Describe the phases present at the eutectic temperature when the overall composition is x(Cu)= 0.5 This image represents a phase diagram for a binary alloy system of Silver (Ag) and Copper (Cu). The diagram plots temperature (T) in Kelvin (K) on the vertical axis against the mole fraction of copper [x(Cu)] on the horizontal axis.### Key Features:- **Temperature Range:** The temperature axis ranges from 300 K to 1400 K.- **Composition Range:** The composition ranges from pure Ag (x=0) to pure Cu (x=1).- **Phases:** - **Liquid Phase:** The upper region is labeled "Liquid," indicating that above this line, the alloy exists in a liquid state. - **Solid Phase (FCC):** Multiple regions are marked "Fcc" (Face-Centered Cubic), indicating solid-phase formation in this crystalline structure.- **Lines and Curves:** - The **liquidus line** demarcates the boundary between liquid and solid-liquid mixtures. - The **solidus line** lies below the liquidus line and separates solid-liquid mixtures from wholly solid phases.- **Critical Point:** A specific point is annotated on the diagram, suggesting special interest, such as a eutectic, peritectic, or azeotropic point.This diagram is crucial for understanding the phase transitions and solidification behavior of the Ag-Cu alloy system.

The detailed phase diagram of Ag-Cu is:

Answered: Describe the phases present at the…

Engineering

Mechanical Engineering

Describe the phases present at the eutectic temperature when the overall composition is x(Cu)= 0.5

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 1.5-kg specimen of a 88 wt% Pb-12 wt% Sn alloy (Animated Figure 9.8) is heated to 220°C; at this temperature it is entirely an a- phase solid solution. The alloy is to be melted to the extent that 50% of the specimen is liquid, the remainder being the a phase. This may be accomplished either by heating the alloy or changing its composition while holding the temperature constant. (a) To what temperature must the specimen be heated? i °C (b) How much tin must be added to the 1.5-kg specimen at 220°C to achieve this state? i kg
Could someone explain in detail how to solve this problem please. I really dont understand it. Thank you so much.
BI (a) Figure BI below shows the equilibrium phase diagram of hypothetical A - B alloy system. Answer the following questions. What are technical names of Line A and Line B? What do they signify? (i) (ii) With the aid sketches, portray the microstructures and phases that are present for the 20wt%A-80wt%B alloy (Alloy A) at the temperatures of 780 °C, 670 °C, 652 °C, and 500 °C, respectively. (iii) Assume an A - B alloy (Alloy B) has 60wt%a - 40wt%L, in terms of weight, at a temperature of 652 °C. Determine the overall composition of Alloy B. (o) emai 700 8 600 500 400 800 0 A 760 °C Line B W a /9.5 20 Line A a + L 650 °C 40 Liquid (L) wt%B Figure B1 52.5 a + ß 60 B+L 80 93.7 B 100 B
The Iron-Carbon system: Phase Diagram 1. You heat treated a 1045 steel plate by heating it to 900°C and slowly cooling it to 725 °C, which is below the eutectoid temperature. What phases are present at 725°C? What are the compositions of each phase at 725°C? What are the weight fractions of each phase at 725°C? What microconstituents are present at 725°C? What are the compositions of each microconstituent at 725°C? What are the weight fractions of each microconstituent at 725°C?
The lead and tin are partially dissolved in each other in solid state although they completely dissolved in liquid state. They form eutectic from solid solutions alfa (a) and beta (B) at alloying composition 62% tin and 38% lead, the eutectic forming temperature is 184°C. Alfa contained 20% tin dissolved in 80% lead at 184°C while beta consist of lead dissolved in tin at 184°C. If the 100 g of eutectic contained 45.5 g of alfa at 184°C.Knowing that the melting temperatures of lead and tin are 329°C and 232°C respectively, and the solubility of tin and lead in each other's diminished to zero at room temperature. Answer the following a) Plot the phase diagram for lead-tin system label all phases and temperature. b) What is the composition of beta at eutectic temperature. c) For 40 % lead alloy calculate the phase amount and composition at 350°C, 170°C, and Tr
I need the answer as soon as possible
For alloys of two hypothetical metals A and B, there exists an a, A-rich phase and a b, B-rich phase. From the mass fractions of both phases for two different alloys (given below), which are at the same temperature, determine the composition of the phase boundary (or solubility limit) for the following: Alloy composition Fraction a Phase Fraction b Phase 60wt%A-40wt%B 0.60 0.40 30wt%A-70wt%B 0.12 0.88 a) a Phase = ___________ wt%A b) b Phase = ___________ wt%A
(a) Determine the composition of each phase at 1300C, 1250C, and 1200C temperatures. Indicate wt%Ni of the first solid to form and the last liquid to solidify. Show it on phase diagram below.
A NIO-20 mol % Mgo ceramic is allowed to solidify. (See the figure below.) Temperature (°C) 2800 2600 2400- 2200 2000 L (Ni, Mg)0 40 60 80 MgO Mole percent MgO NIO 20 (a) Determine the composition (in mol% MgO) of the first solid to form. 80 x (b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions. 35 X%
Determine the composition of the phases;
The solubility of tin in lead matches that required for precipitation hardening. Yet tin does not age-harden lead satisfactorily. Suggest a reason why it does not.
(a) Sketch a Pressure-Temperature phase diagram for a pure substance X where liquid X is less dense than solid X. Insert an isobar at 1 atm and an isotherm at 300 K. Clearly label all physical states, triple point, critical temperature and any normal transition temperatures.