(a) Figure 5 shows a phase diagram for the Nb-80 wt% W alloy which is solidified under under the nonequilibrium condition. Evaluate (i) the liquidus temperature (ii) the non-equilibrium solidus temperature (iii) the freezing range

(a) Figure 5 shows a phase diagram for the Nb-80 wt% W alloy which is solidified under under the nonequilibrium condition. Evaluate (i) the liquidus temperature (ii) the non-equilibrium solidus temperature (iii) the freezing range

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Please use phase diagram to explain why micro-segregation and macro-segregation happen during practical solidification.
Provide a hypothetical procedure for measuring the phase diagram at different temperatures.
Consider 1.0 kg of austenite containing 1.15 wt% C, cooled to below 727 °C (1341 °F). (a) What is the proeutectoid phase? (b) How many kilograms each of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid phase form? (d) Schematically sketch and label the resulting microstructure. Temperature (°C) 1600 1400 1200 1000 800 600 1538°C 400 0 -1493°C 1394°C 912°C y, Austenite 0.76 0.022 a, Ferrite 5 Y+L 2.14 Composition (at% C) 15 10 1147°C a + Fe3C L 4.30 y + Fe3C 727°C 20 Cementite (Fe3C) 5 6 4 (Fe) Composition (wt% C) Adapted from Binary Alloy Phase Diagrams, Vol. 1, 2nd edition, T. B. Massalski (Editor-in-Chief), 1990. Reprinted by permission of ASM International, Materials Park, OH. 25 2500 2000 1500 -1000 6.70 Temperature (°F)
1. Specify all temperature-compositicn points at which eutectics, eutectoids and peritectics. At 700 degrees Celsius and composition of 20% by weight of copper, calculate the compositions by fraction of each phase for copper? 1700 1500 L. 1300 1100 900 TiCu- 700 Ti:Cu4 500 20 40 60 (Ti) Composition (wt% Cu) to (0o) anjesedwa
A 50 wt% Pb-50 wt% Mg alloy is slowly cooled from 700 °C (1290 °F) to 400 °C (750 °F). (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? Temperature (°C) 700 600 500 400 300 200 100 2 0 0 (Mg) 560°C First solid (21 wt% Pb) α 20 465°C 5 a + L Composition (at% Pb) 40 10 L a + Mg₂Pb 20 60 Composition (wt% Pb) Last liquid (67 wt% Pb) 30 Mg₂Pb 40 T T L + Mg₂Pb M 18 80 L + Mg₂Pb 70 100 B B+ Mg₂Pb T B + L D T 1200 1000 800 600 400 200 100 (Pb) Temperature (°F)
3) You see Al-Cu phase diagram below and two microstructures (A and B) having the same nominal composition of 3 percent Cu. In these microstructures, matrix is a and spheres refer to CuAl₂ particles. In A and B, the size of big particles are the same. a) For the same volume constant, if we heat treat the both microstructures at T₁ for a long time, is there any changes in both microstructures? If so, what is that? And is the changes the same for both A and B? Is the rate of changes the same for A and B? Draw the final microstructures of A and B if any changes occur you think so. Temperature a AI 2 I 4 a +CuAl2 1 6 Copper,% CuAl2 α
Referring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…
Consider the binary alloy phase diagram shown schematically below. The left-hand side denotes phase a, and the right-hand side the phase ß. The intermediate region is a coexistence regime with both a and ß phases. The three points 1, 2 and 3 in the coexistence region are at 22.8 wt% A, 28.2 wt% A, and 33.7 wt % A respectively. If the points on the phase boundaries L and R are at 20 wt% A and 39 wt % A, respectively, what is the fraction of a phase at 1, 2 and 3? (This question has only one correct answer) T(°C) A-B binary alloy 1400 Coexistence region 3 1 2 1100 B 20 % 40 % Weight % A
Question: A 50 wt% Ni–50 wt% Cu alloy is slowly cooled from 1400°C (2550°F) to 1200°C (2190°F). (a) At what temperature does the liquid solidify? (b) What is the composition of this last remaining liquid phase?
Silicon having a melting point of 1412°C forms an alloy with aluminum having a melting point of 660°C. The solidification temperature of the alloy is observed to be at 580°C at which the mass fraction of silicon is 0.125 Represent the liquid-solid diagram from the given data. Determine the phases present in the following conditions
Material science Assuming this system forms a laminar type eutectic, determine the volume proportion of phases for an equilibrium solidified 50% Pb alloy. Sketch the expected microstructure.
A 10 30 70 1) For an A-B alloy of composition 25 wt% B (i) Draw the microstructure at T (just above the eutectoid temperature) and calculate the fraction of each phase in the microstructure. (ii) Draw the microstructure at T (just below the eutectoid temperature) and determine the amount of each phase, i.e., fraction of proeutectoid alpha, eutectoid alpha and eutectoid beta. 2) Provide a brief summary of phase transformations which are often observed in the iron-carbon alloy system due to various heat treatment procedures carried out to tune the microstructure. Compare mechanical strength and ductility of the materials/microstructures that form as a result of such heat treatment processes.