QUESTION 4Compute the expected properties of ultimate strength (Suc) of a composite made from S-glass fibers and an epoxy matrix. The volume fraction of fibers is 30%. (Unit ispsi.)Properties of Sample Matrix and Filler MaterialsTensile strengthTensile modulusSpecific weightksiMPa10 psiGPaIbVinIN/mMatrix materials:PolycsterЕрохуAluminumTitanium1018690.402.760.04712.71240.563.860.04712.745310117010.016.5691140.10027.11700.16043.4Filler materials:S-glassCarbon-PANCarbon-PAN (high-strength)Carbon (high-modulus)6004708203254140324012.533.54086.22312766900.090.0640.06524.417.456502200345017.710019.00.07821.2Aramid001310.05214.1Click Save and Submit to save and submit. Click Save AlL Answers to save all answers.Save All Arto searchIA

Tensile strength of S-glass fibers, σf=600 ksi=600×103 psi Tensile strength of Epoxy matrix, σm=18…

Answered: Compute the expected properties of…

Compute the expected properties of ultimate strength (Suc) of a composite made from S-glass fibers and an epoxy matrix. The volume fraction of fibers is 30%. (Unit is psi.)

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: (a) Figure Q4 shows a composite body used in a certain application. Determine the centroid (x, y) of…

A: A composite crossection is given as follows

Q: 4. Shear and Moment Diagram: 500 lb/ft A B 1500 lb/ft 6 ft 4 ft 4 ft- Shear Equation Moment Equation…

Q: A circular FRP composite rod with continuous and aligned fibers has a3 in. diameter. The rod is…

A: Given: Diameter of the FRP composite rod is D=3 in. The span of the rod which is simply supported is…

Q: For the composite bar indicated, determine the permissible bending moment when the bar is bent about…

Q: A cantilever beam of has a length L = 75 mm, of square cross-section of thickness, t = of a CFRP…

Q: A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 65%…

Q: A fiberglass composite consists of epoxy matrix reinforced with glass fibers. The modulus of…

A: Given: Modulus of elasticity of glass fiber = 65 GPa Modulus of elasticity of epoxy = 7 GPa Volume…

Q: An epoxy (E=2.4 GPa) is reinforced with carbon fiber with module of elasticity equal to 260 GPa.…

A: The modulus of elasticity of the epoxy is Em=2.4 GPa. The modulus of elasticity of the fiber is…

Q: A FRP composite includes 40% continuous and aligned Aramid fibers by vol-ume. The moduli of…

A: Modulus of elasticity of polymer(Em)=3.9GPaModulus of elasticity of fibre(Ef)=130GPa

Q: A circular FRP composite rod with continuous and aligned fibers has a 3 in. diameter. The rod is…

A: Diameter of the FRP composite rod is D =3 in.The span of the rod which is simply supported is L=4 ft…

Q: for a fiber reinforced composite material, assume Fibre's volume fraction is 0.3. what is the…

Q: Name three functions of the matrix phase in fiber-reinforced composites. State the reason for the…

A: The material which has high strength / weight and also modulus/weight and has three components of…

Q: Determine the total area of the composite figur e . (mm^2) Determine the x coordinate of the…

Q: A composite beam is made of two brass [E = 105 GPa] plates bonded to an aluminum [E = 63 GPa] bar,…

A: Given data Eb = 105 GPA EAl = 63 GPA M= 1525 Nm = 1525 × 103 N-mm

Question

100%

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Given

Step 1

Step 2

Step 3

Trending now

This is a popular solution!

Step by step

Solved in 4 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66 GPa (2.8x10 and 5.3x 105 psi), respectively. If the volume fraction of fibers is 0.42, determine the moduli of elasticity of fiber and matrix phases. Em- E₁= i GPa GPa
Calculate the modulus of rigidity (shear modulus) of an epoxy resin if the modulus of elasticity (Young's modulus) E = 3.5 GPa and the Poisson's ratio = 0.35. Select one: O a. G = 1.3 GPa Ob. G= 10 GPa O c. G = 0.1 GPa Od. G= 3.15 GPa e. G = 2.6 GPa
A continuous aligned fibre-reinforced composite is produced containing 28% aramid fibres of tensile strength 2.82GPA and the remainder of polycarbonate with tensile strength 60 MPa. What is the longitudinal strength of the composite in MPa? [Enter your answer as a real integer number - do not include the unit]
= 12 mm. The The following figure depicts an aluminum I beam of height h = 0.25 m, width b = 0.2 m, flange thickness ta = 16 mm, and web thickness tw beam is reinforced by two layers of unidirectional composite material of thickness to = 5 mm. The section is subjected to an axial force N₁ = 500 kN. The Young's moduli for the aluminum and unidirectional composite are Ea 73 GPa and Ec 140 GPa, respectively. = (a) Compute the axial stiffness for this structure. (b) Compute the maximum axial stress in both the aluminum and composite layers. CS Scanned with CamScanner 1₁ I h t₂ I b po
Bar A-B-C is made from a fully bonded composite of two materials as shown in the cross section below. Find the Z displacement at point C. A C 1.10 m 20 kN B 1.25 m 50 kN с Y I cross section c-c Uz = 5 mm, material 1 5 mm, material 2 5 mm, material 1 25 mm Material 1 E = 240 (GPa) Material 2 E = 180 (GPa) mm (at C)
Which one of the following reinforcing geometries offers the greatest potential for improving strength and stiffness in the resulting composite material? a) flakes. Ob) particles. O c) discontinuous fibers. O d) continuous fibers
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 45% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite