In the solution with the same concentration, strength loss of the hardened cement paste soaked in magnesium sulfate solution was less than that in sodium sulfate solution.why? Summary of compressive strength evolution in sulphate environment (%)MGSO4solution (%)NazSO,+M9SO4solution (%)Sample IDNazSO4solution (%)ОРС-30-21-35OPC+FA-14-4.8-19

Compressive strength is generally the capacity of concrete to withstand loads before failure.…

Answered: In the solution with the same…

In the solution with the same concentration, strength loss of the hardened cement paste soaked in magnesium sulfate solution was less than that in sodium sulfate solution. why

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: What is the minimum strength that concrete must reach prior to freezing so that the overall strength…

A: The minimum strength that concrete mus overall strength gain is not affected:

Q: ASTM C127 is the Standard Test Method for Density, Relative Density (Specific Gravity), and…

A: Given data in question ASTM C127 For density, Relative density and absorption capacity To find out…

Q: Which compound of cement is responsible for strength of cement? a. Magnesium oxide b. Silica c.…

A: Magnesium oxide It imparts strength and soundness to cement. Cement become unsound if it is in…

Q: Rate of Tricalcium silicate (C3S) is higher in Type III cement.

A: Given statement: Rate of Tricalcium silicate (C3S) is higher in type III cement. Tricalcium…

Q: choose the correct option please Silica fume admixture increase concrete strength up to 60 MPa 120…

A: This question is related to Concrete technology from Civil Engineering. In this question ask about…

Q: The name of the test used to measure the consistency and workability of fresh concrete is called the…

A: The name of the test used to measure the consistency and workability of fresh concrete is called the…

Q: Hydration of cement is exothermic process that generates heat. The table below shows the heat…

A: Option-a:This option implies that utilizing any of the specified cement components is unsuitable for…

Q: We require a mix with a mean 28-day compressive strength of 28 MPa. The slump is selected to be 40…

Q: In the manufacture of Portland cement, gypsum is added to the clinker and they are pulverised…

A: Solution- a) i) Gypsum is a long-lasting admixture. ii) The addition of gypsum to the clinker…

Q: Amswer the following questions: Part I (True or False) 1) Aggregates having high absorption value…

A: 1) False - Aggregate having low absorption ratio are preferable for concrete so that water- cement…

Q: Hydration of cement is due to chemical action of water with * Gypsum Tricalcium aluminate and…

A: Option D is correct...

Q: what is the main chemical reaction that during the production and hydration process of cement.

A: The main chemical reaction during the production and hydration process of cement is "Hydration of…

Q: Increasing the amount of sand in a concrete usually decreases the amount of water needed to make the…

A: Thank you for the question . As per honour code we are allowed to answer three sub parts at a time…

Q: In proportioning a concrete mix, the coarse and fine aggregates had the following properties…

A: Coarse aggregate weight = 800 lbDry aggregate weight = 350 lb

Q: What is the weakest property of concrete? The compressive strength of the coarse aggregate The…

A: What is the weakest property of concrete?The compressive strength of the coarse aggregateThe…

Concept explainers

Reactions with Materials

Limestone

Question

In the solution with the same concentration, strength loss of the hardened cement paste soaked in magnesium sulfate solution was less than that in sodium sulfate solution.

why?

Summary of compressive strength evolution in sulphate environment (%)
MGSO4
solution (%)
NazSO,+M9SO4
solution (%)
Sample ID
NazSO4
solution (%)
ОРС
-30
-21
-35
OPC+FA
-14
-4.8
-19

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

The raw materials used in Portland Cement production are: A) Calcium/Coal/Alumina/Silica B) Alumina/Sandstone/Iron/Coal C) Calcium/Iron/Sandstone/Silica D) Alumina/Silica/Iron/Calcium
Although the constituents of concrete (aggregate and hydrated cement paste) behave in a linear elastic manner if stress is applied to them and the resulting strain is measured, concrete is not a linear elastic material throughout its entire stress-strain curve. What is the main reason for the deviation from this behavior? Interfacial transition zone (ITZ) Incomplete hydration of cementitious phases The loading rate applied according to ASTM C 39 presence of C-S-H very close to the aggregate/paste interface
Which of the following statements is correct? A) Pozzolans react with Calcium Silicate Hydrate (C-S-H) to form Calcium Hydroxide (C-H) B) Pozzolans react with the by-product of cement hydration to produce a denser concrete C) Use of pozzolans in a mix generally improves the durability and strength of the concrete D) b and c
This refers to a change from liquid state to solid state of cement paste.
Most cement slurries will contain some additives to modify the properties of the slurry to produce a better cement job to suit particular requirements. Fluid loss additive helps to maintain constant water to solid ratio in cement slurry. Which of the following is advantage of fluid loss additive? a. Increase free water of cement slurries b. Maximize formation damage c. Changes in slurry rheology is seen d. Prevent stuck pipe
Design a concrete mix for the following performances and ingredients:• Compressive strength at 28 days = 35MPa, slump 85 mm• Crushed coarse aggregate of size 14 mm readily available• Fine aggregate is washed coarse sand, fineness modulus = 2.5• Specific gravity of combined aggregate =2.6• Water absorption of fine aggregate = 5%• Water absorption of coarse aggregate = 3%• Air-dry moisture content of coarse aggregate = 6%• Air-dry moisture content of fine aggregate = 2%
The quality of aggregate packing affects: a) Cement use b) Slump c) Corrosion d) Early cracking
The strength of concrete primarily depends on the:Type of aggregatesWater-cement ratioCuring timeMixing method
Which of the following material is/are used as an accelerator’s additive for cement? a. Sodium Chloride b. Caustic Soda c. Calcium Chloride d. Nitrogen e. Barite f. Bentonite g. Gypsum
Both weathered chert and sound quartz pieces are common constituents in stream gravels. Both have the chemical formula SiO2. Yet the weathered chert is an unsound material in concrete when subjected to freezing and thawing cycles, whereas quartz does not have this problem. Explain why this is the case.
which is considered organic cement from the followings? * all of the mentioned Portland cement lime clay natural resins which is used to mitigate the sulphate problem in lime stabilisation * decrease the mellowing time increase water content all of the mentioned increase the compaction apply all lime required in one shot
Hardening of concrete is caused by "Hydration" True False