Textbook Question
Chapter 14, Problem 44SDP
Figure P14.44 shows a round impression-die forging made from a cylindrical blank, as illustrated on the left. As described in this chapter, such parts are made in a sequence of forging operations. Suggest a sequence of intermediate forging steps to make the part on the right, and sketch the shape of the dies needed.
Figure P14.44
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Question 5
5.1 Calculate the final bend radius for a 3 mm thick 6061 T6 aluminum plate that is formed
using a forming punch with an 8 mm radius, as shown in Figure 3.
R 8
Figure 3: Bend profile that is formed using a V-block die and a punch with a 8 mm
radius
5.2 Explain why there would be a difference between the initial and final bend radius during
the bending process and how this occurrence depends upon material properties, sheet
thickness and the bend radius.
4)
Explain the basic operation of open-die forging. Use sketches to assist the explanation.
Chapter 14 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 14 - What is the difference between cold, warm, and hot...Ch. 14 - Explain the difference between open-die and...Ch. 14 - Explain the difference between fullering, edging,...Ch. 14 - What is flash? What is its function?Ch. 14 - Why is the intermediate shape of a part important...Ch. 14 - Describe the features of a typical forging die.Ch. 14 - Explain what is meant by load limited, energy...Ch. 14 - What type of parts can be produced by rotary...Ch. 14 - Why is hubbing an attractive alternative to...Ch. 14 - What is the difference between piercing and...
Ch. 14 - What is a hammer? What are the different kinds of...Ch. 14 - Why is there barreling in upsetting?Ch. 14 - What are the advantages and disadvantages of...Ch. 14 - Why are draft angles required in forging dies?Ch. 14 - Is a mandrel needed in swaging?Ch. 14 - Describe and explain the factors that influence...Ch. 14 - How can you tell whether a certain part is forged...Ch. 14 - Identify casting design rules, described in...Ch. 14 - Describe the factors involved in precision...Ch. 14 - Why is control of the volume of the blank...Ch. 14 - Why are there so many types of forging machines...Ch. 14 - What are the advantages and limitations of cogging...Ch. 14 - What are the advantages and limitations of using...Ch. 14 - Review Fig. 14.6e and explain why internal draft...Ch. 14 - Comment on your observations regarding the...Ch. 14 - Describe your observations concerning the control...Ch. 14 - Prob. 27QLPCh. 14 - Describe the difficulties involved in defining the...Ch. 14 - Describe the advantages of servo presses for...Ch. 14 - List the general recommendations you would make...Ch. 14 - Which would you recommend, (a) hot forging and...Ch. 14 - Take two solid, cylindrical specimens of equal...Ch. 14 - Calculate the room-temperature forging force for a...Ch. 14 - Using Eq. (14.2), estimate the forging force for...Ch. 14 - To what thickness can a solid cylinder of 1020...Ch. 14 - In Example 14.1, calculate the forging force,...Ch. 14 - Using Eq. (14.1), make a plot of the forging...Ch. 14 - How would you go about estimating the punch force...Ch. 14 - A mechanical press is powered by a 30-hp motor and...Ch. 14 - A solid cylindrical specimen, made of a perfectly...Ch. 14 - Devise an experimental method whereby you can...Ch. 14 - Assume that you represent the forging industry and...Ch. 14 - Figure P14.44 shows a round impression-die forging...Ch. 14 - Prob. 45SDPCh. 14 - Prob. 46SDPCh. 14 - Review the sequence of operations in the...Ch. 14 - Prob. 48SDPCh. 14 - Discuss the possible environmental concerns...Ch. 14 - List the advantages and disadvantages in using a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- An open die forging operation is performed to produce a steel cylinder with a diameter of 9.7mm and a height of 1.7mm. The strength coefficient for this steel is 500MPA, and the strain hardening exponent is 0.25. Coefficient of friction at the die-work interface is 0.12. The initial stock of raw material has a diameter of 5mm. (a) What height/length of stock is needed to provide sufficient volume of material for this forging operation? (b) Compute the maximum force that the punch must apply to form the head in this open- die operation.arrow_forwardA solid cylindrical slug made of 304 stainless steel is 150 mm in diameter and 100 mm high. It is reduced in height by 50% at room temperature by opendie forging with flat dies. Assuming that the coefficient of friction is 0.2 and the flow stress of this material is 1000 MPa, calculate the forging force at the end of the stroke. Manufacturing processesarrow_forwardA upset forging operation is performed in an open die. The initial size of the workpart is: Do = 63 mm, and ho = 100 mm. The part is upset to a diameter = 70 mm. The work metal has a flow curve with strength coefficient = 600 MPa and strain hardening exponent= 0.22. Coefficient of friction at the die-work interface = 0.40. Determine (a) final height of the part, and (b) maximum force in the operation.arrow_forward
