Construct the hy pothetical phase diagram for metal A and B between temperature of 600C° and 1000 C° given the following information:The melting point of A is 940 Cº.The solubility of B in A is negligible at all temperaturesThe melting point of metal B is 830 Cº.The maximum solubility of A in B is 12%A, which occurs at 700 Co.At 600 C°, the solubility of A in B is 8%A.One eutectic occurs at 700 C° and 75%B.A second eutectic occurs at 730 C° and 60%B.A third eutectic occurs at 755 C° and 40%B.One congruent melting point occurs at 780 C° and 51%B.A second congruent melting point occurs at 755 C° and 67%B.There exist two intermetallic compounds: AB at 51%B and AB2 at 67%B.Note all composition are in weight percent.

according to the given question

Construct the hypothetical phase diagram for metal A and B between temperature of 600 C° and 1000 C° given the following information: The melting point of A is 940 Cº. The solubility of B in A is negligible at all temperatures The melting point of metal B is 830 Cº. The maximum solubility of A in B is 12%A, which occurs at 700 C°. At 600 Cº, the solubility of A in B is 8%A. One eutectic occurs at 700 C° and 75%B. A second eutectic occurs at 730 C° and 60%B. A third eutectic occurs at 755 C° and 40%B. One congruent melting point occurs at 780 C° and 51%B. A second congruent melting point occurs at 755 C° and 67%B. There exist two intermetallic compounds: AB at 51%B and AB2 at 67%B. Note all composition are in weight percent,

Construct the hypothetical phase diagram for metal A and B between temperature of 600 C° and 1000 C° given the following information: The melting point of A is 940 Cº. The solubility of B in A is negligible at all temperatures The melting point of metal B is 830 Cº. The maximum solubility of A in B is 12%A, which occurs at 700 C°. At 600 Cº, the solubility of A in B is 8%A. One eutectic occurs at 700 C° and 75%B. A second eutectic occurs at 730 C° and 60%B. A third eutectic occurs at 755 C° and 40%B. One congruent melting point occurs at 780 C° and 51%B. A second congruent melting point occurs at 755 C° and 67%B. There exist two intermetallic compounds: AB at 51%B and AB2 at 67%B. Note all composition are in weight percent,

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Your team has invented a compound for use in refrigeration processes, R−X. You have asked your…

A: The data given for the refrigeration process is T=300 KP=7.0282 barv=0.83357 cm3/gv=29.246…

Q: Reproduce the binary phase diagram depicted in Fig. 3.20. For the composition shown at X, mark on…

A: Binary Phase diagrams: These are temperature vs composition diagrams in which two phases are…

Q: Describe the phases present at the eutectic temperature when the overall composition is x(Cu)= 0.5

A: The detailed phase diagram of Ag-Cu is:

Q: Temperature, °C 10 -10 -20 -30 NaCl 0 Ice + liquid (brine) Liquid (brine) 10 Ice + salt 20 Salt +…

Q: 1. The binary phase diagram for the silver (Ag) and germanium (Ge) system is shown in Figure 1. (a)…

Q: Copper (Cu) and silver (Ag) alloys form a binary alloy system that dissolves each other completely…

A: Please find the solution below

Q: Presume that we have 100 grams of an alloy with overall chemical composition of 90 wt. pct. tin and…

A: The mass of alloy, m = 100 gm The composition of the alloy = 90 wt%Sn and 10 wt% Pb The temperature…

Q: 5. For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, ii. Calculate the…

Q: The phase diagram of copper-nickel is shown. A Cu-Ni alloy bar has an original composition as…

A: All the parts are solved properly with detailed explanation.Hope you got your answer. If any query…

Q: B/ Aluminum (Tm=660 OC) and Silicon (Tm=1410 OC) were fully dissolved in each other in the liquid…

A: Given: The melting point of pure Al with 0% Si, Tal = 660°C The melting point of pure with 0% Al,…

Q: TC C) 1600 3 2 1 1400 5 1148 1200아 7 100아 10 800 727 600 11

A: To determine the compositions at the marked position in the Iron-iron carbide diagram.

