Calculate the modulus of rigidity (shear modulus) of an epoxy resin if the modulus of elasticity (Young's modulus) E = 3.5 GPa and the Poisson's ratio = 0.35. Select one: a. G = 1.3 GPa O b. G= 10 GPa c. G = 0.1 GPa Od. G = 3.15 GPa Oe. G = 2.6 GPa

Calculate the modulus of rigidity (shear modulus) of an epoxy resin if the modulus of elasticity (Young's modulus) E = 3.5 GPa and the Poisson's ratio = 0.35. Select one: a. G = 1.3 GPa O b. G= 10 GPa c. G = 0.1 GPa Od. G = 3.15 GPa Oe. G = 2.6 GPa

Structural Analysis

6th Edition

ISBN:9781337630931

Author:KASSIMALI, Aslam.

Publisher:KASSIMALI, Aslam.

Chapter2: Loads On Structures

Section: Chapter Questions

Problem 1P

See similar textbooks

Related questions

Q: For the composite section shown in the following figure: (a) Determine the location of the…

Q: The first parts of the stress-strain relationships of the components of a randomly oriented…

A: Given:- The first parts of the stress-strain relationships are given for a randomly oriented…

Q: (a) Figure Q4 shows a composite body used in a certain application. Determine the centroid (x, y) of…

A: A composite crossection is given as follows

Q: A composite bar is made by connecting a steel bar with a length of Lst = 300 mm and an brass bar…

A: Steel Length of steel Bar(L1) = 300 mm Elastic modulus(E1) = 200 GPa Coefficient of Thermal…

Q: For the composite bar indicated, determine the permissible bending moment when the bar is bent about…

Q: below. The specimen dimensions are length=254 mm, width=12. 1.4 mm. Determine the tensile modulus…

A: solution stress = LoadArea area = width×thickness = 12.7×1.4 = 17.78 mm2 to…

Q: 7. A solid aluminum cylinder is placed within an ASTM A501 steel tube as shown. Compute the stresses…

A: Given Data: The diameter of the solid aluminum cylinder is d1=3 in. The diameter of the steel tube…

Q: A bar having the cross section shown has been formed by securely bonding brass and aluminum stock.…

A: Reference : Mechanics, Bending moment of composite bars. Given : Modulus of elasticity and allowable…

Q: 4. The two pieces of wood, 2 in. by 4 in., are glued together along the 40º joint shown in Figure 4.…

Q: Problem 4.4 The composite shaft, consisting of aluminum, copper, and steel sections, is subjected to…

Q: What will be the moment of resistance of the composite section shown in the figure below if the…

A: A composite beam section as shown in the below figure-Permissible stress in wood & steel-To…

Question

Calculate the modulus of rigidity
(shear modulus) of an epoxy resin if
the modulus of elasticity (Young's
modulus) E = 3.5 GPa and the
Poisson's ratio = 0.35.
Select one:
O a. G = 1.3 GPa
Ob. G= 10 GPa
O c. G = 0.1 GPa
Od. G= 3.15 GPa
e. G = 2.6 GPa

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Given data

VIEW

Step 2: Modulus of rigidity

VIEW

Solution

VIEW

Step by step

Solved in 3 steps with 2 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.

