Which of the following is correct forLow Heat CementHeat of hydration is reduced bytricalcium aluminate contentSuitable for use in cold weatherareasSuitable for use in Hot weatherareasThis cement requires longer periodof curingHydration of cement is due tochemical action of water with *Tetra calcium AluminoferriteTricalcium silicate and DicalciumsilicateTricalcium aluminate and Tricalciumalumino ferriteGypsum

Which of the following is correct for Low Heat Cement * Heat of hydration is reduced by tricalcium aluminate content Suitable for use in cold weather areas Suitable for use in Hot weather areas This cement requires longer period of curing

Which of the following is correct for Low Heat Cement * Heat of hydration is reduced by tricalcium aluminate content Suitable for use in cold weather areas Suitable for use in Hot weather areas This cement requires longer period of curing

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: 12-. can cause unsoundness of cement. b - Alkalis C- Cao a- sulfate compounds 13- At any stage of…

A: d )CaO and Mgo can cause unsoundness in cement . Option d is correct as lime and magnesia are…

Q: ASTM C127 is the Standard Test Method for Density, Relative Density (Specific Gravity), and…

A: Given data in question ASTM C127 For density, Relative density and absorption capacity To find out…

Q: Once in civil engineering, what is the minimum curing period typically recommended for concrete…

A: In civil engineering, the minimum curing period for concrete structures typically depends on the…

Q: Problems: Identify the following as Element (E), Compound (C), Homogeneous Mix (HOM) or…

Q: 1. What colour is ABS solvent cement? a. Grey b. Green c. White d. Yellow 2. What colour is primer…

A: 1. What colour is ABS solvent cement? a. Grey b. Green c. White d. Yellow Answer : The color of ABS…

Q: For the continuous steel W12x14 beam A-B-C shown below, perform the following: (a) Compute the…

A: LAB = 6 feet LBC = 8 feet

Q: at is the foundation bearing pressure beneath

Q: Amswer the following questions: Part I (True or False) 1) Aggregates having high absorption value…

A: 1) False - Aggregate having low absorption ratio are preferable for concrete so that water- cement…

Q: What are the two main reasons that steel corrodes inside reinforced concrete? ingress of chlorides…

A: Two major factors which cause corrosion of rebars in concrete structures are carbonation and ingress…

Q: What is the weakest property of concrete? The compressive strength of the coarse aggregate The…

A: What is the weakest property of concrete?The compressive strength of the coarse aggregateThe…

Q: Which of the following statements is correct? A) Pozzolans react with Calcium Silicate Hydrate…

A: Pozzolans are silicate-based compounds that combine with the calcium hydroxide produced whenever…

Q: advantage of fluid loss additive? a. Increase free water of cement slurries b. Maximize formation…

A: Which of the following is advantage of fluid loss additive? a. Increase free water of cement…

Q: During the transformation of C3A, the strength of the cement paste lead to decrease in at the late…

A: The transformation of calcium aluminates hydrate from the meta stable hexagonal form to the stable…

Concept explainers

Types of Cement

Cement is a fine mixture of limestone, chalk, or marl and clay which when mixed with water, becomes compacted due to the formation of strong molecular bonds. Due to hydration, cement turns into a hard mass when left for a sufficient amount of time upon mixing with water. The water turns the cement compounds into gel-like submicroscopic particles having higher surface areas. It is due to the hydration properties of cement, they are often known as hydraulic cement. For instance, Portland cement is a popular example in this category.

Question

Which of the following is correct for
Low Heat Cement
Heat of hydration is reduced by
tricalcium aluminate content
Suitable for use in cold weather
areas
Suitable for use in Hot weather
areas
This cement requires longer period
of curing
Hydration of cement is due to
chemical action of water with *
Tetra calcium Aluminoferrite
Tricalcium silicate and Dicalcium
silicate
Tricalcium aluminate and Tricalcium
alumino ferrite
Gypsum

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Design a concrete mix according to the following conditions: Design Specifications Concrete ramp (not reinforced) Slab thickness =270 mm Design strength (fc) = 25.5 MPa Standard deviation s= 1.86 MPa on 200 specimens Environment = Severe exposure to freeze-thaw and de-icing chemicals Slump = 50 mm Materials Available Cement: Type GU; specific gravity 3.15 Admixture: Air entraining admixture 8 ml/1% air/100 kg cement . Coarse Aggregate: Nominal maximum size = 37.5 mm Type = Crushed stone Bulk oven-dry specific gravity = 2.63 Absorption = 2.1% Oven-dry rodded density = 1755 kg/m3 Moisture content = 1.5% Fine Aggregate Type = Natural sand Bulk oven-dry specific gravity = 2.55 Absorption = 3.1% Moisture content = 4.3% Fineness modulus = 2.40
At saturated surface dry (SSD) an aggregate's moisture condition is equal to its: air dry absorption capacity oven dry maximum absorbed volume
(a) In general, which provides better fire performance, carbonate or silicate aggregates? Why? (b) Why does fire design incorporate a load reduction factor (Dfire) = 1.0? (c) Two identical beams (Beam 1 is simply supported, and Beam 2 is fully restrained) are heated under similar conditions. What does the mechanical strain equal to in each of these beams? (d) A design office located in Clemson, SC (with a branch in San Francisco, CA) envisions designing a new composite member made of steel and timber. This to-be designed member is expected to be used in wildfire-prone regions primarily for single family homes. Comment on how you would design such a member to achieve superior fire performance. (e) Plot and discuss the expected degradation faces in three bending elements (say, beams) to be made from concrete, steel and timber?
Listen Concrete is required for the construction of an agricultural dairy barn floor slab in Central Alberta. The floor slab will be exposed to freeze/thaw conditions. Which of the following exposure classes best describes the environmental conditions that the concrete will be exposed to? A) A-2 B) A-4 OC) S-1 OD) S-2 APIO--:--) OLDG BO
The relative amounts of the four chemicals in the final cement depends on the desired properties of the cement concrete. The table below gives the typical compound composition of different types of Portland cements Compound Composition No. C3S C,S C3A C4AF 1 60 13 9. 8 40 40 4 3 26 50 5 12 4 50 24 11 5 42 33 5 13 Depending on the properties of the different chemicals and their relative composition, identify the high early strength (HE) and low-heat (LH) cements from the table. Give detail explanation for your answer
Both weathered chert and sound quartz pieces are common constituents in stream gravels. Both have the chemical formula SiO2. Yet the weathered chert is an unsound material in concrete when subjected to freezing and thawing cycles, whereas quartz does not have this problem. Explain why this is the case.
Hardening of concrete is caused by "Hydration" True False
In the solution with the same concentration, strength loss of the hardened cement paste soaked in magnesium sulfate solution was less than that in sodium sulfate solution. why?
The strength of cement is determined by a number of factors.
The two main raw materials needed for manufacturing ordinary portland cement are