A copper-zine alloy has the properties shown in the table below. Grain Diameter (mm) Strength (MPa) 0.015 170 MPa 0.025 158 MPa 0.035 151 MPa 0.050 145 MPa Determine (a) the constants in the Hall-Petch equa- tion; and (b) the grain size required to obtain a strength of 200 MPa.

A copper-zine alloy has the properties shown in the table below. Grain Diameter (mm) Strength (MPa) 0.015 170 MPa 0.025 158 MPa 0.035 151 MPa 0.050 145 MPa Determine (a) the constants in the Hall-Petch equa- tion; and (b) the grain size required to obtain a strength of 200 MPa.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Match the image with the material property depicted by the image. - 1.…

A: Ductile failure or fracture: When the tensile stress increase in a ductile material than it behaves…

Q: e yield strength for an alloy that has an average grain diameter of 4.1 × 10-2 mm is 131 MPa. At a…

A: Given:σ1=131 MPaD1=4.1*10-2 mmD2=7.6*10-3 mmσ2=246 MPaσ=236 MPa

Q: trength of metals and their alloys increases as grain size decreases. Find out the amount of…

A: From hall patch equation:σy=σ∞+kDHere,σy is the yield strength of grainD=Grain diameterσ∞=Yield…

Q: The effect of temperature on the crystallization of a material is given below. Calculate the…

A: Given is Effect of temperature on the crystallization of the material To determine…

Q: The yield stresses (oy) have been measured using steel and aluminum specimens of various grain…

A: The given table is The Hall-Petch equation is σy=σo+KD-12 here, σy = Yield strength of the material…

Q: t as a separate question that has no relationship to previous parts of the question. 1 and 2 are…

Q: Materials with dislocations have lower shear strengths than materials with no dislocations. Is this…

A: Dislocation: It is a linear crystallography defect inside the crystal structure of the material…

Q: SHORT ANSWER Use the stress-strain figure below to answer the following questions: 1) In the…

A: The given graph in the question is the stress-strain diagram- There are various points in a…

Q: Find the average grain size for the microstructure. Assuming that the length of each line is equal…

Q: Temperature (°C) 1600 (1) 1400 1200 1000 800 600 400 1538°C (Fe) 912°C 8+7 1394°C(F) -1493°C (G) y,…

A: Given:

Q: Question The yield strength for an aluminum alloy that has an average grain diameter of 10 um is 400…

A: OPTION B -668MPa is the right answer. Detailed explanation and solution of the above problem…

Q: If a rod of single-crystal copper (FCC) is pulled in tension in the [210] direction (i.e. force…

Q: A cold worked brass specimen of average grain size 0.02 mm has a yield strengh of 160 MPa. Estimate…

A: From Hall-Petch equation - σy =σi + kyd-12Let us calculate the value of constant σi (Putting the…

Q: 1. The stress and strain of a sample under mechanical testing can be classified into two types and…

Q: V Use the engincering stress strain diagram provided below to answer parts (A) to (1) below (the…

Q: (6) For an aluminum alloy under constant load, the creep rate increased by a factor of 2 when the…

Q: (1) Compute the dislocation density in tungsten if the flow stress is controlled by the stress…

A: Since all the questions are different, according to our guidelines, we are supposed to answer 1st…

Q: Determine values for the constants n and k for the recrystallization of copper (Figure 10.11) at…

Q: 7- Calculate the tensile strength of steel: ou = 700 * c% + 340 N mm ( for hypo eutectoid steel)

Q: 1. Two iron samples with different grain sizes are tensile tested. The grain size of sample A is…

A: The size of grain A and B is 1.1 and 0.37 μm respectively.

