Chapter 12.15, Problem 29KCP
To determine
Explain the microstructure of a hardwood tree. Write the differences between diffuse-porous and ring-porous trees microstructures.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
I need it correct and handwritten
For a continuous and aligned fiber-reinforced composite, the modulus of elasticity in the
transverse direction is 4.91 GPa. If the volume fraction of fibers is 0.3 and the modulus of
elasticity of matrix phase is 3.78 GPa, determine the modulus of elasticity of composite in
longitudinal direction.
None
Chapter 12 Solutions
Foundations of Materials Science and Engineering
Ch. 12.15 - Define a composite material with respect to a...Ch. 12.15 - Prob. 2KCPCh. 12.15 - What are some of the advantages of glass...Ch. 12.15 - Prob. 4KCPCh. 12.15 - Prob. 5KCPCh. 12.15 - What properties make carbon fibers important for...Ch. 12.15 - Prob. 7KCPCh. 12.15 - Prob. 8KCPCh. 12.15 - Prob. 9KCPCh. 12.15 - Prob. 10KCP
Ch. 12.15 - Prob. 11KCPCh. 12.15 - Prob. 12KCPCh. 12.15 - Prob. 13KCPCh. 12.15 - Prob. 14KCPCh. 12.15 - Prob. 15KCPCh. 12.15 - Describe the sheet-molding compound manufacturing...Ch. 12.15 - Prob. 17KCPCh. 12.15 - Prob. 18KCPCh. 12.15 - What are the basic raw materials for portland...Ch. 12.15 - What are the names, chemical formulas, and...Ch. 12.15 - List the five main ASTM types of portland cement...Ch. 12.15 - What is asphalt? Where is asphalt obtained?Ch. 12.15 - What are chemical composition ranges for asphalts?Ch. 12.15 - What does an asphalt mix consist of? What is the...Ch. 12.15 - Prob. 25KCPCh. 12.15 - What are the subrings of the annual growth rings...Ch. 12.15 - Prob. 27KCPCh. 12.15 - Prob. 28KCPCh. 12.15 - Prob. 29KCPCh. 12.15 - Prob. 30KCPCh. 12.15 - Prob. 31KCPCh. 12.15 - Prob. 32AAPCh. 12.15 - Prob. 33AAPCh. 12.15 - Prob. 34AAPCh. 12.15 - Prob. 35AAPCh. 12.15 - Prob. 36AAPCh. 12.15 - Prob. 37AAPCh. 12.15 - Prob. 38AAPCh. 12.15 - Prob. 39AAPCh. 12.15 - A unidirectional carbon fiberepoxy resin composite...Ch. 12.15 - Prob. 41AAPCh. 12.15 - Prob. 42AAPCh. 12.15 - Prob. 43AAPCh. 12.15 - Prob. 44AAPCh. 12.15 - Prob. 45AAPCh. 12.15 - If the tensile strength of the Kevlar 49 fibers is...Ch. 12.15 - Prob. 47AAPCh. 12.15 - Prob. 48AAPCh. 12.15 - Prob. 49AAPCh. 12.15 - Prob. 50AAPCh. 12.15 - Prob. 51AAPCh. 12.15 - What types of chemical reactions occur during the...Ch. 12.15 - Prob. 53AAPCh. 12.15 - Which component of portland cement hardens rapidly...Ch. 12.15 - Prob. 55AAPCh. 12.15 - Prob. 56AAPCh. 12.15 - Prob. 57AAPCh. 12.15 - Prob. 58AAPCh. 12.15 - Prob. 59AAPCh. 12.15 - Prob. 60AAPCh. 12.15 - Prob. 61AAPCh. 12.15 - Prob. 62AAPCh. 12.15 - Prob. 63AAPCh. 12.15 - Prob. 64AAPCh. 12.15 - Prob. 65AAPCh. 12.15 - Prob. 66AAPCh. 12.15 - Prob. 67AAPCh. 12.15 - Prob. 68AAPCh. 12.15 - Prob. 69AAPCh. 12.15 - What characteristics are desirable for the...Ch. 12.15 - Prob. 71AAPCh. 12.15 - Prob. 72AAPCh. 12.15 - Prob. 73AAPCh. 12.15 - Prob. 74AAPCh. 12.15 - Prob. 75AAPCh. 12.15 - Prob. 76AAPCh. 12.15 - Prob. 77AAPCh. 12.15 - Why does wood shrink much more in the transverse...Ch. 12.15 - A newly developed metal-matrix composite is made...Ch. 12.15 - Prob. 81AAPCh. 12.15 - Prob. 82AAPCh. 12.15 - Prob. 83AAPCh. 12.15 - Prob. 84AAPCh. 12.15 - Prob. 85AAPCh. 12.15 - Prob. 86AAPCh. 12.15 - Prob. 87SEPCh. 12.15 - Prob. 88SEPCh. 12.15 - Prob. 89SEPCh. 12.15 - Prob. 90SEPCh. 12.15 - Prob. 91SEPCh. 12.15 - Prob. 92SEPCh. 12.15 - (a) In Problem 12.94, if all three beams are to...Ch. 12.15 - Prob. 97SEPCh. 12.15 - Prob. 98SEPCh. 12.15 - Prob. 99SEPCh. 12.15 - Prob. 100SEPCh. 12.15 - Prob. 101SEPCh. 12.15 - Prob. 102SEPCh. 12.15 - Prob. 103SEPCh. 12.15 - Prob. 104SEPCh. 12.15 - In total hip replacement, most surgeons prefer a...