all5.21 A sieve analysis test was performed on a sample of aggregate and producedthe results shown in Table P5.21.TABLE P5.21Sieve Size, mm251912.59.54.752.36AmountRetained, g0376.7888.4506.21038.4900.1live prised1973Sieve Size,TBAmm1.180.600.300.150.075Panlusta)groadsto storicAmountRetained, g891.5712.6625.2581.5242.944.9Calculate the percent passing through each sieve. Plot the percent passingversus sieve size on:a. a semilog gradation chart, andb. a 0.45 gradation chart (Figure A.25).What is the maximum size? What is the nominal maximum size?

Sieve Analysis : To assess the grain size distribution of soils with a diameter higher than 0.075…

TABLE P5.21 Sieve Size, mm 25 19 12.5 9.5 4.75 2.36 Amount Retained, g 0 376.7 888.4 506.2 1038.4 900.1 Sieve Size, mm 1.18 0.60 0.30 0.15 0.075 Pan toflquoad Amount Retained, g 891.5 712.6 625.2 581.5 242.9 44.9 Calculate the percent passing through each sieve. Plot the percent passing versus sieve size on: a. a semilog gradation chart, and b. a 0.45 gradation chart (Figure A.25). What is the maximum size? What is the nominal maximum size?

TABLE P5.21 Sieve Size, mm 25 19 12.5 9.5 4.75 2.36 Amount Retained, g 0 376.7 888.4 506.2 1038.4 900.1 Sieve Size, mm 1.18 0.60 0.30 0.15 0.075 Pan toflquoad Amount Retained, g 891.5 712.6 625.2 581.5 242.9 44.9 Calculate the percent passing through each sieve. Plot the percent passing versus sieve size on: a. a semilog gradation chart, and b. a 0.45 gradation chart (Figure A.25). What is the maximum size? What is the nominal maximum size?

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

sieve analysis solve the ampty box and draw the chart and find d10.d30.d60
A sieve analysis test was performed on a sample of aggregate and produced the results shown in Table P5.21. TABLE P5.21 Amount Sieve Size, Amount Sieve Size, mm Retained, g mm Retained, g 25 1.18 891.5 19 376.7 0.60 712.6 12.5 888.4 0.30 625.2 9.5 506.2 0.15 581.5 4.75 1038.4 0.075 242.9 2.36 900.1 Pan 44.9 Calculate the percent passing through each sieve. Plot the percent passing versus sieve size on: a. a semilog gradation chart, and b. a 0.45 gradation chart (Figure A.25). What is the maximum size? What is the nominal maximum size?
A sample of a dry coarse grained material of 500 grams was shaken through a nest of sieves and the following results are obtained: 20 | 200 40 0.425 Sieve No. 10 2.00 4 60 100 Pan Opening (mm) % Passing 4.75 0.85 0.25 0.15 0.075 -- 94 60 30 10 7 5 3 31. Determine the uniformity coefficient. b. 4.424 32. Determine the coefficient of curvature. a. 4.706 C. 1.250 d. 0.85 а. 4.706 b. 4.424 C. 1.250 d. 0.85 33. Given that the soil is non-plastic, classify the soil by using the Unified Soil Classification System. a. GW b. GP C. Sw d. SP
Please solve points 4 and 5 only
Q1- The followving data was obtained tensile test on a specimen of 6 mm diameter and gauge length Lo=30 mm: 92.7 160.4 155 4.06 142 124.7 5.1 5.84 0| 38 load(KN) elongation(mm) 0 0.02 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the 76.2 107 149 0.12 0.25 0.50 2.03 3.55 (gy sy), (gu, cu), (of, sf), modulus of elasticity, then detected in the draw ((strain hardening (n)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?
Tension specimens (diameter d0 0.500 in., gage length L0 2.00 in.) made of structural materials A and B are tested to failure in tension. (a) At failure the distances between the gage marks are LAf 2.90 in. and LBf 2.22 in.; the corresponding diameters at the failure cross sections are dAf 0.263 in. and dBf 0.471 in., respectively. Determine the percent elongation in 2 in. and the percent reduction in area for these two materials, and classify each material as either brittle or ductile. (b) From these tensile tests the following data are also obtained: EA 10.0 103 ksi, (Y)A 5 ksi, (U)A 13 ksi; EB 10.4 103 ksi, (Y)B 73 ksi, (U)B 83 ksi. From the data given here, make rough sketches (to scale) of the stress-strain diagrams of materials A and B.
5.22 A sieve analysis test was performed on a sample of coarse aggregate and pro- duced the results in Table P5.22. a. Calculate the percent passing through each sieve. b. What is the maximum size? c. What is the nominal maximum size? d. Plot the percent passing versus sieve size on a semilog gradation chart. TABLE P5.22 e. Plot the percent passing versus sieve size on a 0.45 gradation chart (Figure A.25). f. Referring to Table 5.5 (ASTM C33), what is the closest size number and does it meet the gradation for that standard size? Sieve Size 3 in. 2 in. Questions and Problems 1-1/2 in. 1 in. 3/4 in. 1/2 in. 3/8 in. No. 4 Pan Amount Retained, lb 219 0 0 3.7 15.9 12.0 13.5 26.7 10.1 1.3
Civil Engineering help Table 1 Test No. Rate of deformation Avg. sample length (mm) Avg. sample diameter (mm) Ring factor Cell pressure (kPa) (mm/min). (AIP/N) 100 74.7 38.1 1.27 0.9845 400 75.3 37.7 Table 2 Deformation (mm) Force gauge (divisions) Test 1 Test 2 0.5 22 24 1.0 46 44 1.5 2.0 62 68 80 82 2.5 102 106 132 3.0 121 134 3.5 149 4.0 157 173 5.0 6.0 7.0 182 200 219 231 241 194 195 8.0 197 90 198 200 199 | 196 246 10.0 252 251 244 11.0 12.0 By producing Mohr circles and deviatoric stress vs axial strain plots of the tests using the data presented, determine the average Young's modulus, E (MPa) from the most linear portion of the tests deviatoric stress vs axial strain nints Enterani l ...
Answer part D, E, and F
Give me right solution according to the question. Note: If any data missing please assume that data
Compressive Strength is conducted for each aggregate with 3 specimens for each no. of days of curing. The recorded maximum load when the specimen breaks are as follows 7 Days (kN) | 486.73 14 Days (kN) 28 Days (kN) 678.8 ... 746.3 3/8" Sample 513.14 694.2 754.7 360.71 679.8 759.8 7 Days (kN) 14 Days (kN) 28 Days (kN) 231.86 339.8 377.7 3/4" Sample 252.04 339.6 381.1 206.69 343.3 379.9 Compute the compressive strength, in psi, for each size of aggregate on each no. of days of curing. Please indicate if the sample passed the required strength for each no.of days of curing. Conversion: 1lb-f = 4.488 N Attach your solution on the box below, image type.
Complete the table below.