The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 141 kN. - Length of the specimen is 24 mm. - The yield strength is 74 kN/mm². - The percentage of elongation is 41 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 15 kN,

The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 141 kN. - Length of the specimen is 24 mm. - The yield strength is 74 kN/mm². - The percentage of elongation is 41 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 15 kN,

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

I need the answer as soon as possible
The following data are obtained from a tensile test of a copper specimen. - The load at the yield point is 148 kN. - Length of the specimen is 26 mm. - The yield strength is 83 kN/mm². - The percentage of elongation is 49 %. Determine the following (i) Diameter of the specimen, ii) Final length of the specimen, iii) Stress under an elastic load of 13 kN, iv) Young's Modulus if the elongation is 2.9 mm at 13 kN and (v) Final diameter if the percentage of reduction in area is 22 %. Young's Modulus of the Specimen (in N/mm?) Final Area of the Specimen at Fracture (in mm) 1. Final Diameter of the Specimen after Fracture (in mm)
Draw a typical stress vs strain tensile test curve for the following materials (two seperate graphs) and label the axis. A ductile metallic test specimen that is stretched to failure displaying a characteristic yield point and show the following parts on the curve. 1- Yield point 2- Ultimate Tensile Strength 3- Breaking point 4- Elastic Region 5- Plastic Region 6- Necking region
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…
1 J A cylindrical specimen of steel having a diameter of 14.36 mm and length of 209 mm is deformed elastically in tension with a force of 58.9 kN. Suppose that the Poisson's ratio (v) is 0.3, determine The change in diameter of the specimen? (E of steel = 207 GPa)
3. An aluminum sample was tensile tested with a force of 35,500 N. The sample has a rectangular cross section with dimension 10 mm x 12.7 mm. It was observed that only elastic deformation occurred. If the modulus of elasticity of Al is 69 GPa, calculate the resulting strain.
During a test, a copper specimen alloy having a diameter of 10.2 mm is applied with a tensile load of 8900 N. Given a maximum allowable elongation of 0.25 mm, determine the maximum length (mm) of the specimen before deformation.
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm. Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area. TENSILE-TEST DATA Load(kN) Elongation(mm) 5 0.005 10 0.015 30 0.048 50 0.084 60 0.099 64.5 0.109 67.0 0.119 68.0 0.137 69.0 0.160 70.0 0.229 72.0 0.259 76.0 0.330 84.0 0.584 92.0 0.853 100.0 1.288 112.0 2.814 113.0 Fracture
A tensile test specimen of 1045 hot-rolled steel having a diameter of 0.505 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the ultimate strength. Stress (ksi) 60 50- 40- 30- 20 10- 0 0 0 Upper scale O 66 ksi 28 ksi O 72 ksi O 53 ksi O 62 ksi Lower scale. 0.025 0.050 0.075 0.100 0.125 0.150 0.175 0.002 0.004 0.006 0.008 0.010 0.012 0.014 Strain (in./in.)
A mild steel tensile specimen of initial length 44 mm and initial diameter 6.4 mm is subjected to a tensile test and the following data are obtained. - Yield Strength as 88 MPa - Maximum Strength as 212 MPa - Fracture Strength as 152 MPa - Percentage of Elongation as 63 % - Percentage of Reduction in area as 39% Determine the Final length, Final area, Yield load, Ultimate load