Question

Magnesium oxide particles are compacted and fired at a high temperature to produce a strong ceramic
shape. The theoretical density of MgO is 3.58 g/cm³. The ceramic shape subsequently is weighed when
dry (340 g), after soaking in water (450 g), and while suspended in water (242 g). Calculate the apparent
porosity, bulk density and fraction of closed pores.

Expert Solution

Trending now

This is a popular solution!

Step by step

Solved in 4 steps

SEE SOLUTION Check out a sample Q&A here

Blurred answer

Similar questions

Finds the theoretical density of a solid that crystallizes into a face-centered cubic unit cell, where a = 3.48 Å and its molecular weight 40 g / mol
Janice is grilling a steak for her July 4th barbecue dinner. The steak initially weighs 300 grams and is 25 mm thick. After grilling it for a while, she considers the steak done, and measures it again: it now weighs 215 grams, and is 15 mm thick. For both the cooked and uncooked steak, she uses the thumb-test to determine the done-ness, i.e. she uses her thumb (area ~5cm2) to push down with a force of 5 N. The uncooked steak compresses by 7 mm, and the cooked steak by 2 mm. The change in elasticity of the steak on cooking is due partly to the loss of water volume (so that existing bonds get closer together) and partly to the creation of new bonds. Assume all of the difference in raw vs. cooked steak thickness is due to water loss that makes it thinner (25 mm thick in the uncooked steak, versus 15 mm thick in the cooked steak), and that the other dimensions of the steak (length and width) have not changed. By what percentage has the steak's volume decreased from the original value?…
One component of a metal sculpture consists of a solid cube with an edge of length 36.9 cm. The alloy used to make the cube has a density of 6610 kg/m³. Find the cube's mass. m = kg
A gunpowder explosion in a cannon reaches a gas pressure of 3.0E8 Pa. If the cross sectional area of cannonball is 75 cm^2 what force is applied
For a 40 wt.% Sn60 wt.% Pb alloy at 150\deg C, (a) what phase(s) is (are) present? (b) What is (are) the composition(s) of the phase(s)? (c) What is (are) the relative amount of the phase(s) in terms of mass fraction?
Using the value of 1.29 gcm^3as silk density, calculate a fiber equivalent diameter in μm if such fiber linear density was 0.99 den.
(Electroplating) A steel part with surface area A = 130 cm² is to be tin-plated. What average plating thickness will result if 15 amps are applied for 10 min in an acid sulfate electrolyte bath? The cathode efficiency for tin is E = 90% and the plating constant C = 4.21 x 10-2 mm³/amp-s. V = CIt V = ECIt d = V A Typical cathode efficiencies in electroplating and values of plating constant C. Compiled from [18]. Plate Metal Electrolyte Cadmium (2) Cyanide Chromium (3) Chromium-acid-sulfate Copper (1) Gold (1) Nickel (2) Silver (1) Tin (4) Zinc (2) Cyanide Cyanide Acid sulfate Cyanide Acid sulfate Chloride Plating Constant ca Cathode Efficiency % mm³/amp-s (in³/amp-min) 6.73 × 10-² (2.47 × 10-4) X 2.50 × 10-2 (0.92 × 10-4) 7.35 x 10-2 10.6 x 10-² 3.42 x 10-2 (2.69 × 10-4) (3.87 × 10-4) (1.25 × 10-4) 10.7 x 10-2 (3.90 × 10-4) 4.21 x 10-2 (1.54 × 10-4) 4.75 × 10-2 (1.74 x 10-4) 90 15 98 80 95 100 90 95 ¹Most common valence given in parentheses (); this is the value assumed in determining…