The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained. Concept introduction: The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300 − 2000 ° C to decrease the voids between atoms and increase the density.

Question

Want to see the full answer?

Answer 1

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

If a reaction occurs, what would be the major products? Please include a detailed explanation as well as a drawing showing how the reaction occurs and what the final product is.

Please help me answer the following questions using the data I included. 1&2

Assign all the Protons in HNMR

Answer 2

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 3

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 4

Question

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 5

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Answer 6

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Answer 7

Chapter 12, Problem 12.133SP

Interpretation Introduction

Interpretation:

The reason that explains silicon carbide-reinforced alumina is stronger and tougher than pure alumina should be explained.

Concept introduction:

The process that results in a final product of ceramic material from raw material is known as ceramic processing. The ceramic processing starts with a fine powder of raw material combined by an organic binder. Then it is shaped, compacted and at last sintered at a temperature of 1300−2000 °C to decrease the voids between atoms and increase the density.

Answer 8

Expert Solution & Answer

Answer 9

Expert Solution & Answer

Answer 10

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 11

Ch. 12 - Calcium metal crystallizes in a cubic...Ch. 12 - Polonium metal crystallizes in a simple cubic...Ch. 12 - Polonium metal crystallizes in a simple cubic...Ch. 12 - The density of a sample of metal "as measured to...Ch. 12 - Zinc sulfide crystallizes in the following cubic...Ch. 12 - Prob. 12.6A Ch. 12 - Prob. 12.7P Ch. 12 - Prob. 12.8A Ch. 12 - Prob. 12.9P Ch. 12 - Prob. 12.10A

Solution Summary: The author explains the process that results in a final product of ceramic material from raw material is known as ceramic processing. The strength and ture toughness of these ceramics can be increased through reinforced by whiskers.

Concept explainers

Want to see the full answer?

Chapter 12 Solutions