Steady-state creep rate data are gven here for some aloy taken at 200°C (473 K): , (h) a (MPa) 2.5x 10 55 2.3x 102 71 If it is known that the activation energy for creep is 160000 /mol, compute the steady state creep rate at a temperature of 220°C (493 K) and a stress level of 48 MPa. the tolerance is +/-9

Steady-state creep rate data are gven here for some aloy taken at 200°C (473 K): , (h) a (MPa) 2.5x 10 55 2.3x 102 71 If it is known that the activation energy for creep is 160000 /mol, compute the steady state creep rate at a temperature of 220°C (493 K) and a stress level of 48 MPa. the tolerance is +/-9

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: A long plastic rod of 20-mm diameter (k = 0.3 W/m-K and pc, = 1040 kJ/m3.K) is uniformly heated in…

A: Given: The diameter of rod, d = 20 mm = 0.02 m The thermal conductivity, k = 0.3 W/m.K The…

Q: Iculate the activation energy (in J/mol) for creep for an alloy having the steady state creep havior…

Q: You have been given the S-N plot below for a test material: What is the Fatigue Limit for this test…

A: S-N curve represents fatigue life against a fatigue load.

Q: Repeat Prob. 8-1 for cesium iodide. which has a transmissivity of approximately 0.92 between O.3 and…

A: Given, a. τ=0.9λ1=0.2μmλ2=4μmT=800°C=1073Kλ1T=0.2×1073λ1T=214.6μm.Kλ2T=4×1073λ2T=4292μm.KFraction of…

Q: Convider the following data for a range of materials. In which of the following sifuation is range…

A: Creep failure can be defined as the permanent deformation of a material when subjected to a constant…

Q: Problem 4: Fracture An alloy steel is being considered for an application in shipbuilding. Suppose a…

A: The dimension of plate is The crack length is At low temperature At high temperature

Q: A solid 0.125 in. diameter steel [E 30,000 ksi; \alpha = 6.5 \times 10-6/\deg F] wire is stretched…

Q: A thin bar of length L = 3 meters is situated along the x axis so that one end is at x = 0 and the…

A: Given: Length, L=3m Thermal diffusivity, k=0.4 Initial temperature, f(x)=100-10x Boundary…

Q: A truss-type structure is constructed of four equal bars of 1.23 meters long (AC, CD, AB and BD) and…

A: Let the magnitude of force be F

Q: Calculate the activation energy in j/mol for the creep of an alloy having the steady state creep…

Q: Give me right solution with clear calculations Question-3: - Initial error of the impact tester is…

Q: A square piece is initially at 10 degrees Celsius everywhere. Each side is 0.05 m long. Then the…

A: To solve this problem, we can use the heat equation to model the temperature distribution in the…

Q: A ceramic with KIc = 4 MPa m1/2 contains pores with radius a = 5 µm due to incomplete sintering.…

Q: The graph below shows the yield stress for a polycrystalline metal as a function of the grain size…

Q: 3. A structural component is made from a steel alloy with a plain strain fracture toughness of 77.0…

A: Given:Plain strain fracture toughness, Yield strength, Design stress, Geometric factor, The flaw…

Q: Creep Curve - Constant Stress * Secondary creep Tertiory creep ーロー Frocture Primory creep -I- =…

Q: c. Find the homologous temperature (or the percent homologous) of Material A with a melting point of…

A: Given

Q: A uniformly dense rod with a length of 6.9 m and a mass of 6 kg is free to rotate around a…

Q: A cylindrical acetal polymer bar 64 cm long and 1.27 cm in diameter is subjected to a vibrational…

A: Given Data :- diameter of the bar=1.27 cm=12.7mm load acting on the bar=4849 N frequency of the…

Q: When s-0, the springs were unstretched. What is the weight of the block? What are the stretches in…

Q: What are some common ways of dealing with nonlinearities in material behavior or kinematic…

Q: Sintered silicon nitride parts are expected to experience tensile stresses 50% of the ultimate…

A: Given data:- tensile stresses (σ) =50% of the ultimate tensile strength Specific surface energy (γ)=…

Q: 2- the rubber blocks shown in Figure 2 are used in a double U shear mount component. The dimensions…

A: Given:The dimensions of the rubber block are The value of the applied load, The deflection in the…

Q: ank the materials from highest to lowest of which has the best thermal shock resistance without…

A: Thermal shock resistance refers to a material's capacity to withstand quick and abrupt…

Q: 25 30 35 40 45 50 |12. 10° (R-h) х103 х103 х103 х103 х103 х103 Larson-Miller 100,000 |2.2- 10° (K-Һ)

A: stress=80MPa(11600psi)Temperaure=700°C(973k) To-Find:- Time to rupture =.................hours

Q: The following creep curve is derived from an aluminum alloy tested at 380℃ with a constant stress of…

A: Creep:

Concept explainers

Thermal Properties of Materials

In mechanical engineering, the thermal property is represented as the physical quantity that is relevant to the application of heat. The thermal properties are evaluated by variations in any specific material due to low heat or high heat. The quantities that influence the thermal property of the materials are mass, density, temperature, and many others.

