A low-carbon steel has a yield strength of 622 MPa when the average grain diameter is 180 um. When the grain diameter is reduced to 22 um, the yield strength increases to 663 MPa. (a.) Calculate the yield strength when the grain diameter is reduced to 10 μm. Keep track of units, and show all work. (b.) Did we reach the "magical value" of 100 ksi?

A low-carbon steel has a yield strength of 622 MPa when the average grain diameter is 180 um. When the grain diameter is reduced to 22 um, the yield strength increases to 663 MPa. (a.) Calculate the yield strength when the grain diameter is reduced to 10 μm. Keep track of units, and show all work. (b.) Did we reach the "magical value" of 100 ksi?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The minimum yield strength for iron with an average grain size of 6x10-²mm is 135 MPa, this increases to 260 MPa when the average grain size is reduced to 8x10-³ mm. What must the average grain size be to achieve a yield strength of 205 MPa.
In order to find out the effects of the grain sizes on the mechanical strength of a metal, three different grain sizes of 10 µm, 500 nm and 10 nm were produced. What will be the yield stresses of these same metals at different average grain sizes? The yield strength for a grain or reference point is 78 MPa, while the material proportional constant is 29.2 MPa-mm1/2.
Pravinbhai
A 3105 aluminum plate is reduced from 4.38 cm to 2.88 cm. Determine the final properties of the plate. See attached figure
The yield strength for an alloy that has an average grain diameter of 5.9 x 10-2 mm is 148 MPa. At a grain diameter of 7.8 × 10-³ mm, the yield strength increases to 233 MPa. At what grain diameter, in mm, will the yield strength be 247 MPa? d = i mm
an alloy with an avg grain diameter of 0.053 mm is l16 MPa. When the grain diameter is 0.008Amm, the yeild strength goesupto 231 MPa.lf the yeild strength is 207MPA, what would the grain diameter be?
The yield strength for an alloy that has an average grain diameter of 5.2 x 102 mm is 110 MPa. At a grain diameter of 6.3 x 103 mm, the yield strength increases to 251 MPa. At what grain diameter, in mm, will the yield strength be 222 MPa? d = mm
3. An uncold-worked brass specimen of average grain size 0.01 mm has a yield strength of 150 MPa (21,750 psi). Estimate the yield strength of this alloy after it has been heated to 500°C for 1000 s, if it is known that the value of σo is 25 MPa. (Note that the axis has logarithmic scale). Grain diameter (mm) (Logarithmic scale) 1.0 0.1 0.01 1 10 850°C 800°C 700°C 102 Time (min) (Logarithmic scale) 600°C 500°C 103 104
The yield strength for an alloy that has an average grain diameter of 4.6 x 10-2 mm is 105 MPa. At a grain diameter of 7.7 × 103 mm, the yield strength increases to 248 MPa. At what grain diameter, in mm, will the yield strength be 234 MPa? d = i mm
Consider a single crystal of some hypothetical metal that has the BCC crystal structure and is oriented such that a tensile stress is applied along a [2 2 1] direction. If slip occurs on a (2 1 1) plane and in a [-1 1 1] direction, compute the stress at which the crystal yields if its critical resolved shear stress is 2.4 MPa.
(3) Metals tend to expand when heated and contract when cooled. If a clock has a pendulum made of a bob attached to the end of a metal rod (as opposed to the string we used in our lab), completely describe the effect that temperature would have on the accuracy of the clock (i.e., would the clock run too fast or too slow) and why? k
6.31 The flow stress for an alloy is 100 MPa when its dislocation density is 106 cm-2, and 150 MPa when its dislocation density is 108 cm-². When the flow stress is 190 MPa, what is the dislocation density?