- Explain briefly the relationship between the load-stroke in open die forging as illustrated in the figures bellow. Take in consideration the effect of coefficient of friction.arrow_forward1. A component is designed to be hot forged in an impression die. The projected area of the product is 5800 mm2. During the forging process flashing is formed so that the area including the flash will be 8900 mm2. The part geometry is considered to be simple and the heated work material yields at 92 MPa. Calculate the maximum force required to perform the operation. 2. What are the advantages and disadvantages to forge a product through the open forging process, rather than to machine it from the same material?arrow_forwardA cylindrical part is warm upset forged in an open die. The initial diameter is 50 mm and the initial height is 40 mm. The height after forging is 30 mm. The coefficient of friction at the die-work interface is 0.25. The yield strength of the work material is 285 MPa, and its flow curve is defined by a strength coefficient of 600 MPa and a strain-hardening exponent of 0.12. Calculate the strain at yield point.arrow_forward
- A compound die will be used to blank and punch a large rectangle (90x150mm blank dimensions) out of 6061ST aluminum alloy sheet stock 3.5 mm thick. The diameter of inside hole is 25 mm. The aluminum sheet metal has a tensile strength 310 MPa. Determine the minimum tonnage press (force) to perform the blanking and punching operation (1) assume that blanking and punching occur simultaneously and (2) assume that punching occurs first, then blanking, Take: Ac-0.06arrow_forwardQuestion 6 6.1 A round wire made from 1020 carbon steel is being drawn from a diameter of 12.5 mm to 9.5 mm in a draw die of 10°. For a coefficient of friction of 0.15, calculate required drawing force. 6.2 How would the extrusion process be effected if the die angle is increased?arrow_forwardCalculate (1) die pressure distribution and (2) forging force for plane strain forging (open die forging). Assume yield strength of the material is Y, and yielding criterion is von Mises. ho 2Lo h Forged to 2L xdx L 'x+value Note: Assume Zo Constant Plane strain Die pressure distribution h L L Die pressure distribution h MATERIAL L dx -(-1) Friction Hill Y L When 0; =Y P=Y' = Calculate forging force X L dF elemental volume Average pressurearrow_forward
- You have been asked to work on some design problems and technically support the team working on extrusion and forging operations: 1) The team are extruding a billet that is 80 mm long with diameter of 40 mm is directly to a diameter of 20 mm. The extrusion die has a die angle of 75°, see Figure 1. For the work metal, K = 600 MPa and n = 0.25. In the Johnson extrusion strain equation, a = 0.8 and b = 1.4. Remaining billet length 75 Ram pressure, p D. Dr Figure 1: Extrusion process. Determine the following design parameters: (a) Extrusion ratio. (b) True strain (homogeneous deformation). (c) Extrusion strain. (d) Ram pressure at L= 80, 40, and 10 mm. (e) Draw the relationship between the ram pressure and billet length and discuss the results. What are your recommendations to dccrcase the required ram pressure?arrow_forwardA 10 mm thick plate is rolled to 7 mm thick in a rolling mill using 1000 mm diameter rigid rolls. The neutral point is located at an angle of 0.3 times the bite angle from the exit. What will be the thickness of the plate at the neutral point.arrow_forwardA blanking operation is to be performed on 2.0 mm thick cold-rolled steel (half hard). The part is circular with diameter 75.0 mm. Calculate the appropriate punch and die sizes for this operation. (Take Allowance coefficient A. = 0.075)arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Types of Manufacturing Process | Manufacturing Processes; Author: Magic Marks;https://www.youtube.com/watch?v=koULXptaBTs;License: Standard Youtube License