Q: Given a blank phase diagram, label the solid, liquid, and gas phases for a pure substance. Give the…

Q: c) The Cu-Zn phase diagram is shown in Figure 2. i) For a sample of composition 40 wt% Zn and 60 wt%…

Q: Use the phase diagram for carbon (shown at right) to describe the phase changes that a sample of…

Q: 1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After…

A: Given: Mass of steel=1000 grams Weight % of carbon=1.5 % To find: The amount of pure iron or pure…

Q: Which of the following statements are true about the following phase diagram? Group of answer…

A: At atmospheric pressure three allotropic forms of iron exist: alpha iron (α-Fe), gamma iron and…

Q: 7. Consider 1.5 kg of a 99.6 wt% Fe-0.4 wt% C steel that is cooled to a temperature just below the…

A: In this problem we are asked to consider 2.0 kg of a 99.6 wt% Fe-0.4 wt% C alloy that is cooled to a…

Q: At what temperature does the first liquid phase form at 90% Ni? T(°C) 1600 1500 1400 1300 1200 1100…

Q: 13) If you have an alloy with a composition of 22 wt% Ag at a temperature of 779.1° C, identify: a)…

Question

Construct the hy pothetical phase diagram for metal A and B between temperature of 600
C° and 1000 C° given the following information:
The melting point of A is 940 Cº.
The solubility of B in A is negligible at all temperatures
The melting point of metal B is 830 Cº.
The maximum solubility of A in B is 12%A, which occurs at 700 Co.
At 600 C°, the solubility of A in B is 8%A.
One eutectic occurs at 700 C° and 75%B.
A second eutectic occurs at 730 C° and 60%B.
A third eutectic occurs at 755 C° and 40%B.
One congruent melting point occurs at 780 C° and 51%B.
A second congruent melting point occurs at 755 C° and 67%B.
There exist two intermetallic compounds: AB at 51%B and AB2 at 67%B.
Note all composition are in weight percent.

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps with 1 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Types of Phase Diagrams and Its Applications in Metallurgy

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Hi i keep getting these wrong
Given the equilibrium phase diagram (a) below, briefly describe the mechanisms of precipitation hardening/strengthening of an aluminium alloy making reference to the transitions shown in (b) below to X, X to A, X to D, A to B and A to C. а +0 D B Time (a) (b) - anedua Temperature
Consider the phase diagram below. The three points A, B, and C are at concentrations of 26.4, 31.3, and 34 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300 L (liquid) 1200 20 A B C L + a C1 S liquidus L + a solidus a (solid) 50 wt% Ni a. Walpha=0.21; WL=0.33; Walpha/WL = 13.17 b. Walpha=0.09; WL=0.32; Walpha/WL = 15.00 c. Walpha=0.07; WL=0.46; Walpha/WL = 11.17 d. Walpha=0.14; WL=0.37; Walpha/WL = 9.00
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
A hypothetical eutectic phase diagram for metals A and B shows that cooling a liquid melt with a concentration of 50 wt% A-50 wt% B to just below 625 °C (eutectic isotherm temperature) results in simultaneous formation of alpha and beta phases. The phase diagram also shows that alpha (A rich) and beta (B rich) phases exist at left and right extremes of the phase diagram, respectively. At the eutectic isotherm temperature, the maximum solubility of B in A and A in B is 10 wt% and 5 wt%, respectively. The phase diagram does not have any intermetallic compounds. A new solid alloy is made by melting together 86 gr of a 40 wt% A-60 wt% B alloy with 136 gr of 65 wt% A-35 wt% B alloy followed by cooling the melt to 400 °C. If the new alloy is heated up from 400 °C to just below 625 °C, answer the following questions: a. Calculate the overall alloy composition. b. Determine phases present and calculate their respective masses. Calculate the masses of the primary phase, eutectic phase, and…
Consider the phase diagram below. The three points A, B, and C are at concentrations of 27, 31.9, and 33.8 wt% Ni respectively. The ends of the tie line are at C1 = 25% wt% Ni and C2 = 35 wt% Ni. What are the weight fractions of the alpha phase at A and the L phase at B, as well as the alpha phase/L phase ratio at C? T(°C) 1300-L (liquid) 1200 20 ABC L + a C1 30 S C2 liquidus 40 L + a solidus α (solid). O a. Walpha=0.12; WL=0.41; Walpha/WL = 9.41 O b. Walpha=0.27; WL-0.26; Walpha/WL = 11.11 O c. Walpha=0.15; WL-0.26; Walpha/WL = 11.80 Od. Walpha=0.20; WL-0.31; Walpha/WL = 7.33 50 wt% Ni