Answered: In rolling process, calculate the…

In rolling process, calculate the applied torque in (N.m) when w= 600mm, K = 275 MPa, n = 0.10, %3D ho=35 mm, hf=29mm, R=-373.3

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Von mises and tresca agree in pure shear

A: In machine design, mainly five failure theories are used to relate stress with the strength of…

Q: Rolling: A rolling operation is performed on a 5 mm thick sheet of low carbon steel (K=530, n=0.26…

A: Given:To find:

Q: If coefficient of friction µ in a rolling process is 0.5 and radius of roller is 1,000 mm, what is…

A: Given, Coefficient of friction = μ = 0.5 Radius of the roller = R = 1000 mm Maximum possible…

Q: See the figure below. This figure shows three compression processes A, B and C. Assuming that the…

A: Three compression processes A, B and C are done on same equipment and working fluid but different…

Q: the blanks: the center distance in (cm) of 4 direct contact rolling.cylinders. Cylinders A-D have a…

Q: A 300-mm-wide strip 25-mm thick is fed through a rolling mill with two powered rolls each of radius…

A: The answer has been attached in the form of images as follows:

Q: 3. During the rolling process, the average flow stress is 20,000 lb/in², determining the amount of…

Q: Drawing: A round rod of annealed 302 stainless steel (K = 1300 MPa and n = 0.3) is being drawn from…

A: Given:To find:

Q: A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that…

Q: During drawing process, using the Ao=5mm2, Af =4 mm2, K=200 MPa and n = 0.20, the average flow…

Q: required at the moment of reaching the yield point (ℇ = 0.002) b) Force required when you have a…

Q: process, a 150 mmx15 nd rotational speed is nis reduction is the m=

Q: In a 'tandem' rolling process, a wide metal strip passes continuously between four sets of rolls,…

Q: plate material is 300 MPa. The power required for the rolling operation in kW is closest to

A: Given, In a single pass rolling operation:h1=20mmh2=18mmR=250 mmwidth=100mmσ0=300 MPa We have to…

Q: The minimum possible thickness

A: Given; A thick sheet having 4 mm is rolled with 300 mm diamaterOr, d=300 mm t=4 mmFriction…

Q: entry angle = 15o. The starting diameter is 0.100 in. And the final diameter = 0.080 in. The…

A: first of all find out tru strain and then mean flow stress from given data.refer below image.

Q: please very urgent i need to slove all part

A: Step 1a.The kutzbach equation for calculating the degree of freedom of a planar mechanism is given…

Q: (3) A machine part of uniform thickness t = b/2.5 is shaped as shown and machined all over from AISI…

A: “Since you have asked multiple questions, we will solve the first question for you. If youwant any…

Q: A flat-rolling operation of 250 mm wide alloy stee Calculate roll torque

A: GIVEN: **Width (Wt)=250mm **Diameter of rollers (D)=600mm **Height before rolling (ho)=30mm**Height…

Q: Q3/A/ a steel slab is upset forged from: (50mm×200mm×100mm) to (25mm × 200mm × 200mm). If the…

Q: Write the difference between damped and undamped vibrations?

A: Answer :- The difference between damped vibration and undamped vibration has been summarised in…

Q: A cylindrical 4135 cold-rolled steel workpiece has an upsetting load applied at room temperature…

A: “Since you have posted a question with multiple sub parts, we will provide the solution only to the…

Q: A sheet 300mm wide 25mm thick with two drives, each with a radius of 250mm it is passed through a…

Q: Identify at least FIVE (5) factors that affect the Force, F in Figure

A: factors affect the force in above fig these factors leads to improper process and non uniform force…

Q: Find the angle of bite

A: Given; In single pass rolling bearing process using ;Diameter,d=510 mm R=255 mmwidth,W=110So,Acc.…

Q: (2) A round aluminium bar, with the initial diameter do = 36 mm, has to be cold formed into a…

Q: Explain the significance of rolling disc on inclined plane apparatus.

Q: uring the rolling process, the average flow stress is 20,000 lb/in², etermining the amount of…

A: Given Data The average flow stress is:γf=20000 lb/in2 The strength coefficient is:K=35000 lb/in2…

Q: a strain hardening exponent= 0.15. The roll force is 483,000 lb 583,000 lb 383,000 lb none

A: Given: to=4.5 intf=3.87 inK=30000 lb/in2n=0.15To determine:The roll force

Q: A strip (300x30 mm) is fed through a rolling mill with two powered rolls (each with radius of 300…

Q: Q4: Proof the validity true strain additive feature in compression deformation?

A: introduction; true strain gives the information of accurate view of stress-strain relationship.

Q: please very urgent with count the number on the graph i wil give u good feedback

A: Please see attached detailed solution/explaination below:

Q: Two thick slabs of 300mm each, the first one is used in cold rolling where μ=0.08 while the second…

Q: A hot/cold rolling setup is shown right. The operation first hot rolls a 3/8” thick plate, 12” wide…

A: Given: The thickness of plate in first roll, to = 3/8 in = 9.52 mm The width of plate, b = 12 in The…

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

In rolling process, calculate the
applied torque in (N.m) when w=
600mm, K = 275 MPa, n =
0.10,
ho=35 mm, hf=29mm, R=-373.3

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

I need the answer as soon as possible
Q1/ A two-high rolling mill is used to reduce plate that is 450 mm wide and 45 mm thick in a single pass to a thickness of 30 mm. The roll has a radius = 500 mm, and its speed = 25 m/min. The work material has a strength coefficient = 300 MPa and a strain hardening exponent = 0.15. Determine: Roll force 8,519,975.11 N 8,619,975.11 N none of the mentioned 8,419,975.11 N
If the plate thickness in the previous problem were 1 cm, would the thickness be sufficient for a JIC test? Assume these material properties: E = 205 GPa, v = 0.25.
Name the following terms
Asap
cylindrical roller of radius R1 = 1in. and length L = 1.5 in. is subjected to a load F = 1000 lb as it runs on a parallel roller with radius R2 = 1 in. Both rollers are made of AISI 4340 steel HB 320-340 (E = 30 Mpsi, ν = 0.28). The rollers are in combined rolling with 9% sliding. The coefficient of friction is µ = 0.33. Estimate the lifetime of the rollers.
Note:- • Do not provide handwritten solution. Maintain accuracy and quality in your answer. Take care of plagiarism. • Answer completely. • You will get up vote for sure.
Given: Flat rolled sheets are produced in wide rolling mills, but many products are manufactured from strip stock. The below figure is a free-body diagram of a shaft for a short slitting line where a single blade is placed in the center of the shaft and a motor drives the shaft through a pulley at the far right end. Find: The shaft diameter If the maximum shear stress is 40 MPa and the largest gage sheet causes a blade force of 2000 N,
Assume you are bending a 3/16” thick rolled plate of Al 6061-T6 at a 90-degree angle. The initial bend radius (after the part is bent in the press brake) is 0.35”. Look up material properties on the Internet a) What is the final bend radius after the part has “relaxed”?b) Is it within the 2-4% rule of thumb?Show your work, and write down any values you choose to reference/use.
Second problem only. Read and Solve carefully, make sure readable if it is in hand written form, include the units in every step and draw the diagram. Your work will be appreaciated much. Thanks! See attached figure for the problem.