Q: b) Estimate the yield stress of copper containing an array of equally spaced second phase…

A: Yield strength alludes to the pressure at which the event of a foreordained measure of super durable…

Q: le) Name four methods used for strengthening of metals. What is the common principle that these…

Q: For the alloy Mg-45 wt % Pb alloy at 500°C, what is the weight percentage of Pb in Liquid? It does…

A: Given: The wt percentage of Pb, Co = 45 The temperature of alloy, T = 500 C

Q: The yield strength for an alloy that has an average grain diameter of 5.3 x 10-2 mm is 146 MPa. At a…

Q: 2. Immediately after recrystallization during annealing, this alloy was quickly cooled. Assume that…

A: Based on the information provided, the likely mechanism for the increase in yield strength (σy)…

Q: Calculate the dislocation density in tungsten if the stress is controlled by the stress necessary to…

A: Given:To determine:The dislocation density in tugsten

Q: Please show how the value of b was calculated Calculate the dislocation density in tungsten if the…

A: The already calculated solution for the given problem is as below.The expression for the dislocation…

Q: respectively. Q.3 ( Suppose we count 18 grains per square inch in a photomicrograph taken at…

Q: From the grain distribution curve, D60 = 1.45 mm, D30 = 0.75 mm and D10 = 0.45 mm. Determine the…

A: Write the formula for uniformity coefficient. Cu=D60D10 Here, Cu is the uniformity coefficient, D60…

Q: lease solve as fast as. Don

A: Given-Information:- Hypereutectoid steel = 2.5 kgHeated upto temperature = 725°CFerrite = 1000 g…

Q: Calculate the tensile modulus (G) of a 1-cm poly(methyl methacrylate) (CAS# 9011-14-7) rod with a…

Q: Strain hardening aluminium increases the strength by reducing the number of dislocations True False

Q: You need to produce a Ci-Ni alloy having minimum yield strength of 20,000psi, a minimum tensile…

A: Required properties for Cu-Ni alloy:Minimum yield strength (σy) = 20,000 psiMinimum tensile strength…

Q: | 1. A stacking fault region is a planar defect TT 2. Screw dislocation can cross slip under…

Q: Figure below shows the grain boundaries of low-carbon steel under a microscope with 200X…

Q: Q3: Analyze the following figure and answer the following question (Fe-C Diagram) ? 1639 Liquid 1400…

Q: derive the generalized hook's law for an isotropic homogeneous elastic solid in terms of lame's…

A: given; derive the generalized hook's law for an isotropic homogeneous elastic solid in terms of…

Q: The influence of grain size on the yield strength of metallic material is shown in the figure, what…

Q: Briefly explain the ASTM grain-size standard

A: ASTM grain size standard : The grain size measurement play an important role in improving the…

Q: According to Hall-Petch equation, the 1 point decreasing in grain size causes strengthening of…

A: Hall-Petch equation or Grain-boundary Strengthening predicts that when the grain size decreases…

Q: 4-58 Determine the ASTM grain size number if 38750 grains/m2 magnification of 50. are observed at a

A: Relation between the grain size and number of grains can be given as –

Q: Given an iron-carbon alloy that is heated at 770°C and has been held at this temperature long enough…

A: As per Bartelby guidelines for answering multiparts, i am answering only three subparts. Given:…

Q: Excellent combinations of hardness, strength, and toughness are obtained from bainite. One heat…

A: The eutectoid composition of austenite is approximately 0.8% carbon; steel with less carbon content…

Q: onsider the tensile stress-strain diagram in the figure below labeled 1 and 2. These diagrams are…

Q: To put lattice defects in perspective, consider a metal blank that has a dislocation density of 10^3…

A: Given DataDislocation Density=103mm-2Dislocation Volume=103mm3Increased Dislocation Density=1010mm-2…

Q: Tensile stress-strain diag 450 400 350 300 250 200 150 100

A: given:

Q: Column A Column B Increasing thickness of alumina Hardness Column A Column B Increase in atomic…

A: 1) increase in thickness of the lamina DECREASE the hardness. 2)Increase in atomic packing factor…

Q: 4.50 Following is a schematic micrograph that rep- resents the microstructure of some hypothetical…

A: Step:I Given data:- scole bar no in figure=200μmTo find:-1.Mean intercept length2. ASTM…

Question

A copper-zine alloy has the properties
shown in the table below.
Grain Diameter (mm) Strength (MPa)
0.015
170 MPa
0.025
158 MPa
0.035
151 MPa
0.050
145 MPa
Determine
(a) the constants in the Hall-Petch equa-
tion; and
(b) the grain size required to obtain a
strength of 200 MPa.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