Similar questions

Determine the total area of the composite figur e . (mm^2)Determine the x coordinate of the centroid of composite figure. (mm)Determine the y coordinate of the centroid of composite figure. (mm)
IV- It is necessary to design a continuous and aligned glass fiber-reinforced polyester having a tensile strength of at least 1400 MPa in the longitudinal direction. The maximum possible specific gravity is 1.65. Using the following data, determine whether such a composite is possible. Justify. Assume a value of 15 MPa for the stress on the matrix when the fibers fail. Material Glass fiber Polyester Specific gravity 2.5 1.35 Tensile strength (MPa) 3500 50
The first parts of the stress-strain relationships of the components of a randomly oriented composite are shown in Figure P11.25. Estimate the volume percentage of fibers in the composite assuming a fiber efficiency parameter (K) of 0.2. Stress (MPa) 1400 1200 1000 800 600 400 200 I T FIGURE P11.25 0.002 Fibers Strain (m/m) 0.004 Composite Matrix 0.006
A wood beam reinforced by an aluminum channel section is shown in the figure. 150 mm 230 mm 38 mm 6.5 mm -163 mm- The beam has a cross section of dimensions 150 mm x 230 mm, and the channel has a uniform thickness of 6.5 mm. If the allowable stresses in the wood and aluminum are 8 MPa and 50 MPa, respectively, and if their moduli of elasticity are in the ratio 1 to 6, what is the maximum allowable bending moment for the beam? Enter the magnitude in kN · m. (Assume that the component parts of the beam are securely bonded by adhesives or connected by fasteners. Also, be sure to use the transformed-section method in the solution.) (No Response) 14.06 kN· m
A bar having the cross section shown has been formed by securely bonding brass and aluminum stock. Taking h= 9 mm and using the data given below, determine the largest permissible bending moment when the composite bar is bent about a horizontal axis. Brass Aluminum 30 mm Modulus of elasticity Allowable stress h 30 mm h Aluminum 70 GPa 100 MPa The largest permissible bending moment is Brass 105 GPa 160 MPa 1.17 kN-m.
For the composite bar indicated, determine the permissible bending moment when the bar is bent about a vertical axis. Aluminum stress is 100 %3D MPa, Brass stress is 160 MPa, Eb = 105 GPa, Ea = 70 GPa Brass 6 mm Aluminum 30 mm 6 mm -30 30 mm
SITUATION 1. A composite bar is made by attaching a copper rod of length 900 mm and diameter 30 mm and a brass rod of length 600 mm and diameter 45 mm as shown. A load of 20 kN is applied at 20°C. For copper, E = 120 GPa and a = 18 x 10-6/°C. For brass, E = 90 GPa and a = 20 x 10-6/°C. The temperature rises to 50°C. Copper 44.95 MPa 63.29 MPa 72.84 MPa 900 mm 40.70 MPa + What is the stress in the copper rod if the supports are unyielding? Brass - 20 kN 600 mm
The composite bar shown is fixed at the ends and is subjected to the axial load P shown. If the aluminum is stressed to 10 ksi, find the force P and the stress in the steel. 10in. 15in. Aluminum Steel A=1.5 in? E=10x10°psi A=2.0 in? 6 E=30x10°psi 6
What is the maximum diameter of aggregate considering the clear spacing of the reinforcements in mm? 160mm slab Slab=10mm 130mm beam 700mm 17.25cm 500mm 4 Obeam=25mm D =?
How to solve for the centroid of the composite body using the principle of moments and treat each part as a finite element of the whole figure (Show a step by step solution)
A composite sample of carbon reinforced epoxy has dimensions of in 20 in x 20 in x 0.135 in and mass of 3 lb. The carbon fibres have a modulus of elasticity of 80(106) lb/in2 and a density of 0.15 lb/in3. The epoxy matrix has modulus of elasticity of 0.90(106) lb/in2 and a density of 0.05 lb/in3. Assume there are no voids in the sample, calculate the volume fraction of: (i) The carbon fibres (ii) The epoxy matrix in the sample.
A composite beam made of steel and bronze has the cross section shown. The cross-sectional dimensions are b1 = 0.5 in, b2 = 1.5 in., and d = 1.0 in. The elastic modulus of the steel is E1 = 30,000 ksi, and its allowable bending stress is 24 ksi. The elastic modulus of the bronze is E, = 15,000 ksi, and its allowable bending stress is 16 ksi. Calculate the magnitude of the allowable bending moment that can be applied about the z centroidal axis. y Bronze (2) Steel (1) bị b2 Answer: M = i Ib-in. Save for Later Attempts: 0 of 1 used Submit Answer