Three different materials, designated A, B, and C, are tested in tension using test specimens having diameters of 0.525 in. and gage lengths of 1.9 in. (see figure). Gage length At failure, the distances between the gage marks are found to be 2.05 in., 2.40 in., and 2.70 in., respectively. Also, at the failure cross sections, the diameters are found to be 0.504 in., 0.408 in., and 0.233 in., respectively. Determine the percent elongation of each specimen. material A material B material C % Determine the percent reduction in area of each specimen. material A material B material C Using your own judgment, classify each material as brittle or ductile.

Three different materials, designated A, B, and C, are tested in tension using test specimens having diameters of 0.525 in. and gage lengths of 1.9 in. (see figure). Gage length At failure, the distances between the gage marks are found to be 2.05 in., 2.40 in., and 2.70 in., respectively. Also, at the failure cross sections, the diameters are found to be 0.504 in., 0.408 in., and 0.233 in., respectively. Determine the percent elongation of each specimen. material A material B material C % Determine the percent reduction in area of each specimen. material A material B material C Using your own judgment, classify each material as brittle or ductile.

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.5P: The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen...

See similar textbooks

Similar questions

4. The following creep data were obtained for a metal alloy tested under a constant load and at a constant temperature (the initial length of the unloaded sample was 2.0 inches): Sample Length (in) Time (hr) 2.004 2.01 100 2.02 200 2.03 400 2.045 1000 2.075 2000 2.135 4000 2.193 6000 2.23 7000 2.30 8000 (fracture) a.) Plot the strain versus time (in hours) curve for this material. b.) Determine the steady-state creep rate.
I. Problem Solving: Answer what is being required. Show you complete solution. 1. Compute the compressive stress for the respective ages of the specimen. The diameter of the specimens is 150mm and the height is 300mm. Load (N) 176,000 Stress (MPa) Age 7days 14 days 28 days 252,000 340,000 2. Compute the tensile stress from the value acquired from the experiment if the breaking load is 105KN. The diameter of the specimen is 150mm and the height is 300mm. 3. Compute the flexural stress of the sample specimen if its dimension is 150mm x 150mm x 500mm in a 3 point loading. The effective length is 400mm. The specimen failed at 44,300N in the middle third. 4. Compression test was applied to a certain type of wood. Compute the stress based on the following dimensions. The grains are parallel with the length. а. Dimension (mm) Load (N) Compressive stress (МРа) Compression Test
with fbd
a) A tension test was carried out for a specimen having 610 mm in length and an average diameter of 12.80 mm. The test was conducted until the specimen failed. The data record from a tensile test for the specimen is given in Table 1. A 50 mm gauge length was marked on the specimen before load applied.Referring to the data in Table 1;i) Plot a stress-strain diagram by using a scale of 1:0.02 mm/mm for the x-axis and 1:40 MPa for the y-axis. Redraw the elastic region by using a strain scale of 1:0.004 min/mm.ii) Determine the approximate modulus of elasticity, ultimate stress, and the yield strength of this material at 0.20% offset.iii) Calculate the modulus of toughness.iv) Calculate the final length of the specimen, if the specimen elongated about 26.78%.v) Calculate the percentage of reduction of area and the final diameter at breakage, if the cross-section area decreases to 105.13 mm2
5.7 During the test of a specimen in a tensile testing ma- chine, it is found that the specimen elongates 0.0024 inch between two punch marks that are initially two inches apart. Evaluate the strain.
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
A tension test is being conducted on a steel-rod specimen with a gauge length of L0=2 in and initial diameter of d0=0.5 in. Data were collected to form the conventional stress-strain diagram as shown. From the diagram, f = 74.0 ksi, e = 104.0 ksi , g = 85.0 ksi , and h = 0.15 in/in. Assuming that the strain remains constant throughout the region between the gauge points, determine the nominal strain ε experienced by the rod if it is elongated to L = 2.7 in . Assuming that the stress is constant over the cross-sectional area and if the tension force used is P = 11.0 kips, find the nominal stress experienced by the rod. Determine the force P needed to reach the ultimate stress in the steel-rod specimen.
need help asap plsss tq....
I. Problem Solving: Answer what is being required. Show you complete solution. 1. Compute the tensile stress from the value acquired from the experiment if the breaking load is 105KN. The diameter of the specimen is 150mm and the height is 300mm. 2. Compute the flexural stress of the sample specimen if its dimension is 150mm x 150mm x 500mm in a 3 point loading. The effective length is 400mm. The specimen failed at 44,300N in the middle third. 3. Compression test was applied to a certain type of wood. Compute the stress based on the following dimensions. The grains are parallel with the length. а. Compression Test Dimension (mm) Load (N) Compressive stress (МРa)
th
Using the stress-strain curve in Figure 3, please answer questions: iv) If the specimen is loaded to stress of 65 Mpa and then unloaded, determine the residual plastic strain v) If the diameter of the unloaded specimen is 1cm and the Poisson's ratio of the material is v=0.3, what is the specimen diameter just prior of yield of the tensile specimen
In a tensile test on a steel tube of external diameter 18 mm and internal diameter 12 mm and an axial pull of 2 kN produced a stretch of 6.72x 10 mm in a length of 100 mm and a lateral contraction of 3.62x10 mm in the outer diameter. Calculate the three modulus and Poisson's ratio for the material of the tube.