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Example 1 A continuous and aligned glass fiber-reinforced composite consists of 40 vol% of glass fibers having a modulus of elasticity of 69 GPa and 60 vol% of a polyester resin that, when hardened, displays a modulus of 3.4 GPa. (a) Compute the modulus of elasticity of this composite in the longitudinal direction.arrow_forwardIt is desired to produce an aligned and continuous fiber-reinforced epoxy composite having a maximum of 50% fibers. A minimum longitudinal modulus of elasticity of 55 GPa and a minimum tensile strength of 1200 MPa are required. E-glass and carbon (PAN standard modulus) fibers are the possible candidates to select. In addition, assume the stress levels on the epoxy matrix at fiber failure are 70 MPa for E-glass fiber and 30MPa for carbon fiber, respectively. Which fiber meets the design requirement? Use the properties given in the Table below to evaluate your selection. Materials Epoxy matrix E-glass Carbon Modulus of Elasticity (GPa) 3.1 72.5 230 Tensile Strength (MPa) 69 3450 4000arrow_forwardFor a glass/epoxy lamina with a 70% fiber volume fraction using the properties in the tables provided below (a) Find the ultimate tensile strength. (b) Find the minimum and critical fiber volume fractions related to (a). (c) Find the compressive strength when the matrix undergoes extension mode and when the matrix undergoes shear mode, which one controls the compressive failure? Property Axial modulus Transverse modulus Axial Poisson's ratio Transverse Poisson's ratio Shear modulus Axial tensile strength Axial compressive strength Transverse tensile strength Transverse compressive strength Shear strength Epoxy Glass Units 3.4 85 GPa 3.4 85 GPa 0.3 0.20 0.3 0.20 1.308 35.42 GPa 72 1550 MPa 102 1550 MPa 72 1550 MPa 102 1550 MPa 34 35 MPaarrow_forward
- Explain what the following terms mean:decomposition temperature, heat distortion temperature, glass-transition temperature, and melting temperature. Why is itthat thermoplastics do not have a fixedmelting or glass-transition temperature?arrow_forwardA unidirectional fiber reinforced composite contains Kevlar 49 fibres and epoxy resin. the fibers are to carry 88% of a load applied in the longitudinal direction. determine the volume fraction of fibers that will be required ( two decimal places, e.g. 0.31).( elastic modulus of Kevlar 49 is 129GPA, and elastic modulus of epoxy 4.6 GPaarrow_forwardMaterial Sciencearrow_forward
- A discontinuous fibre reinforced composite consists of 20mm long carbon fibres in a polymer matrix. The volume fraction of the composite is 0.5, interfacial shear strength 5MPa and the critical fibre length 2.5mm. The fibre modulus is 250GPa and strain to failure 1.5%. The matrix modulus is 3.5GPa and failure strain 10%. Calculate the tensile strength of the composite in the fibre direction. Answer: 3564arrow_forwardNeed correctly.arrow_forwardA continuous and aligned glass fiber-reinforced composite with modulus of elasticity of 55 GPa. The volume fiber fraction is 40 and the modulus of elasticity of the fiber is 75 GPa. Calculate the volume fraction of epoxy matrix if you know the modulus of elasticity of the modulus of elasticity of the matrix is 2.5 GPa and then determine the strain that is sustained by each phase under applied stress of 27 Mpa. (assume that the cross-section area is 150 mm2)arrow_forward
- A composite with a minimum elastic modulus of 50 GPa is to be created by mixing uniaxial epoxy with metal fibre. Calculate the minimum Elastic modulus of the metal fibre given the following data for the epoxy matrix: Elastic modulus of the epoxy matrix is 5 GPa • Volume fraction of the epoxy matrix is 0.6 A- в I U S x2 xarrow_forwardA composite with a vinyl ester (VE) matrix contains 2 vol% CNTS with the following characteristics: 1= 7 um, d= 50 nm, di = 4 nm, and EcCNT = 900 GPa. The modulus of the VE matrix is 1.9 GPa. %3D c. Find the Major Poisson's ratio for this composite using strength of materials approach. d. Find the in-plane shear modulus for this composite using strength of materials approach.arrow_forwardb. i. Calculate the tensile modulus of elasticity of a unidirectional Kevlar-49 fibers epoxy composite material that contains 63% by volume of Kevlar 49 fibers and is stressed under isostrain conditions. The Kevlar 49 fibers have a tensile modulus of elasticity of 189.8 GPa and the epoxy matrix a tensile modulus of elasticity of 3.8 GPa.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
composite-materials; Author: Tonya Coffey;https://www.youtube.com/watch?v=Vu6ik-bcKf4;License: Standard youtube license