A NIO-20 mol % Mgo ceramic is allowed to solidify. (See the figure below.)Temperature (°C)280026002400-22002000L(Ni, Mg)040 60 80 MgOMole percent MgONIO 20(a) Determine the composition (in mol% MgO) of the first solid to form.80x(b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions.35X%

(a) Determine the composition (in mos MD) of the first sold to form (b) Determine the composition…

A NIO-20 mot% Mgo ceramic is allowed to solidify. (See the figure below.) Temperature (°C) 2800 2600 2400- 2200 2000 L (Ni, Mg)0 NIO 20 40 60 80 MgO Mole percent MgO (a) Determine the composition (in mol% MgO) of the first solid to form. 80 x (b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions. 35 X%

A NIO-20 mot% Mgo ceramic is allowed to solidify. (See the figure below.) Temperature (°C) 2800 2600 2400- 2200 2000 L (Ni, Mg)0 NIO 20 40 60 80 MgO Mole percent MgO (a) Determine the composition (in mol% MgO) of the first solid to form. 80 x (b) Determine the composition (in mol% MgO) of the last liquid to solidify under equilibrium conditions. 35 X%

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Hi i keep getting these wrong
In a binary Fe-Fe3C system, what is the transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the concentrations of the total and partial phases? Data: eutectoid temperature: 723 ºC, eutectoid concentration: 0.76% C, limit concentration of ferrite: 0.022%, limit concentration of cementite: 6.7%.
Determine the composition and fraction with 50% Ni and 1300 ° C
Compare the diffusion coefficients (in cm²/s) of nitrogen in BCC and FCC iron at the allotropic transformation temperature of 912°C. Decc -153606 X Your response differs from the correct answer by more than 10%. Double check your calculations, cm²/s -1976-7 Dicc x Your response differs significantly from the correct answer. Rework your solution from the beginning and check each step carefully. cm2/s
Use the first image to solve two part question
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
Please help me urgent
Should correct
At what temperature does solidification form at 10% Ni? T(°C) 1600 1500 1400 1300 1200 1100 1000, Answer: L (liquid) L+a solidus liquidus 20 40 60 wt% Ni 86 100
Calculate the volume of water in ltrs
1000 grams of steel containing 1.5 weight percent carbon is heated to complete melting. After equilibrium is achieved, we slowly cool the alloy. At 720C we keep the alloy to maintain equilibrium. Determine the amounts of the following, in grams. Pearlite Proeutectoid phase Total cementite
*About the Pb/Sn binary system, find the percentages of phases at room temperature for each of the following alloys. Alloy Chemical composition Percentages of phases at room temperature no. 20%Sn,80% Pb 40% Sn,60% Pb 3 62% Sn,38% Pb 70%Sn,30% Pb 90% Sn, 10% Pb 4