Calculate the number of Frenkel defects per cubic meter in zinc oxide at 939°C. The energy for defect formation is 2.51 eV, while the density for ZnO is 5.55 g/cm³ at this temperature. The atomic weights of zinc and oxygen are 65.41 g/mol and 16.00 g/mol, respectively. N₁- i 6.5e17 defects/m3

Calculate the number of Frenkel defects per cubic meter in zinc oxide at 939°C. The energy for defect formation is 2.51 eV, while the density for ZnO is 5.55 g/cm³ at this temperature. The atomic weights of zinc and oxygen are 65.41 g/mol and 16.00 g/mol, respectively. N₁- i 6.5e17 defects/m3

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: Calculate the number of vacancies per cubic meter for some metal, M, at 806°C. The energy for…

Q: The activation energy for the diffusion of atomic species A in metal B is 118 kJ/mol. Calculate the…

A: D1=Diffusion Coefficient At 1140=6.1×10-11 m2/sT1=Temperature=1140°C=1413.15 kT2=840°C=1113.15…

Q: Materials with dislocations have lower shear strengths than materials with no dislocations. Is this…

A: Dislocation: It is a linear crystallography defect inside the crystal structure of the material…

Q: Determine the concentration of vacancies (number/m³) needed for an FCC Cu crystal lattice to have a…

A: FCC Cu crystal lattice density =8.10 g/cm3 Lattic Parameter of Cu =3.61×10-10m Atomic Weight of…

Q: Determine the following 1. Determine what substance has a great strength? Calculate and…

A: Given: To find: 1. Determine what substance has a great strength? Calculate and demonstrate. 2.…

Q: A cube of aluminum has a mass of 200 grams and its temperature rises from 15.0 °C to 28.5 °C when…

A: Given details: m=200 gramsCAl=0.921 J/g°CT1=15°CT2=28.5°C

Q: Consider an fcc lattice with cube side length 2.7 Ă. What are the planar densities of the (110) and…

Q: what is the delta H of 40 g of silver dropping from 300 K to 270 K? c = 0.25

A: The mass of silver is m=40 g=40 g×kg1000 g=0.04 kg. The initial temperature of silver is T1=300 K.…

Q: For a hypothetical material, experiments show that a sample containing 1 billion atoms has 40…

A: Given; Number of atoms (N) @600° C is 1 billion (1×109 ) Numbers of vacancies (Nv) @600° C is 40…

Q: In an electrochemical cell, a metal anode lost 0.227 g while a total volume of 0.08149 L of hydrogen…

Q: A pump draws benzene at 25°C from a tank whose level is 2.6 m above the pump inlet. The suction line…

A: Atmospheric pressure=98.5kPa Vapour pressure = 13.3kPa Head loss= 0.8m To find net positive suction…

Q: On the basis of ionic charge and ionic radii given in Table 3.4, predict crystal structures for the…

Q: Out of every 1000 Tera atoms in pure Si, 28 atoms provide a free electron at room temperature. (1)…

Q: The attached photo shows the Young’s modulus of a cubic single crystal as a function of orientation.…

A: Write the vector notation of <110>, [100], [010] and [001]. Write the expression of the angle…

Q: For a hypothetical material, experiments show that a sample containing 1 billion atoms has 40…

A: Given Data T=6000c = T=600+273=873k N=number of atomic sites per cubic meter = 1x109 atoms/m3…

Q: Consider two hypothetical metallic crystal structures A and B. A has an fcc and Ba bcc lattice…

Q: Determine the planar density for FCC nickel in the (111) plane with lattice parameters of ao=3.5187.…

Q: Square lattice. Consider a square lattice in two dimensions with the crystal potential U(x, y)=-4U…

Q: Calculate the number of vacancies per cubic meter for some metal, M, at 850°C. The energy for…

A: We have to find Calculate the number of vacancies per cubic meter

Q: In order to produce a certain semiconductor, a process called doping is performed in which…

Q: What is the Miller index for the plane shown below in a hexagonal close-packed crystal (this…

A: Miller index is a set of numbers that is used to denote or specify the lattice plane and the plane…

Q: Od 10.6x106 O e. 10.60 Clear my choice ion 7 Calcium (Ca) has the Face-Centered Cubic (FCC) crystal…

Q: A polypropylene specimen has a mass of 28 kg and density of 1.65x103 kgm-3 . Determine the…

Q: Q3 (10 points) Consider a silicon semiconductor at T = 200 K. Determine the electron and hole…

A: Approach to solving the question: To solve for the electron and hole concentrations in a silicon…

Q: The activation energy for the diffusion of atomic species A in metal B is 114 kJ/mol. Calculate the…

A: D1=Diffusion Coefficient At 1140=76.7×10-12 m2/sT1=Temperature=1170°C=1443KT2=891°C=1164 KE=The…

Concept explainers

Chemical and Phase Equilibrium

Phase diagrams or equilibrium phase diagrams are the graphical representations that show the phase transformations of the constituting elements with respect to the pressure, temperature, and compositions. The diagrams show the conditions that limit the different phases, namely solid, liquid, and gas. The diagram can also be utilized to verify the relations between the state variables. Most of the phase diagrams are temperature-pressure phase diagrams, with the variable parameter as the composition. Usually other variables such as solubility and pressure parameters are not indicated in the phase diagram. For a one-component system (unary phase diagram), the phase diagram is generally a function of temperature and pressure as the state variables, or temperature and volume. However, for a binary system (two-phase) having two components, the phase diagram is a function of temperature and composition as the state variables only. Coexisting of the different phases of the constituting elements is indicated in the phase diagram. A ternary phase diagram can be characterized by consisting of three phases in equilibrium.

Question

empt in Progress
Calculate the number of Frenkel defects per cubic meter in zinc oxide at 939°C. The energy for defect formation is 2.51 eV, while the
density for ZnO is 5.55 g/cm³ at this temperature. The atomic weights of zinc and oxygen are 65.41 g/mol and 16.00 g/mol,
respectively.
N₁=
6.5e17
defects/m³
M
Qu
Mult
Ques
Multin

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1: Given Data

VIEW

Step 2: Evaluation of the number of Frenkel defects

VIEW

Solution

VIEW

Step by step

Solved in 3 steps with 4 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

i need the answer quickly
Q1/A Prove that the volume of an FCC unit cell, Vc is; Vc = 16R³√2 B) Explain in general terms, why many polymers and some ceramic glasses have an amorphous or semicrystalline structure.
I need help on this question
1. Many substances crystallize in a cubic structure. The unit cell for such crystals is a cube having an edge with a length equal to do. -Face diagonal a. What is the length, in terms of do, of the face diagonal, which runs diagonally across one face of the cube? (Hint: Use the Pythagorean theorem.) b. What is the length, again in terms of do. of the cube diagonal, which runs from one corner, through the center of the cube, to the opposite corner? (Hint: Make a right triangle having a face diagonal and an edge of the cube as its sides, with the hypotenuse equal to the cube diagonal, then use the Pythagorean theorem again.) 2. In an FCC structure, the centers of the atoms are found on the corners of the cubic unit cell and at the center of each face. The unit cell has an edge whose length is the distance from the center of one corner atom to the center of another corner atom on the same edge. The atoms on the diagonal of any face are touching. One of the faces of the unit cell is shown…
A mixture of species of A, B, and C is injected into a liquid chromatographic column with length of 20.0 cm. The obtained separation results are listed as follows: Please calculate the average number of theoretical plates from the data. Please round your result to whole number. The answer would be 2,153 (Need getting the answer)
The activation energy for the diffusion of atomic species A in metal B is 103 kJ/mol. Calculate the diffusion coefficient at 842°C, given that the value of D at 1150°C is 6.5 x 10-12 m²/s. i m²/s
Consider two hypothetical metallic crystal structures A and B. A has an fcc and Ba bcc lattice structure. Both have the same unit cell volume. The Atomic Packing Factor for A is 0.740 and that for B is 0.680. What is the ratio of the fcc to bcc atomic radii? (This question has only one correct answer) O a. 0.92 Ob. 0.44 Ос. 0.63 O d. 0.82 е. 1.21
Sketch the planar cross section for the following planes in the FCC structure (label the edge lengths in terms of a and R) and calculate the planar densities for the three planes (do so in terms of both atoms/nm2 AND the dimensionless quantity): a. (001)b. (011)c. (111)
In copper, what percentage of the volume change which occurs as the specimen is heated from room temperature to its melting point is due to the increased vacancy concentration, assuming that the vacancy concentration is just below the melting point (1083 oC) is 10-4. Given: Assume that the linear thermal expansion coefficient of copper is 16.5×10-6 K-1 over the whole temperature range.
Calculate the shape function of the elements in the figure below.
Copper is a typical face-centered-cubic metal. In its pure state, it has extremely high electrical conductivity. Oxygen in copper causes a major reduction of conductivity. To investigate this issue further, I want to you to tell me whether oxygen atoms substitute for copper atoms, or if they enter interstitial sites.
The spacing of adjacent atoms in a NaCl crystal is 0.282 nm, and the masses of the atoms are 3.82*10-26 kg (Na) and 5.89*10-26 kg (CI). Use this information to calculate the density of NaCl. p= kg/m³