Q1 Figure below shows the stress strain curves of 6 samples.1280A701060В8.5040D3020E10F0.10.2Strain(a) From Figure above, select 1 sample that would experience brittle fracture. Evaluate and explain in detail (atleast 6 points) on the failure mode experienced by this sample based on the characteristic shown in the figure.(b) By referring to the sample E, determine the following:(i) The modulus of elasticity and fracture strain(ii) The tensile strength, yield strength, rupture strengthStress (MPa)Stress (10 psi)

Answered: Image /qna-images/answer/798a82b8-9ce8-456e-afcf-b4a2461b76e9.jpg

QI Figure below shows the stress strain curves of 6 samples. 12 80 A 70 10 60 D 20 10 F 0.1 0.2 Strain a) From Figure above, select 1 sample that would experience brittle fracture. Evaluate and explain in det (sd o) sas B. Stress (MPa

QI Figure below shows the stress strain curves of 6 samples. 12 80 A 70 10 60 D 20 10 F 0.1 0.2 Strain a) From Figure above, select 1 sample that would experience brittle fracture. Evaluate and explain in det (sd o) sas B. Stress (MPa

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

I just can't find The percent elongation at fracture.
For a steel element with a 0.2% steel characteristic, a stress test was applied and the analysis of the data thrown by the material is required in terms of a variation of force and the respective deformations. Determine the following: A.Determine the percentage elongation at the point where the part develops the fracture. B.Construct the “Stress-Strain” diagram C.Maximum tensile strength of the part.
1. For the stress-strain curve shown below, please estimate the properties indicated. (a) Fracture Strain Please do your work on a separate sheet of paper, and put your answers in the boxes on the right. Be sure to include the proper symbol and units. Stress Strain 70 60 50 Stress (ksi) 240 30 20 10 70 0 0.000 60 50 Stress (ksi) 40 20 10 KULL 0 0.000 0.010 0.050 0.100 Strain (in/in) Stress Strain 0.020 0.030 Strain (in/in) 0.040 0.150 0.050 (b) Ultimate Tensile Stress (c) Fracture Stress (d) Proportional Limit (e) Elastic Modulus (1) Yield Stress (g) Tensile Toughness (Modulus of Toughness) (h) Modulus of Resilience
I need the answer as soon as possible
I need the answer as soon as possible
5. The following data were collected from a standard 0.505-in.-diameter test specimen of a copper alloy (initial length lo= 2.0 in.). After fracture, the total length was 3.014 in. and the diameter was 0.374 in. Load (Ib) Al (in.) 00000 3,000 6,000 0.00167 0.00333 7,500 0.00417 9,000 10,500 0.0090 0.040 12,000 0.26 12,400 11,400 0.50 (maximum load) 1.02 (fracture) a) Plot the data as engineering stress versus engineering strain. b) Compute the modulus of elasticity. c) Determine the yield strength at a strain offset of 0.002. d) Determine the tensile strength of this alloy. e) What is the approximate ductility, in percent elongation? f) Compute the modulus of resilience. g) Compute from the data and plot true stress versus true strain diagram.
Please calculate each material individually Steel 4340 Maraging Steel A1 7075
Estimate the theoretical fracture strength of a brittle material if it is known that fracture occurs by the propagation of an elliptically shaped surface cra of length 0.5 mm and having a tip radius of curvature of 0.005 mm, when a stress of 1040MPa is applied. Your answer must be in GPa. Write your answer to 1 decimal place. Answer: V 30 (0) 00 a W 4340 steel alloy. Determine the ductile to brittle transition
Small Question please answer
Part A The stress-strain diagram for a steel alloy having an original diameter of 0.40 in. and a gage length of 9 in. is shown in the figure below. (Figure 1) Determine the modulus of elasticity for the material. Express your answer to three significant figures and include appropriate units. HA ? Eapprox = Value Units Submit Request Answer Figure < 1 of 1 Part B a (ksi) 80 Determine the load on the specimen that causes yielding. 70 Express your answer to three significant figures and include appropriate units. 60 50 40 HA 30 20 Py = Value Units 10 € (in./in.) 0.04 0,08 0.12 0,16 0,20 0,24 0,28 O 0.0005 0.001 0.0015 0.002 0.0025 0.0030.0035 Request Answer Submit
The following data were obtained from the tensile test of Aluminum alloy. The initial diameter of testspecimen was 0.505 inch and gauge length was 2.0 inch. Plot the stress strain diagram and determine(a) Proportional Limit (b) Modulus of Elasticity (c) Yield Stress at 0.2% offset (d) Ultimate Stress and(e) Nominal Rupture Stress.
Stress Strain Diagram The Data shown in the table have been obtained from a tensile test conducted on a high-strength steel. The test specimen had a diameter of 0.505 inch and a gage length of 2.00 inch. Using software. plot the Stress-Strain Diagram for this steel and determine its: A= TTdT(050s A %3D 1. Proportional Limit, 2. Modulus of Elasticity, 3. Yield Strength (SY) at 0.2% Offset, 4. Ultimate Strength (Su), 5. Percent Elongation in 2.00 inch, 6. Percent Reduction in Area, 7. Present the results (for Steps 1-6) in a highly organized table. e Altac ie sheet (as problelle 4 A = 0.2.002 BEOINNING of the effort Elongation (in) Elongation (In) Load Load #: #3 (Ib) (Ib) 1 0.0170 15 12,300 0.0004 1,500 16 12,200 0.0200 0.0010 3. 3,100 17 12,000 0.0275 0.0016 4,700 18 13,000 0.0335 5. 6,300 0.0022 19 15,000 0.0400 0.0026 6. 8,000 20 16,200 0.055 0.0032 9,500 21 17,500 0.0680 0.0035 8. 11,000 22 18,800 0.1080 0.0041 11,800 23 19,600 0.1515 0.0051 24 20,100 0.2010 10 12,300 0.0071 25…