Answered: Using linear interpolation determine…

Using linear interpolation determine the DBTT of a given steel with the following Charpy tests results: 18 J at -18°C 28 J at -2°C 45 J at 5°C 60 J at 12°C -3.6°C -4.6°C -5.6°C -2.6°C

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: PLEASE MSKE SURE THE ANSWER IS CORRECT 100% Question 1: choose the correct answer: 1. Which of the…

A: Note: Hi! Thank you for the question As per the honor code, We’ll answer the first question since…

Q: y 6 mm 6 mm

Q: We would like to increase the yield strength of the bar through cold work. (a) Using the Copper…

Q: A Charpy V Notch (CVN) test was performed on a steel specimen and pro- duced the readings shown in…

A: Tabulate the values that are used to plot the graph. Temperature, C Toughness, Joule (N.m) 40 7…

Q: A tensile test was conducted on reinforcement steel bar having a diameter of 10 mm to record the…

A: For the given data of stress and strain, the stress vs strain curve has to be plotted. Also, the…

Q: 7. A solid aluminum cylinder is placed within an ASTM A501 steel tube as shown. Compute the stresses…

A: Given Data: The diameter of the solid aluminum cylinder is d1=3 in. The diameter of the steel tube…

Q: SEATWORK The figure as shown, ADD the last 2 digits of your i.d. number in the load P. Student i.d.…

A: Determine load for every P in three case

Q: A steel specimen having a modulus of elasticity equal to 29x103ksi has a width of 1.0in and…

A: Given Data: Modulus of elasticity, E =29×103 ksi Width of specimen, B =1.0 in Thickness of specimen,…

Q: A tension test was conducted for a cylindrical specimen of stain-less steel having an initial…

A: The given data is: Initial diameter, Di=15.35 mm Final diameter, Df=10.25 mm

Q: In the connection shown, 1/4-in. side and end fillet welds are used to connect the 3-in.-by-1 in.…

Q: If the bridge contains a welded flange in a fracture-critical member, does the steel have adequate…

Q: A UNIFORMLY DISTRIBUTED FORCE OF Px=3 (COMPRESSION), Py=6 (TENSION) AND Pz=9 (COMPRESSION) IN THE X,…

A: Given data Px=3KN (COMPRESSION), Py=6KN (TENSION) AND Pz=9KN (COMPRESSION) IN THE X, Y AND Z…

Q: The composite shaft shown in the figure consists of a bronze sleeve (1) securely bonded to an inner…

Q: A tensile test specimen of stainless steel alloy having a diameter of 0.550 in. and a gage length of…

Q: Determine if w12x14 (A36) section is Compact, Non-Compact or slender. Show neat handwriting and…

A: The given data is shown below: W12×14A36 steel

Q: A composite beam is made of two brass (E - 111 GPa) bars bondedt subjected to a bending moment of…

A: Given:- a = 10 mm b = 65 mm c = 20 mm d = 45 mm BM = 250 N-m

Q: 0.5 mm 350 mm - Bronze A = 1500 mm² E = 105 GPa x = 21.6 x 10-6C 450 mm Aluminum A = 1800 mm² E = 73…

Q: a) Explain the performance metrics as an analytical methods for materials selection used in…

A: Given Diagram with stiffness and angle of twist equations To answer a) Explain the performance…

Q: A tensile test was conducted on a mild steel bar. The following data was obtained from the test:…

Q: Tensille strengin 450 MPa (65,000 psi) Strain = 0 Stress = 0 MPA 500 Stress = 0 psi 70 Strain = 0…

Q: The following terms apply to LRFD (limit state design) and ASD. E. Yield Strength L. Plastic…

A: LRFD - It focuses on developing load and resistance factors. ASD - It focuses on ensuring that…

Q: The composite bar as shown in figure is placed between two rigid walls. If P = {(50+CN) KN, Find the…

Q: Give me right solution A steel bar that is 28 feet long is subjected to a 251 kip load. Maximum…

Q: A storage tank of air, 30 inches in diameter, is to withstand an internal pressure of 180 psi with a…

A: Given:- d=30 inches internal pressure=180 psi design factor=3.5 C1020 annealed relative strength=92%…

Q: 400 тm 500 mm 800 mm Steel Aluminum Bronze A = 800 mm² E = 200 GPa a = 11.7 x 10-6/°C a = 23.5 x…

A: As the temperature is increased so material will offer resistance by having compressive stress. So…

Q: A combined section of steel and copper is subjected to a compressive load. Refer to the table below…

A: Assume that 100 kN load is applied. Then using equilibrium and compatibility equation the load…

Q: the composite section as shown in figure 1, determine the following. 1. The value of x̄ 2. The value…

Q: lost steel reinforcing bars manufactured in the U.S. exhibit a sharp yield plateau. Two xceptions,…

A: The gradual yielding of quenched-and-tempered and straightened reinforcing steel is due to the…

Q: Sample: Malleable Steel (AISI 4145) Original Diameter: 6.14mm Gauge Length: 55 mm Final Length:…

A: Given data, Original diameter D = 6.14 mm Gauge length L = 55 mm

Q: The part of the shown graph shows no permanent deformation. Select one: a. Black b. Red C. Green d.…

A: The given graph is stress-strain curve of mild steel.