4. The average grain diameter for a brass material was measured as a function of time at T, which is tabulated below at two different times: Time (min) Grain Diameter (mm) 30 90 3.9 × 10-2 6.6 × 10-2 (a) What was the original grain diameter (using n=2)? (b) What grain diameter would you predict after time, t, at temperature, T? Use T = 650 °C; t = 150 min; n = 2 in the grain size equation
The flow stress of a coarse-grained dilute copper alloy increased from 2 to 55 MPa when the dislocation density was increased from a low value of 10 cm via cold working to a modest value of 100 cm2. Calculate the flow stress for this alloy when heavy cold working introduces a dislocation density of 10¹2 cm². An equation similar to the Hall-Petch equation has been proposed for dislocations, and is: Tflow To ka Paisl where Tflow is the flow stress (i.e., the force per unit area necessary to get plastic deformation), pdisi is the dislocation density (the dislocation line length per unit volume), and To and ka are constants for a given material. The easiest way to solve this problem is to put values into this equation twice, subtract one expression from the other, and solve for ka. Then enter your value of ka into either original equation to determine To. Keep track of units, and then solve the problem stated above.
Consider an iron single crystal with CCC crystal structure oriented in such a way that a tensile stress is applied to the along one direction [010]. a) Calculate the shear stress resolved along a plane (110) and a direction [11] when a tensile stress of 52 MPa is applied. The normal to the slip plane foms 45° with traction direction. the direction of slip forms 55° with the traction direction. b) If the slip occurs in one plane (110) and in one direction [ī11] and the critical resolved shear stress is 30 MPa, calculate the magnitude of tensile stress that must be applied to initiate the flow.
Please answer the whole solution. i provided the equation
When a cold-worked metal is heat-treated below its melting point over a period of time, which of the following phenomena occur? (This question has more than one correct answer) a. Strength is increased b. Dislocation density decreases c. Grain size increases d. Internal lattice strains decrease e. Ductility is reduced
You are given three metal test samples, with the same chemical composition and differing grain sizes: A: 5.0, B: 10.0 and C: 20.0 microns. Samples A and B have been tested and have yield stresses of 142.4 MPa and 135.8 MPa (all numbers are rounded off to the 1st decimal point). Based on this information, which of the following values do you think will be the closest to the yield stress of Sample C? In calculating the answer, use the Hall-Petch relation between yield stress of a metal o vield and the grain size of the metal d, which is Oyield = 00 + kd¬1/2 where k and og are constants. (This question has only one correct answer) а. 100.6 MPa b. 131.1 MPa С. 152.4 MPa O d. 115.8 MPa е. 128.1 MPa
N MPa = 10 2.2. When the Hall-Petch coefficient is 20 GPa nm/2, estimate the grain size of this alloy after recrystallization. -1/2 d O=O₂+ Kuda куба го вра има че app MPa = 150 MPa + 20 × 10 °MPant -150MPa 1
Consider a dislocation condition as shown below. A) what is the strain state in the upper region and B) how would addition of small impurity atoms in the region indicated by "*"s change it? OOOOOO ooooooo OO OO O O O O O O O O O O O O Select one: a. Tensile, would increase tensile strain b. Shear, would increase compressive strain c. Tensile, would decrease tensile strain O d. Compressive, would reduce compressive strain e. Compressive, would increase compressive strain
Hall-Petch Constants Material Y; (MPa) k (MPa.ma) Copper 25 0.12 Titanium 80 0.40 Mild Steel 70 0.74 Using Hall-Petch equation, determine the Yield Stress (MPa) for a Mild Steel piece of metal having a grain size of 100 um. O 115 MPa O 101 MPa O 144 MPa O 130 MPa
Please type answer no write by hend.
S/N Grain Diameter (mm) Strength (MPa) 1. 0.015 170 2. 0.025 158 3. 0.035 151 4 0.050 145 Determine The constants in the Hall-Petch equation; and The grain diameter to obtain strength of 200 Mpa.
2. Sketch: a. 3 stages of single crystal stress-strain curve under uniaxial stress b. Frank-Reed mechanism for dislocation multiplication.