Question
Chapter 10, Problem 10.23QP
a)
To determine
Draw the graph between load and deflection using spread sheet.
b)
To determine
Plot the proportional limit on the graph.
c)
To determine
The modulus of rupture of the wood specimen.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A wood specimen was prepared with actual dimensions of 25 mm * 25 mm *
150 mm and grain parallel to its length. Displacement was measured over a
100 mm gauge length. The specimen was subjected to compression parallel to
the grain to failure. The load-deformation results are as shown in Table P10.24.
TABLE P10.23
Deflection
Load (N)
(10 3 mm)
445
709
890
1412
1335
2113
1779
2825
2224
3556
2669
4234
3114
4935
3559
5644
4003
6353
4448
6995
4893
7996
5338
9131
5783
10287
6228
11902 (failure)
TABLE P10.2 4
Load (N)
Displacement (mm)
31
0.30
45
1.73
387
4.17
2358
4.57
7584
5.28
12740
5.99
16859
6.81
20489
7.62
23745
8.23
22757
9.14
19875
9.75
19265
10.5
a. Using a computer spreadsheet program, plot the stress-strain relationship.
b. Calculate the modulus of elasticity.
c. What is the failure stress?
SOM 1. Show your detailed/correct solution.
please solve it quickly, thanks ❤️
Chapter 10 Solutions
EBK MATERIALS FOR CIVIL AND CONSTRUCTIO
Ch. 10 - What are the two main classes of wood? What is the...Ch. 10 - Prob. 10.2QPCh. 10 - Prob. 10.3QPCh. 10 - Discuss the anisotropic nature of wood. How does...Ch. 10 - Prob. 10.5QPCh. 10 - Prob. 10.6QPCh. 10 - Prob. 10.7QPCh. 10 - Prob. 10.8QPCh. 10 - Prob. 10.9QPCh. 10 - Prob. 10.10QP
Ch. 10 - Prob. 10.11QPCh. 10 - Prob. 10.12QPCh. 10 - Prob. 10.13QPCh. 10 - Prob. 10.14QPCh. 10 - Prob. 10.15QPCh. 10 - Prob. 10.16QPCh. 10 - Prob. 10.17QPCh. 10 - Prob. 10.18QPCh. 10 - Prob. 10.19QPCh. 10 - Prob. 10.20QPCh. 10 - Prob. 10.21QPCh. 10 - Prob. 10.22QPCh. 10 - Prob. 10.23QPCh. 10 - A wood specimen was prepared with actual...Ch. 10 - A pine wood specimen was prepared with actual...Ch. 10 - Prob. 10.26QPCh. 10 - Prob. 10.27QPCh. 10 - Prob. 10.28QPCh. 10 - Prob. 10.29QPCh. 10 - Prob. 10.30QPCh. 10 - Prob. 10.31QPCh. 10 - Prob. 10.32QPCh. 10 - Prob. 10.33QP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- A 32-mm rebar with a gauge length of 200 mm was subjected to tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in TableUsing a spreadsheet program obtain the following:a. A plot of the stress–strain relationship. Label the axes and show units.b. A plot of the linear portion of the stress–strain relationship. Determine modulus of elasticity using the best-fit approach.c. Proportional limit.d. Yield stress.e. Ultimate strength.f. If the rebar is loaded to 390 kN only and then unloaded, what is the permanent change in length?arrow_forwardA composite section shown in Figure (2) consisted of a rectangular and triangular sections with a semicircle hole as shown in Fig. Locate the centroid (x, y) of this section using the below table. Y Area 90 mm A, X: A; Y; A (mm) (mm) (mm') | (mm') Part 20 mm (mm') +Yellow 120 mm rectangle 40 mm + Blue triangle 20 mm - White 60 mm semicircle Totals X= Y= Figure (2)arrow_forward1. For the 15 foot copper bar shown in the figure below, find the total elongation (or shrinkage). The bar has a square cross section of 2" x 2" ( 16,000 lbs 4000 lbs 12' Punch Force 12000 lbs 2. A metal plate is 125 inch thick. What force is required to punch out a square piece 1" x 1"? The ultimate shear stress of the metal is 37,000 psi, and the ultimate tensile stress is 60,000 psi.arrow_forward
- Question No.1 : A 32-mm rebar with a gauge length of 200 mm was subjected to tension to fracture according to ASTM E-8 method. The load and deformation data were as shown in table below. Using calculations and diagram obtain the following: a. A plot of the stress-strain relationship. Label the axes and show units. b. A plot of the linear portion of the stress-strain relationship. Determine modulus of elasticity using the best-fit approach. c. Proportional limit. d. Yield stress. e. Ultimate strength. f. Modulus of resilience and toughness. g. If the rebar is loaded to 390 kN only and then unloaded, what is the permanent change in length? Load (kN) Displacement (mm) Load (kN) Displacement (mm) 472.9 8.4 62.2 0.1 487.1 9.7 188.9 0.2 496.4 11.1 329.8 0.4 505.7 12.4 383.4 1.7 512.8 13.7 426.0 4.0 522.6 15.3 447.3 5.9 532.4 18.5 462.5 7.2 525.9 22.4arrow_forwardPlease fill in all sectionsarrow_forwardPlease answer complete questionarrow_forward
