Two carburising processes are being compared. Process one is completed at850°C and takes 22 hours. Process two is completed at 900°C. The diffusionconstant for carbon in iron is 2.99 x 10 16 m²/s at 850°C and 1.58 x 10 15 m2/sPeWhaat 900°C. How long does process two take to achieve the same result? Give youranswer in hours to two decimal places.ThebeforType your answer...only Go

Given that At 850 C D = 2.99 x10-16 m2/s t =22 hrT =900 CD = 1.58 x 10-15 m2/s

Answered: Two carburising processes are being…

Introduction to Chemical Engineering Thermodynamics

8th Edition

ISBN:9781259696527

Author:J.M. Smith Termodinamica en ingenieria quimica, Hendrick C Van Ness, Michael Abbott, Mark Swihart

Publisher:J.M. Smith Termodinamica en ingenieria quimica, Hendrick C Van Ness, Michael Abbott, Mark Swihart

Chapter1: Introduction

Section: Chapter Questions

Problem 1.1P

See similar textbooks

Similar questions

A wet solid initially contains x1% free moisture, and it is subjected to a stream of hot air flowing at a rate of Q and inlet conditions of T1 and RH1. We want to dry the solid down to its critical moisture content. Which of the following will result to the fastest rate of drying? increasing Q increasing RH1 increasing contact time none of the choices decreasing T1
Explain in detail about the electrolytic determination of different heavy metals at constant current method. Explain in detail about the electrolytic determination of different heavy metals at constant current methodh.
Which one can be said according to the graph given below? Temperature ("C) i. This figure shows a DSC thermograph. ii. The thermograph belongs to a semi-crystalline polymer. ilI. Point A indicates a thermal transition of amorphous regions in a polymer. iv. The degree of crystallinity of this polymer can be calculated with the data of the curves where the B and C points are located. A Il and M B I, Il and V II, III and M 1, I, Il and V Heat Flow (mW)
Q1 (30 points) a) Name and describe 3 heat transfer mechanisms. (15 points) b) Give one example for each heat transfer mechanisms. (15 points)
The activation energy for Al in a Cu solvent is 1.6 x 108 J/kmol. What is the diffusion coefficient, D, at 575 °C if the constant of proportionality, Do, is 7 x 10-6 m2/s? a. 2.31 x 10-5 m2/s c. 2.04 x 10-20 m2/s b. 9.75 x 10-16 m2/s d. 4.04 x 10-47 m2/s
Gel-time and viscosity changes of a polymer were given below. What is the relation between the temperature values according to the gelling time? got, -Tree A TL-TZT3>T4 B T3>T2>TL>T4 TZTL>T3>T4 T4>T3>T2>T1
One integrated circuit design calls for the diffusion of arsenic into silicon wafers; the background concentration of As in Si is 2.5 × 1020 atoms/m³. The predeposition heat treatment is to be conducted at 1000°C for 45 minutes, with a constant surface concentration of 8 x 1026 As atoms/m³. At a drive-in temperature of 1100°C, determine the diffusion time required for a junction depth of 1.2 μm. For this system, values of Qd and Do are 4.10 eV and 2.29 × 10-³ m²/s, respectively. hours
(b)A device engineer fabricates a sensor by depositing an a-Si:H film on a glass substrate and then depositing an Al electrode onto the a-Si:H film. The device has the structure glass/a-Si:H/metal. The glass substrate is 10 mm thick. The a-Si: is 5 µm thick and the Al electrode is 0.2 µm thick. The expansion coefficients of glass, a-Si:H and Al are about 7x106 K-!, 4×10-6 K-', 23×10-6K-l respectively. Elastic moduli are Eglass = 70 GPa, Ea Si:H = 100 GPa, EAI = 70 GPa. Calculate the stress in each layer if the temperature drops from 25 °C to –50 °C.
Why, the removal of lignin in Pulp washers is important? a. To maintain constant bleaching chemical demand b. To reduce bleaching chemical demand c. To freeze bleaching chemical demand d. To increase bleaching chemical demand
3
What does the evaporation rate of a liquid in g / s and mol / cm2s depend on? Explain.
Give a good detailed explanation also along with the correct answer. Not just the answer.

SEE MORE QUESTIONS

Recommended textbooks for you

Introduction to Chemical Engineering Thermodynami…

Chemical Engineering

ISBN:

9781259696527

Author:

J.M. Smith Termodinamica en ingenieria quimica, Hendrick C Van Ness, Michael Abbott, Mark Swihart

Publisher:

McGraw-Hill Education

Elementary Principles of Chemical Processes, Bind…

Chemical Engineering

ISBN:

9781118431221

Author:

Richard M. Felder, Ronald W. Rousseau, Lisa G. Bullard

Publisher:

WILEY

Elements of Chemical Reaction Engineering (5th Ed…

Chemical Engineering

ISBN:

9780133887518

Author:

H. Scott Fogler

Publisher:

Prentice Hall

Introduction to Chemical Engineering Thermodynami…

Chemical Engineering

ISBN:

9781259696527

Author:

J.M. Smith Termodinamica en ingenieria quimica, Hendrick C Van Ness, Michael Abbott, Mark Swihart

Publisher:

McGraw-Hill Education

Elementary Principles of Chemical Processes, Bind…

Chemical Engineering

ISBN:

9781118431221

Author:

Richard M. Felder, Ronald W. Rousseau, Lisa G. Bullard

Publisher:

WILEY

Elements of Chemical Reaction Engineering (5th Ed…

Chemical Engineering

ISBN:

9780133887518

Author:

H. Scott Fogler

Publisher:

Prentice Hall

Process Dynamics and Control, 4e

Chemical Engineering

ISBN:

9781119285915

Author:

Seborg

Publisher:

WILEY

Industrial Plastics: Theory and Applications

Chemical Engineering

ISBN:

9781285061238

Author:

Lokensgard, Erik

Publisher:

Delmar Cengage Learning

Unit Operations of Chemical Engineering

Chemical Engineering

ISBN:

9780072848236

Author:

Warren McCabe, Julian C. Smith, Peter Harriott

Publisher:

McGraw-Hill Companies, The

SEE MORE TEXTBOOKS