Q: Engineering strain of a mild steel sample is recorded as 0.100%. The true strain is 1. 0.010% 0.055%…

Q: USE NSCP 2015 as reference: B. Minimum/maximum value of steel strain(st) (from nscp2015). C.…

Q: 8

A: Given data- Gage Length of brass(L) = 50 mm Diameter (D) = 10 mm Tensile load (P) = 20k N Increase…

Q: The aluminum shell is fully bonded to the brass core, and the assembly is unstressed at a…

A: Given Data:Temperature of 78°FChange in Temperature = 210°FBrass…

Q: A mild steel bar of 2cm is subject to tensile test. The bar yields under a load of 80kN. It reaches…

A: Given data, Diameter of steel bar = 2 cm Yield under load = 80 KN Maximum load = 150 KN Breaking…

Q: Question one: Question 1: For the following values of state stress find the factor of safety using…

A: FACTOR OF SAFETY : Effective stress, Using MSS = 25 - 15 - (-5) / 3 = 15 FOS is 0.5 Using MDE =…

Question

Using linear interpolation determine the DBTT of a given steel with the following
Charpy tests results:
18 J at -18°C
28 J at -2°C
45 J at 5°C
60 J at 12°C
-3.6°C
-4.6°C
-5.6°C
-2.6°C

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step 5

Step 6

Step by step

Solved in 6 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

10/10 FIND STRESS IN STEEL MATERIALS IN COMPOSITE COLUMIN SHOWN BELOW. IF E st= 200 kN/MM2, Ealu.=70 kN/MM2 100 kN RALU=30 MM Aluminum Steel 1m R ST 20 MM
A steel specimen is tested in tension. The specimen is 2 in. wide by 2.3 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 30 kips and fractured at 40 kips. a) Determine the tensile stress at yield and fracture; b) If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 2 the yield stress.
An unstiffened web I-section fabricated from a 10 mm thick plate by fillet welding as shown in the figure. If yield stress of steel is 250 MPa, the maximum shear load that section can is take is [2 Marks] 10 mm 300 mm 10 mm 200 mm
Part B,G, and H. Please provide proper units
QI/ An aluminum bar carries the axial loads at the positions shown in Fig. 1, below. The diameter for part AB, BC and CD is 35 mm, 40 mm and 30 mm, respectively. The elastic modulus for aluminum is 72.4 x 10 N/mm. Determine the internal stresses at section (A-B), (B-C) and (C- D), and the elongation (AL) in length at each part of aluminum due to loading. в D 37 kN 10 kN 45 kN 18 kN 1000 mm 800 mm I 600 mm Fig. 1
Condition #1:E A structural support for a machine is subjected to a static compression load of 20 kN. The support is manufactured from a circular rod made from SAE 1040 Hot Rolled steel. Specify suitable diameter for the cross section of the rod based on the basic size. Steel data are available in Table A-10 from the textbook. Condition #2: The same structural support of the basic size determined in Condition 1 is subjected to a tensile load of 15 kN that is repeated several thousand times over the life of the machine. This load is not an addition to the 20 kN. Specify a suitable steel that is suitable to this application based on the basic size determined in Condition #1. Loading of Condition #1 does not apply here. Condition #3: The same structural support from Condition 2 is heated from room temperature of 25°C. The support is placed inside a frame on both ends. There is a total clearance of 0.2 mm between the support and its frame. Initial length of the rod is 200 mm. Specify the…
A composite beam is made of two brass [E = 120 GPa] bars bonded to two aluminum [E = 73 GPa] bars, as shown. The beam is subjected to a bending moment of 445 N-m acting about the z axis. Using a = 15 mm, b = 125 mm, c = 30 mm, and d = 75 mm, calculate (a) the maximum bending stress in the aluminum bars. (b) the maximum bending stress in the brass bars. Z Aluminum C Aluminum Answers: (a) Ogl Brass (b) Obr= i i b Brass a MPa MPa
Find the value of p
Date: Course: Time: Pind the vertical movement os is 120 KN Stsel Aluminum 3 m Im B P=120 kat Aluminum A = 900 mm² E = 70 GN m² steel A= 600 mm E 200 GNM² %3D
The composite material is fastened to their junction at rigid plate B and attached to rigid fixed supports at both ends subjected to two loads of 12k positioned symmetrically at B. Determine the stresses and their corresponding behavior for each material. Use 2 decimal places in every solved value. 亚 А 12k 12k 1 ft Steel Est = 29 x 10° psi Ast = 1.03 in? B Aluminum 2 ft Eal = 10 × 106 psi Aal = 8.92 in² C
A steel bar of 22 mm diameter and 8 cm gage length was axially loaded in tension and the following load deformation diagram was obtained. Determine: a) The yield strength by 0.2% off-set method. b) Modulus of elasticity by initial tangent method. c) Modulus of elasticity by tangent method at 2/3 of the yield strength. d) Modulus of elasticity by secant method at 70% of ultimate strength. e) Strain in fracture.