PROBLEM 3 A tensile test is performed on a brass specimen 10mm in diameter using a gage length of 50mm. When the tensile load P reaches a value of 20KN, the distance between the gage marks has increased by 0.122 mm. What is the Poisson's ratio if the diameter decreases by 0.00830 mm.?

PROBLEM 3 A tensile test is performed on a brass specimen 10mm in diameter using a gage length of 50mm. When the tensile load P reaches a value of 20KN, the distance between the gage marks has increased by 0.122 mm. What is the Poisson's ratio if the diameter decreases by 0.00830 mm.?

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.4P: A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the...

See similar textbooks

Similar questions

A tensile test was performed on a metal specimen with a diameter of 1 2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The dam were plotted on a load-displacement graph. P vs. L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/L =1392 kips/in. What is the modulus of elasticity?
A tensile test was performed on a metal specimen having a circular cross section with a diameter 0. 510 inch. For each increment of load applied, the strain was directly determined by means of a strain gage attached to the specimen. The results are, shown in Table: 1.5.1. a. Prepare a table of stress and strain. b. Plot these data to obtain a stress-strain curve. Do not connect the data points; draw a best-fit straight line through them. c. Determine the modulus of elasticity as the slope of the best-fit line.
The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
Q-
A steel specimen of 300 mm length and 30 mm diameter is subjected to tensile test in a computerizedUTM. Under 54 kN of tensile load, the final length and diameter are observed as 300.112 mm and29.99634 mm respectively. Calculate (a) the Poission’s ratio and (b) the values of three moduli.
A results below were recorded during tensile test for a steel specimen to be used to manufacture water reticulation steel pipes. The diameter of the specimen measured by an electronic vernier was found to be 0.597cm. Other measurements noted were the gauge length of 5.010cm,elongation 0.0635mm at load of 7.11kn, 7.33kn load at the yield point and 8.15kn load at the point of failure. The reduction of the cross-sectional at failure is estimated to be 35.06%. Calculate the yield stress in N/mm^2
A tensile test was performed on a metal specimen with a diameter of 1⁄2 inch and a gage length (the length over which the elongation is measured) of 4 inches. The data were plotted on a load-displacement graph, P vs. ∆L. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P y∆L 5 1392 kips yin. What is the modulus of elasticity?
1.5-7 The data shown in the table were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2 in.² in area and a gage length (the length over which the elongation is measured) of 2.000 inches. d. Estimate the value of the proportional limit. e. Use the 0.2% offset method to determine the yield stress. Load (kips) 0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0 4.5 5.0 ܩܙ ܘ 5.5 6.0 6.5 Elongation × 10³ (in.) 0 0.160 0.352 0.706 1.012 1.434 1.712 1.986 2.286 2.612 2.938 3.274 3.632 3.976 Load (kips) 7.0 7.5 8.0 8.5 9.0 9.5 10.0 10.5 11.0 11.5 12.0 12.5 13 Elongation × 10³ (in.) 4.386 4.640 4.988 5.432 5.862 6.362 7.304 8.072 9.044 11.310 14.120 20.044 29.106
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 a) Calculate the proportionality limit, modulus of elasticity, tensile strength, maximum uniform elongation, and contraction-elongation ratio of the metal. b) Since the measured diameter of the metal at break is 12 mm, find the constriction ratio and the actual stress at break.
The (G-E) diagram obtained in the tensile test performed on a metal sample with a diameter of 16 mm is as follows. The loads at points A, B and C and the elongation measured on l. 16 cm gauge length were determined as follows: B A B C Load (kgf) 4800 8400 7200 Elongation (mm) 0.192 28.8 38.4 c) Calculate the fracture work and the maximum elastic energy the metal rod can store. d) Find the cross-sectional area of a 6 m long rod made of this metal such that it can carry 12 tons of load with 2 times the safety of yield strength. How long does the rod extend under this load?
A Charpy V Notch (CVN) test was performed on a steel specimen and produced the readings shown in Table . Plot the toughness-versus-temperature relation and determine the temperature transition zone between ductile and brittle behavior.
2.7 The following readings were recorded during a tensile test of a mild steel specimen 24 mm wide by 10 mm thick and with a gauge length of 200 mm. Force (kN) 16 32 48 64 68 72 76 79 Elongation (mm) 0,066 0,133 0,198 0,264 0,281 0,304 0,355 1,125 Force (kN) 76,8 83,7 103,8 111 112,8 108 96 Elongation (mm) 3,75 6,66 15,00 25,00 36,5 45,0 50,0 The test piece fractured at a 50-mm elongation. Plot the load-extension dia- gram using the following scales: 10 divisions on the x-axis = 5-mm exten- sion; 10 divisions on the y-axis = 10 kN. On the same graph paper and using the scale 10 divisions on x-axis = 0,5-mm extension, and 10 divisions on y-axis = 10 kN, replot the elastic portion of the graph. Using the graphs, determine the (a) modulus of elasticity for mild steel; (b) yield stress; (c) ultimate tensile stress; and (d) percentage elongation.