Class work IdiameterGiven: metal specimen x-section (circular) = 0.55 in.Gage length = 2.030 fm.in.Fracture occurred atpounds #final lengthfinal dia.Determine28,500 €= 2.30 in.= 0.43 in.tensile stress in kşi c) Reduction of x-sect, areaa percentagepricentageas aa) Ultimate6) Elongation asNote: Gaye length - length over which elongation is measuredall

Initial diameter, Initial length, Failure load, Final length, Final diameter, To find: (a) Ultimate…

diameter Given: metal specimen x-section (circular) = D.55 in. Gage length = 2.030 in. Fracture occurred at pounds # final length final dia. Determine 28,500 = 2.30 h. = 0.43 in. tensile stress in ksi c) Reduction of as a a) Ultimate 6) Elongation as a Note: Gaye length length over which elongation is measured a percentage x-sect. area percentage

diameter Given: metal specimen x-section (circular) = D.55 in. Gage length = 2.030 in. Fracture occurred at pounds # final length final dia. Determine 28,500 = 2.30 h. = 0.43 in. tensile stress in ksi c) Reduction of as a a) Ultimate 6) Elongation as a Note: Gaye length length over which elongation is measured a percentage x-sect. area percentage

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Similar questions

Determine the deformation of the steel rod (inches) in the figure shown under the given loads Given: A1 = 0.91 in2, A? = 0.31 in2, P1 = 81 kips, P2 = 47 kips, P3 - 31 kips and E = 29x106 psi %3D %3D Your final answer should have three decimal places A1 A2 B. D' P3 P1 P2 -/- --16 in 12 in. 12 in.
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
Getting measurements from Figure , determine approximate values of the following items for steel with different carbon contents. Use one system of units only as specified by the instructor.a. Yield stressb. Ultimate strengthc. Strain at failured. Effect on modulus of elasticitye. Approximate toughness. Curves may be approximated with a series of straight lines.f. Comment on the effect of increasing carbon content on items a through e above.
The information in the photo attached shows elastic properties of a human tibula bone. If you were to take a small cuboidal cross section of the tibula bone and apply the ultimate shear stress, what would be the resulting strain? (a) 1.0 % (b) 6.7 % (c) 10 % (d) 15 % (e) None of the above.
A steel component is subjected to alternate cyclical loading. The steel follows Basquin's law for high cycle fatigue, o, x N = C, (where the stress amplitude is in MPa). Ignore the geometric detail and assume that Marin's modifying factors are all equal to 1. You are given the minimum stress ain = -213 MPa, the maximum stress omax = 213 MPa. The material data are Tensile strength oUTS = 539 MPa, Basquin's constant c, = 875 MPa, Basquin's exponent a = 0.085. a) Calculate the stress ratio R, the stress amplitude o, in MPa and the mean stress am in MPa. The answers are acceptable with a tolerance of 0.01 for R and of 1 MPa the stresses. R: MPa MPа b) Calculate the corresponding life, in 10° cycles, (tolerance of 0.1 106 cycles) N :
The state of plane stress shown occurs at a critical point of a steel machine component. As a result of several tensile tests, it has been found that the tensile yield strength is o, = 250 MPa for the grade of steel used. Determine the factor of safety with respect to yield using (a) the maximum shearing stress criterion, and (b) the maximum distortion energy criterion. ↑y 40 40 MPa 80 MPa 25 MPa ➜X
A load P is applied to a steel component which is supported an aluminum plate into which a 12 mm diameter hole has been drilled. Knowing that the maximum allowable shearing stress is 86.5 MPa in the steel and 160 MPa in the aluminum plate, determine the largest load which may be applied to the steel component. Provide your answer in kN with precision to two decimal points. 10 mm Answer: 12 mm 40 mm P 8 mm
Problem 4 Given two welded plates n A36 plates t= 3/ • fillet size w=1/4" Electrode Fexx= 70 ksi • plate width = 9" ● ● ↑ t=¾/2" = 2) = Pu= smaller of (1) A(2) w=1/4" Base Metal Strength, DRn is given by: ÞRn = 0.75(0.6Fu) (tBM)(Lw) t=3/8" Determine max Pu that can be applied to this connection ? hint: Dobtain Pue based on weld strength (transverse) BM strength = where tbm = thickness of the thinner connected plate Lw= length of the weld Fillet weld this side only i.e. lw= 9 in کہ ۔ Ри opy
Given: metal specimen x-section (circular) = 0.5sin Gaye length Fractured final final diameter Determine ^ = 2.030 In occured at 28, 500 # length = 2.30in dia = 0.43 in al Ultimate b7 Elongation c) Reduction tensile stress in ksi a percentage as of x-section area as a percentage
A steel bar of 22 mm diameter and 8 cm gage length was axially loaded in tension and the following load deformation diagram was obtained. Determine: a) The yield strength by 0.2% off-set method. b) Modulus of elasticity by initial tangent method. c) Modulus of elasticity by tangent method at 2/3 of the yield strength. d) Modulus of elasticity by secant method at 70% of ultimate strength. e) Strain in fracture.
A small aluminum alloy [E = 73 GPa] teeshape is used as a simply supported beam as shown. For this beam, a = 150 mm. The cross- sectional dimensions of the teeshape are b = 25 mm, d= 38 mm, and t=7 mm. After loads are applied to the beam at B, C, and D, a compressive normal strain of 490cis measured from a strain gage located at c= 9 rmm below the topmost edge of the tee stem at section 1-1. What is the applied load P? 3P Strain gage d a a H Answer: P = i