A continuous aligned fibre-reinforced composite is produced containing 28% aramid fibres of tensile strength 2.82GPA and the remainder of polycarbonate with tensile strength 60 MPa. What is the longitudinal strength of the composite in MPa? [Enter your answer as a real integer number - do not include the unit]

A continuous aligned fibre-reinforced composite is produced containing 28% aramid fibres of tensile strength 2.82GPA and the remainder of polycarbonate with tensile strength 60 MPa. What is the longitudinal strength of the composite in MPa? [Enter your answer as a real integer number - do not include the unit]

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: Determine the (x, y, z) coordinates for the composite volume 130 mm Z 190 mm 275 mm 220 mm 190 mm…

A: A 3D structure is given. To determine the centroid x, y, z of the section. Steps- First, take 2D…

Q: Calculate the expected elastic modulus for a carbon-fiber composite with a continuous uniaxial…

A: Ematrix = 5 GPaEreinforcement = 120 GPaVmatrix = 0.63Vreinforcement = 0.37 Ecomposite =…

Q: A circular FRP composite rod with continuous and aligned fibers has a3 in. diameter. The rod is…

A: Given: Diameter of the FRP composite rod is D=3 in. The span of the rod which is simply supported is…

Q: A cantilever beam of has a length L = 75 mm, of square cross-section of thickness, t = of a CFRP…

Q: It is necessary to fabricate an aligned and discontinuous carbon fibre-epoxy matrix composite having…

Q: Q.6) Determine Ixx and lyy for the composite section shown below. 40 mm 60 mm 30 mm

Q: Calculate the expected elastic modulus for a carbon-fiber composite with a continuous uniaxial…

A: If you have any doubts please comment

Q: A FRP composite includes 40% continuous and aligned Aramid fibers by vol-ume. The moduli of…

A: Modulus of elasticity of polymer(Em)=3.9GPaModulus of elasticity of fibre(Ef)=130GPa

Q: A circular FRP composite rod with continuous and aligned fibers has a 3 in. diameter. The rod is…

A: Diameter of the FRP composite rod is D =3 in.The span of the rod which is simply supported is L=4 ft…

Q: Compute the expected properties of ultimate strength (Suc) of a composite made from S-glass fibers…

A: Tensile strength of S-glass fibers, σf=600 ksi=600×103 psi Tensile strength of Epoxy matrix, σm=18…

Q: for a fiber reinforced composite material, assume Fibre's volume fraction is 0.3. what is the…

Q: What median provides a structural component in a composite? The medium that provides the structural…

A: Load Stress of the composite materials is taken only by the fibres making the composites as…

Q: For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the…

Concept explainers

Glass

Glass is a brittle, supercooled, non-crystalline liquid. It is a clear amorphous solid, meaning, its atomic arrangements lack a definite pattern and long orderly arrangement. Glass can be thought of as a frozen liquid whose molecular flowability is retarded to much sower rate. Studies and science related to glass is an emerging field, with this, a new branch of materials science and engineering has developed known as, "glass engineering". Glass engineering focuses on the design and development of ceramics, glass, and composites. Engineers in this field test and work on new materials, that can be used in place of the traditional glass in terms of strength and durability. A glass engineer also engages himself in developing new equipment and manufacturing techniques, which can lead to the production of glass with enhanced properties.

Question

A continuous aligned fibre-reinforced
composite is produced containing 28%
aramid fibres of tensile strength 2.82GPA and
the remainder of polycarbonate with tensile
strength 60 MPa. What is the longitudinal
strength of the composite in MPa? [Enter
your answer as a real integer number - do
not include the unit]

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

The composite shaft shown consists of a solid brass segment (1) and a solid aluminum segment (2) that are connected at flange B and securely attached to rigid walls at A and C. Brass segment (1) has a diameter of 18 mm, a length of L₁ 235 mm, and a shear modulus of 39 GPa. Aluminum segment (2) has a diameter of 24 mm, a length of L₂ = 165 mm, and a shear modulus of 28 GPa. If a concentrated torque of 270 N-m is applied to flange B, determine (a) the maximum shear stress magnitudes in segments (1) and (2). (b) the rotation angle of flange B relative to support A. N 235 mm (1) B 165 mm Partial Ans: Max shear stress in Member 1 is 55.7 MPa 270 N-m (2)
A continuous and aligned glass fibre-reinforced composite consisting of 40 vol% of glass fibres having a modulus of elasticity of 69 GPa and 60 vol% of a polyester resin that, when hardened, displays a modulus of 3.4 GPa. Compute the elastic modulus of the composite material in the longitudinal direction. Compute the elastic modulus of the composite material perpendicular to the direction of fibre alignment
Bar A-B-C is made from a fully bonded composite of two materials as shown in the cross section below. Find the Z displacement at point C. A C 1.10 m 20 kN B 1.25 m 50 kN с Y I cross section c-c Uz = 5 mm, material 1 5 mm, material 2 5 mm, material 1 25 mm Material 1 E = 240 (GPa) Material 2 E = 180 (GPa) mm (at C)
Which one of the following reinforcing geometries offers the greatest potential for improving strength and stiffness in the resulting composite material? a) flakes. Ob) particles. O c) discontinuous fibers. O d) continuous fibers
A fiber-reinforced polymer composite under isostrain condition consists of 35% fibers and 45% polymer by volume. The moduli of elasticity of the fibers and the polymer are 260 GPa and 3.4 GPa, respectively, and the Poisson’s ratios of the fibers and the polymer are 0.25 and 0.41, respectively. Calculate the following:a. modulus of elasticity of the composite.b. percentage of load carried by the fibersc. Poisson’s ratio of the composite