Textbook Question
Chapter 11, Problem 11.31QP
A circular FRP composite rod with continuous and aligned fibers has a 3 in. diameter. The rod is simply supported with a span of 4 ft and is subjected to three-point bending with a 270 lb center load.
a. If the maximum allowable center deflection cannot exceed 0.02 in., what is the minimum modulus of the composite in order to meet this requirement?
b. If the FRP has a modulus as obtained in Part a and the moduli of the matrix and the fibers are 0.5 × 106 psi and 20 × 106 psi, respectively, what is minimum percent of fibers that meets this requirement?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Explain
IV- It is necessary to design a continuous and aligned glass fiber-reinforced
polyester having a tensile strength of at least 1400 MPa in the longitudinal direction.
The maximum possible specific gravity is 1.65. Using the following data, determine
whether such a composite is possible. Justify. Assume a value of 15 MPa for the
stress on the matrix when the fibers fail.
Material
Glass fiber
Polyester
Specific gravity
2.5
1.35
Tensile strength
(MPa)
3500
50
A circular FRP composite rod with continuous and aligned fibers has a 3 in. diameter. The rod is simply supported with a span of 4 ft and is subjected to three-point bending with a 270 lb center load.
a. If the maximum allowable center deflection cannot exceed 0.02 in., what is the minimum modulus of the composite in order to meet this requirement?
b. If the FRP has a modulus as obtained in Part a and the moduli of the matrix and the fibers are 0.5 × 10" psi and 20 × 10* psi, respectively. what is minimum percent of fibers that meets this requirement?
Chapter 11 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 11 - Prob. 11.1QPCh. 11 - Prob. 11.2QPCh. 11 - Prob. 11.3QPCh. 11 - Prob. 11.4QPCh. 11 - Prob. 11.5QPCh. 11 - Prob. 11.6QPCh. 11 - Prob. 11.7QPCh. 11 - Prob. 11.8QPCh. 11 - Prob. 11.9QPCh. 11 - What are the functions of aggregate used in...
Ch. 11 - Prob. 11.11QPCh. 11 - Prob. 11.12QPCh. 11 - What are the benefits of adding dispersed steel...Ch. 11 - Getting measurements from Figure 11.20, determine...Ch. 11 - Three 6 in. 12 in. concrete cylinders with...Ch. 11 - Prob. 11.16QPCh. 11 - Prob. 11.17QPCh. 11 - Prob. 11.18QPCh. 11 - Prob. 11.19QPCh. 11 - Prob. 11.20QPCh. 11 - Prob. 11.21QPCh. 11 - Prob. 11.22QPCh. 11 - Prob. 11.23QPCh. 11 - Prob. 11.24QPCh. 11 - Prob. 11.25QPCh. 11 - Prob. 11.26QPCh. 11 - Prob. 11.27QPCh. 11 - Prob. 11.28QPCh. 11 - Prob. 11.29QPCh. 11 - Prob. 11.30QPCh. 11 - A circular FRP composite rod with continuous and...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- In Example Problem 12.1, a uniaxial composite material is made into a circular rod Vbith a 1.27-cm diameter from 70 volume percent continuous carbon fibers and 30 volume percent epoxy. The rod is subject to an axial force of 100,000 N. The composite matcrial in Example Problem 12.1 is to be replaced with a less expensive composite made of 70 volume percent continuous E-glass fibers and 30 volume percent epoxy. The elastic moduli are 5 GPa for the epoxy resin and 72.4 GPa fos the E-glass. (a) Compare the elastic modulus, composite strain, fiber and matrix stresses, and density of this composite with the carbon epoxy composite in Example Problem 12.1. Usc the density of UHM carbon, and assume the density of the epoxy is 1.2g/cm3 . (b) Can both the E-glass fiber and matrix withstand the applied force?arrow_forwardEstimate the transverse tensile strength of the concrete in Problem 12.6.arrow_forwardA circular FRP composite rod with continuous and aligned fibers has a3 in. diameter. The rod is simply supported with a span of 4 ft and is subjected to three-point bending with a 270 lb center load.a. If the maximum allowable center deflection cannot exceed 0.02 in.,what is the minimum modulus of the composite in order to meet this requirement?b. If the FRP has a modulus as obtained in Part a and the moduli of the matrix and the fibers are 0.5 * 106 psi and 20 * 106 psi, respectively, what is minimum percent of fibers that meets this requirement?arrow_forward
