Textbook Question
Chapter 17, Problem 41QTP
The axisymmetric part shown in Fig. P17.41 is to be produced from fine copper powder and is to have a tensile strength of 175 GPa. Determine the compacting pressure and the initial volume of powder needed.
FIGURE P17.41
Expert Solution & Answer
Trending nowThis is a popular solution!
Students have asked these similar questions
Granule strength is very important in pressing powders.
The force applied to a granule with a radius of 1 mm is 0.5 Newton. Calculate the breaking
strength of the granule.
b) It is observed that the pressed granules break easily during pressing. Write down the reasons
of this situation and what would you take precations to solve this problem? Why? (please write
down 3 precautions with reasons).
odluck
Your die setter brings you a print of a cylinder with a 2 inch outside diameter and a 1.75 inch inside
diameter. The cylinder is to be molded of iron powder with a green density of 6.8 g/cc. The apparent
density of the powder is 2.9 g/cc. What is the die fill if the green part is to have a height of 2.5 inches?
(show your work)
3
Chapter 17 Solutions
Manufacturing Engineering & Technology
Ch. 17 - Describe briefly the production steps involved in...Ch. 17 - Name the various methods of powder production and...Ch. 17 - Explain why metal powders may be blended.Ch. 17 - Describe the methods used in metal powder...Ch. 17 - What is isostatic pressing? How is it different...Ch. 17 - What hazards are involved in PM processing?...Ch. 17 - Describe what occurs to metal powders during...Ch. 17 - Prob. 8RQCh. 17 - Why might secondary and finishing operations be...Ch. 17 - Prob. 10RQ
Ch. 17 - Prob. 11RQCh. 17 - Prob. 12RQCh. 17 - Prob. 13RQCh. 17 - What is screening of metal powders? Why is it...Ch. 17 - Why are protective atmospheres necessary in...Ch. 17 - Why is there density variation in the compacting...Ch. 17 - What is the magnitude of the stresses and forces...Ch. 17 - List the similarities and differences of forging...Ch. 17 - Give some reasons that powder-injection molding is...Ch. 17 - How does the equipment used for powder compaction...Ch. 17 - Explain why the mechanical and physical properties...Ch. 17 - What are the effects of the different shapes and...Ch. 17 - Describe the relative advantages and limitations...Ch. 17 - How different, if any, are the requirements for...Ch. 17 - The powder metallurgy process can be competitive...Ch. 17 - What are the reasons for the shapes of the shown...Ch. 17 - Should green compacts be brought up to the...Ch. 17 - Because they undergo special processing, metal...Ch. 17 - In Fig. 17.12, it can be seen that the pressure is...Ch. 17 - Why do the compacting pressure and the sintering...Ch. 17 - What will be stronger: a blend of stainless steel...Ch. 17 - Name the various methods of powder production and...Ch. 17 - Estimate the maximum tonnage required to compact a...Ch. 17 - Refer to Fig. 17.11a. What should be the volume of...Ch. 17 - Determine the shape factors for (a) a cylinder...Ch. 17 - Estimate the number of particles in a 500-g sample...Ch. 17 - Prob. 37QTPCh. 17 - A coarse copper powder is compacted in a...Ch. 17 - A gear is to be manufactured from iron powders. It...Ch. 17 - What volume of powder is needed to make the gear...Ch. 17 - The axisymmetric part shown in Fig. P17.41 is to...Ch. 17 - Prepare an illustration similar to Fig. 13.1,...Ch. 17 - Prob. 44SDPCh. 17 - Compare the design considerations for PM products...Ch. 17 - Prob. 46SDPCh. 17 - Prob. 47SDPCh. 17 - Using the Internet, locate suppliers of metal...Ch. 17 - Explain why powder metal parts are commonly used...Ch. 17 - Prob. 50SDPCh. 17 - Describe how the information given in Fig. 17.15...Ch. 17 - It was stated that, in the process shown in Fig....Ch. 17 - Prob. 53SDPCh. 17 - The axisymmetric parts shown in Fig. P17.54 are to...Ch. 17 - Assume you are working in technical sales. What...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Explain the difference between gas atomized powder and water atomized powder and why they are importantarrow_forwardA thin steel disk of an oil separator of 100mm outside diameter is shrunk onto a solid steel shaft of 20mm diameter. The system is to be designed to make sure the disc does not become loose at speeds lower than 100000rev/min. Determine the shrinkage allowance required in order to avoid separation disc and shaft, at a speed of 100000rev/min. For the material assume a Young's Modulus, Poisson Ratio and density of 210GPa, 0.3 and 7850kg/m³ respectively.arrow_forwardFor a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm3 andcrystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous andcrystalline states is 0.870 g/cm3 and 0.998 g/cm3 respectively)(This question has only one correct answer)% Crystallinity = 55.45%% Crystallinity = 65.50%% Crystallinity = 76.99%% Crystallinity = 82.30%% Crystallinity = 57.25%arrow_forward
- Name the various methods of powder production and the morphology of the powders produced.arrow_forward2arrow_forwardFor a powder binding process that mixes a 3:1 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm³ and 0.998 g/cm³ respectively)arrow_forward
- Review Problems The extrusion die for a polyethylene parison used in blow molding has a mean diameter of 18.0 mm. The size of the ring opening in the die is 2.0 mm. The mean diameter of the parison is observed to swell to a size of 21.5 mm after exiting the die orifice. If the diameter of the blow molded container is to be 150 mm, determine (a) the corresponding wall thickness of the container and (b) the wall thickness of the parison.arrow_forwardGKN Sinter Metals Company pressed iron powders using a compaction pressure of 600 MPa to produced a cylindrical bearing which is 70 cm long and has internal and external diameters of 8 cm and 16 cm, respectively. Determine (a) the most appropriate pressing direction, (b) the required press tonnage to perform this operation, and (c) the final weight of the part if the porosity is 12%, given that the density of iron, ρ = 7.87 g/cm3. Assume shrinkage during sintering can be neglectedarrow_forward8) In powder metallurgy operation, sintering of components Improves strength and reduced hardness. Reduced brittleness and improves strength. Improves hardness and reduced toughness. Reduces porosity and increases brittlenessarrow_forward
- QUESTION 1 (a) Powder Metallurgy (PM) has become competitive with processes such as casting, forging and machining, particularly for complex parts made of high strength and hard alloys. Compare the design considerations for products made of powder metallurgy, casting and forging process. Evaluate your observation. (b) Products made of sheet metals can be easily found around us. Identify some of the products in your automobile which are made from sheet metal, and discuss the process or combination of processes required to produce such products.arrow_forwardFor a powder binding process that mixes a 3:1 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm3 and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm3 and 0.998 g/cm3 respectively) a. % Crystallinity = 35.50% b. % Crystallinity = 55.25% c. % Crystallinity = 53.35% d. % Crystallinity = 61.20% e. % Crystallinity = 45.96%arrow_forwardFor a powder binding process that mixes a 1:2 volume ratio mixture of semi-crystalline polyethylene powder with a density of 0.900 g/cm³ and crystalline polyethylene powder, what is the percent crystallinity of the manufactured parts? (The density of polyethylene in its amorphous and crystalline states is 0.870 g/cm³ and 0.998 g/cm³ respectively) (This question has only one correct answer) О а. % Crystallinity = 55.45% O . % Crystallinity = 57.25% О с. % Crystallinity = 76.99% Od. % Crystallinity = 82.30% % Crystallinity = 65.50%arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Polymer Basics; Author: Tonya Coffey;https://www.youtube.com/watch?v=c5gFHpWvDXk;License: Standard youtube license