Ch. 19 - Obtain different styles of toothpaste tubes,...Ch. 19 - By incorporating small amounts of blowing agent,...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Review Problems The extrusion die for a polyethylene parison used in blow molding has a mean diameter of 18.0 mm. The size of the ring opening in the die is 2.0 mm. The mean diameter of the parison is observed to swell to a size of 21.5 mm after exiting the die orifice. If the diameter of the blow molded container is to be 150 mm, determine (a) the corresponding wall thickness of the container and (b) the wall thickness of the parison.arrow_forwardWhat kind of system is compression molding machine? open, closed, or isolated? Explain.arrow_forwardExplain the extrusion blow molding in detail.arrow_forward
- A typical plastic shopping bag made by blown film has a lateral dimension (width) of 550 mm. Assume the tube is expended from 1.5 to 2.5 times the extrusion die diameter. Calculate the extrusion die diameter size.arrow_forwardDescribe the defects found on the injection/ compression moulded parts with different temperatures or time setting. Discuss the possible causes for each case.arrow_forwardQ1arrow_forward
- Compare compression and injection molding for speed, cost per part, investment cost, and flexibility in types of material that can be handled?arrow_forwardWhich law of thermodynamics best apply to compression molding machine? Explain why.arrow_forwardAn extruder has barrel diameter and length of 150 mm and 3.1 m, respectively. The screw rotational speed = 55 rev/min, channel depth = 8 mm, and flight angle = 18°. The plastic melt has a shear viscosity = 175 Pa-s. Determine: (a) the extruder characteristic, (b) the shape factor Ks for a circular die opening with diameter = 4.0 mm and length = 15 mm, and (c) the operating point (Q and p).arrow_forward
- May I have help with this please?arrow_forwardConsider the extrusion of a cylindrical billet, and compute the following. Assume the starting billet to have a length of 0.3m and a diameter of 15cm. This is extruded into a cylindrical product that is 3cm in diameter and 7.5cm long. Neglecting the areas on the two ends, compute the ratio between the product surface area (wraparound cylinder) and the surface area of the starting billet. How would this ratio change if the product were a square with the same corss-sectional area as that of the 3cm diameter circle?arrow_forwardA 10 mm thick plate is rolled to 7 mm thick in a rolling mill using 1000 mm diameter rigid rolls. The neutral point is located at an angle of 0.3 times the bite angle from the exit. What will be the thickness of the plate at the neutral point.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license