- Question 2 Calculate the bending stress at the bottom edge of the following composite beam subject to a bending moment of M= 1500 Nm. The lower section is made from steel (E = 200 GPa) and the upper section is made from aluminium (E = 70 GPa). All dimensions are in mm. 100 YA 100 Z 10 >arrow_forwardGive me right solution according to the questionarrow_forwardA steel bar and an aluminum bar are bonded together as shown to form a composite beam. Knowing that the vertical shear in the beam is 4 kips and that the modulus of elasticity is 29 * 106 psi for the steel and 10.6 *106 psi for the aluminum, determine (a) the aver-age shearing stress at the bonded surface, (b) the maximum shearing stress in the beam.arrow_forward
- The composite shaft, consisting of aluminum, copper, and steel sections, is subjected to the loading shown. The cross-sectional areas of sections AB, BC, and CD are AAB = 0.08 in², ABC = 0.11 in², and Acp = 0.06 in², respectively. The modulus of elasticity for each section are shown in the figure. Neglect the size of the collars at B and C.arrow_forwardThe load-strain data obtained in a tension test of a unidirectional carbon fiber/epoxy composite are given below. The specimen dimensions are length=254 mm, width=12.7 mm and thickness is 1.4 mm. Determine the tensile modulus and Poisson ration for each fiber orientation Axial strain Load (N) Transverse strain % 自 % 0° 45° 90° 0° 45° 90° 0.05 2130 130 67 -0.012 -0.113 -0.0004 0.10 4270 255 134 -0.027 -0.021 -0.001 0.15 6400 360 204 -0.041 -0.029 -0.0014 0.20 8620 485 333 -0.054 -0.038 -0.0019 0.25 565 396 -0.048 -0.0025arrow_forwardSub question: At what temperature will the aluminum and steel segments in this problem have stresses of equal magnitude after the 50-kip force is applied? Show full solutionarrow_forward
- A composite beam is made of two brass [E - 111 GPa] bars bonded to two aluminum [E - 72 GPa] bars, as shown. The beam is subjected to a bending moment of 250 N-macting about the z axis. Using a - 10 mm, b- 65 mm, c- 20 mm, and d- 45 mm, calculate (a) the maximum bending stress in the aluminum bars. (b) the maximum bending stress in the brass bars. Aluminum Brass Brass Aluminum Answers: (a) Oa i MPa (b) Oer MPa Save for Later Attempts: 0 of 1 used Submit Answerarrow_forwardQ1 A cantilever composite beam is formed by bonding together brass bar (EB = 100 GPa) and aluminium (EA = 70 GPa) with cross section and loading at free end as shown in Figure Q1. Parameter x, y, and z are given by: X=0 Y=0 Z=2 (a) Determine the centroid and the moment of inertia of the composite section. (b) Calculate the maximum tensile and compressive stresses in the brass and aluminium. brass 5x mm (10 mm 20mm |4y mm 0.5(4y) mm M=2.z kN.m 4y mm aluminium Figure Q1 |arrow_forwardDetermine the y-bar centroid of the composite figure shown. Where: y = 20mm and x = 10 mmarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
The History of Composite Materials, From Brick to Bakelite to Biomimetic Hybrids; Author: Autodesk;https://www.youtube.com/watch?v=VS_Kg-VEvzE;License: Standard YouTube License, CC-BY