QuestionThe yield strength for an aluminum alloy that has an average grain diameter of 10 umis 400 MPa. As the grain diameter is increased to 80 um, the yield strengthdecreases to 260 MPa. When the grain diameter is 2 um, its yield strength is close to760 MPa668 MPa566 MPa419 MPa

OPTION B -668MPa is the right answer. Detailed explanation and solution of the above problem…

Question The yield strength for an aluminum alloy that has an average grain diameter of 10 um is 400 MPa. As the grain diameter is increased to 80 μm, the yield strength decreases to 260 MPa. When the grain diameter is 2 um, its yield strength is close to 760 MPa O668 MPa 566 MPa 419 MPa

Question The yield strength for an aluminum alloy that has an average grain diameter of 10 um is 400 MPa. As the grain diameter is increased to 80 μm, the yield strength decreases to 260 MPa. When the grain diameter is 2 um, its yield strength is close to 760 MPa O668 MPa 566 MPa 419 MPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The yield strength for an alloy that has an average grain diameter of 5.3 x 10 146 MPa. At a grain diameter of 7.8 × 10-3 mm, the yield strength increases to 249 MPa. At what grain diameter, in mm, will the yield strength be 236 MPa? d = Ex 0.0022 mm Check Try again 1
Parvinbhai
Using the values found in the previous two questions, use the Hall-Petch equation and the graph below for a 70 Cu-30 Zn cartridge brass to predict the yield strength (in MPa) of this alloy when the average grain diameter is 1.0 x 10³ mm. Enter only the numerical value, do not include the unit. Grain size, d (mm) 10- 10-2 5 x 103 200 150 100 50 4 8. 12 16 d1/2 (mm-1/2) Yield strength (MPa)
The yield strength for an alloy that has an average grain diameter of 4.6 x 10-2 mm is 105 MPa. At a grain diameter of 7.7 × 103 mm, the yield strength increases to 248 MPa. At what grain diameter, in mm, will the yield strength be 234 MPa? d = i mm
O The following engineering stress-strain data were obtained for a 0.2% C plain-carbon steel. (i) Plot the engineering stress-strain curve. (ii) Determine the ultimate tensile strength of the alloy. (iii) Determine the percent elongation at fracture. Engineering Engineering Engineering Engineering Stress Strain Stress Strain (ksi) (in./in.) (ksi) (in./in.) 76 0.08 30 0.001 75 0.10 55 0.002 73 0.12 60 0.005 69 0.14 68 0.010 65 0.16 72 0.020 56 0.18 74 0.040 51 0.19 75 0.060 (Fracture)
The yield strength for an alloy that has an average grain diameter of 4.1 × 10-2 mm is 131 MPa. At a grain diameter of 7.6 × 10-3 mm, the yield strength increases to 246 MPa. At what grain diameter, in mm, will the yield strength be 236 MPa?
Mechanical
An uncold-worked brass specimen of average grain size 0.006 mm has a yield strength of 178 MPa. Estimate the yield strength of this alloy (in MPa) after it has been heated to 600°C for 1000 s, if it is known that the value of ky is 11 MPa-mm1/2. The Animated Figure 7.25 may be helpful. Attached is the question and the figure referenced.
1. What is the approximate ductility (%EL) of a cold worked brass that has a yield strength of 345 MPa (50,000 psi) 140 120 1040 Steel 1040 Steel 120 700 600 100 500 Brass Brass eo S400 Brass 300 Copper 40 200 Copper 040 e 00 40 Copper 100 O 10 20 30 40 50 60 70 Percent cold work 200 0 10 20 30 40 50 60 70 Percent cold work O 10 20 30 40 D0 60 70 Percent cold work (a) (b)
3. An uncold-worked brass specimen of average grain size 0.01 mm has a yield strength of 150 MPa (21,750 psi). Estimate the yield strength of this alloy after it has been heated to 500°C for 1000 s, if it is known that the value of σo is 25 MPa. (Note that the axis has logarithmic scale). Grain diameter (mm) (Logarithmic scale) 1.0 0.1 0.01 1 10 850°C 800°C 700°C 102 Time (min) (Logarithmic scale) 600°C 500°C 103 104
Mechanical Engineering Consider two polycrystalline samples with grain size of 0.25 and 5 um. Cooling of the materials produces cracks due to the thermal expansion mismatch. The approximate dimensions are similar to the grain-boundary facets. Determine the tensile strength of the two materials if both have Kiç as 3.5 MN m0.3. Which sample would you use for your project that requires high strength? (geometric factor is unknown)
The average grain diameter and yield strength for a brass material were measured as a function of time at 650°C. Given the following yield strengths for the two specimens, compute the heat treatment time required at 650°C to give a yield strength of 100 MPa. Assume a value of 2 for n, the grain diameter exponent. Time (min) 30 90 Yield Strength (MPa) 90 75 min Grain Diameter (mm) 3.9 x 10-2 6.6 x 10-2