- A pine wood specimen was prepared with actual dimensions of 50 mmx50 mm x 250 mm and grain parallel to its length. The deformation was measured over a gauge length of 200 mm. The specimen was subjected to compression parallel to the grain failure. The load- deformation results are shown in table below: Load (kN) Deformation (mm) 8.9 0.457 17.8 0.597 26.7 0.724 34.5 0.838 43 0.965 52.9 1.118 62.01 1.27 71.03 1.422 80.1 1.588 89 1.765 99.6 1.956 108 2.159 111.3 2.311 112 2.456 a. Using a computer spreadsheet program, plot the stress-strain relationship. b. Calculate the modulus of elasticity. С. What is the failure stress?arrow_forwardA round steel bar with a diameter of 12.5 mm and a gauge length of 50 mm was subjected to tension to rupture following ASTM E-8 test procedure. The load and deformation data were as shown in Table P3.30. Using a spreadsheet program obtain the following: a. A plot of the stress-strain relationship. Label the axes and show units. b. A plot of the linear portion of the stress-strain relationship. Determine modulus of elasticity using the best fit approach. c. Proportional limit. d. Yield stress. e. Ultimate strength. f. When the applied load was 18 kN, the diameter was measured as 12.7 mm Determine Poisson's ratio. g. After the rod was broken, the two parts were put together and the diameter at the neck was measured as 10.6 mm What is the true stress value at fracture? Is the true stress at fracture larger or smaller than the engineering stress at fracture? Why? h. Do you expect the true strain at fracture to be larger or smaller than the engineering strain at fracture? Why? TABLE P3.30…arrow_forwardProblem 20.2 Concrete has a notable capacity against compression stresses but very little capacity against tension stresses (it cracks easily). One strategy to counteract this weakness in tension involves using wires or rods to prestress the concrete beam in regions where flexural tension can be anticipated. Consider the simply-supported beam shown, which has a rectangular cross section of 18" x 12". If concrete has specific weight of 150 pcf (pounds per cubic foot) determine the required tension in rod AB, which runs through the beam so that no tensile stress is developed in the concrete at its center section a-a. Neglect the size of the rod and any deflection of the beam. a 16 in. B 2 in. 18 in. 6 in. 6 in. -4 ft- - 4 ft Tip: the beam's self-weight causes and internal moment at the midspan section and therefore flexural tension stress at the bottom of the beam. When the rod is tensioned it applies both an axial stress and a bending moment (since it is applied eccentrically on the…arrow_forward
- Problem # 2: For the composite area shown, calculate the moment of inertia about X and Y ахes. 95 mm Ŕ = 60 mm 55 mm 35 mm 70 mm 80 mm 125 mmarrow_forward1.7arrow_forwardENGINEERING MECHANICS (STATICS) Topic: Centroids Answers in the third place value after the decimal place. Place in it a box.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Structural Analysis (10th Edition)Civil EngineeringISBN:9780134610672Author:Russell C. HibbelerPublisher:PEARSON
Principles of Foundation Engineering (MindTap Cou...Civil EngineeringISBN:9781337705028Author:Braja M. Das, Nagaratnam SivakuganPublisher:Cengage Learning
Fundamentals of Structural AnalysisCivil EngineeringISBN:9780073398006Author:Kenneth M. Leet Emeritus, Chia-Ming Uang, Joel LanningPublisher:McGraw-Hill Education
Traffic and Highway EngineeringCivil EngineeringISBN:9781305156241Author:Garber, Nicholas J.Publisher:Cengage Learning
Structural Analysis (10th Edition)
Civil Engineering
ISBN:9780134610672
Author:Russell C. Hibbeler
Publisher:PEARSON
Principles of Foundation Engineering (MindTap Cou...
Civil Engineering
ISBN:9781337705028
Author:Braja M. Das, Nagaratnam Sivakugan
Publisher:Cengage Learning
Fundamentals of Structural Analysis
Civil Engineering
ISBN:9780073398006
Author:Kenneth M. Leet Emeritus, Chia-Ming Uang, Joel Lanning
Publisher:McGraw-Hill Education
Traffic and Highway Engineering
Civil Engineering
ISBN:9781305156241
Author:Garber, Nicholas J.
Publisher:Cengage Learning