Question

100%

X Incorrect.
Steady-state creep rate data are given here for some alloy taken at 200°C (473 K):
(h) a (MPa)
2.5x 10
2.3 x 102
71
If it is known that the activation energy for creep is 160000 /mol, compute the steady state creep rate at a temperature of 220°C (493 K) and a
stress level of 48 MPa.
the tolerance is +/-9%
the tolerance is +/-9%

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step 3

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 3 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Properties of Engineering Materials

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

The problem was solved tp verify the performance by doing the calculations in the image. Redo the same problem, but by changing the design either to a Cylinder or Cube from Spherical.
A cylindrical sample of a biological product (10. mm in diameter and 18 mm in height) was exposed to a constant strain test. Assume that the stress in the sample can be described using Standard linear model. The axial load applied to the sample at time zero was 80. N and then after the infinitely long time the force equilibrated 20. N. The viscosity coefficient of the viscous element in the Maxwell arm is 7.50 x103 kPas, and the modulus of elasticity of the elastic element in the Maxwell arm is 15 kPa. Determine after what time the compression force will decrease to 36% of its original value and the modulus of elasticity of the elastic element in the equilibrium arm.
Cu single crystal is anisotropic in nature. If it has the Compliance matrix elements such as shown below, what is the various E’s, G’s and Poisson’s ratios of this anisotropic single crystal Cu?
A structural component in the form of a wide plate is to be fabricated from a steel alloy that has a plane strain fracture toughness of 88 MPam (ksi √/in.)) and a yield strength of 880 MPa (63820 psi). The flaw size resolution limit of the flaw detection apparatus is 3 mm (0.1181 in.). (a) If the design stress is one-half of the yield strength and the value of Y is 1.11, what is the critical flaw length? i mm (b) On the basis of this value, is a critical flaw subject to detection?
Can you represent strain as a function of time using the Maxwell Viscoelastic Model.
1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resilience
The creep data have been taken on an ahuminum alloy at 400°C and constant stress of 25MPA are shown in below Table, Find the steady state or minimum creep rate. Time (min) strain Time (min) 16 strain 0.135 0.0 0.0 2 0.025 18 0.153 4 0.043 0.065 20 0.172 0.193 0.218 22 0.078 24 10 0.092 26 0.255 12 0.109 28 0.307 14 0.120 30 0.368
8-6 Examples The following creep data were taken on an aluminum alloy at 480 °C and a constant stress of 2.75 MPa. Plot the data as strain versus time, then determine the steady-state or minimum creep rate. Note: The initial and instantaneous strain is not included. Time (min): 0 Strain: 4 10 12 14 18 0.82 20 22 0.95 16 24 26 28 30 32 0 0.22 34 1.77 0.34 0.41 0.48 0,55 0.62 0.68 0,75 0.88 1.03 1.12 1.22 1.36 1.53
4) In the temperature range from 600°C to 750°C, a steel wire with 100 mm length shows the steady state creep behavior. The wire was exposed to 600°C under 300 MPa for ten years, how long the specimen would be? ( TH Trung Trong Stress (MPa) 1000 FTTinh Tru Trung Trung Trong th 800 600 400 200 100 80 60 40 815 C 20 d 10-6 104 10-5 650 C 730 C 925°C d d d d d 10-3 10-2 10-1 1 10 10² Steady-state creep rate (h-¹) 10³
A Tensile Tests of structural steel indicate that it fails whe the axial tensile strain is 1.80x10 μ. 3 Let maximum change in length that 0.25 [in] diamoren in tension car with stand before failure Length Find Structural Steel rad it It is 24 [in] in ni sa 9102
In a laboratory creep experiment at 1273K, a steady-state creep rate of 5 ××10-1 %, per hour is obtained in a metal alloy. The creep mechanism for this alloy is known to be dislocation climb with an activation energy of 200 kJ>mol. Predict the service temperature in (°C) for a creep rate of 8.68 ×10-5 %, per hour. (Assume that the laboratory experiment duplicated the service stress.)
Calculate the activation energy in J/mol for creep for an alloy having the steady state creep behavior shown in the figure. Use the data taken at stress level of 300MPa and temperature of 650C and 730C. Assume that the stress component n is independent of the temperature.