Question 3A rolling operation on a 250 mm wide, 8 mm thick, 1112 cold rolled steel takesplace using hardened steel rolls with a surface finish of 0.03 um. The rolls havea diameter of 350 mm and rotates at 115 rpm. The final thickness of the plateis 6 mm and the entry speed of the plate is 1.8 m/s. Calculate:3.1 The minimum coefficient of friction required, that will make the rolling operationpossible.3.2 The required roll force.3.3 The position of the neutral point, xn3.4 Indicate, using a sketch, the neutral point showing all relevant notation anddimensions.

Since it is not mentioned how many parts in the question are to be solved, the first three subparts…

A rolling operation on a 250 mm wide, 8 mm thick, 1112 cold rolled steel takes place using hardened steel rolls with a surface finish of 0.03 um. The rolls have a diameter of 350 mm and rotates at 115 rpm. The final thickness of the plate is 6 mm and the entry speed of the plate is 1.8 m/s. Calculate: The minimum coefficient of friction required, that will make the rolling operation possible. The required roll force.

A rolling operation on a 250 mm wide, 8 mm thick, 1112 cold rolled steel takes place using hardened steel rolls with a surface finish of 0.03 um. The rolls have a diameter of 350 mm and rotates at 115 rpm. The final thickness of the plate is 6 mm and the entry speed of the plate is 1.8 m/s. Calculate: The minimum coefficient of friction required, that will make the rolling operation possible. The required roll force.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: A piece with a height of 120 mm and a diameter of 75 mm can be increased to 80 mm in height by…

A: Permissible stress is stress which produces due to pressure or forces which does not exceed the…

Q: 6.100 A 0.25-m-wide billet of 5052-O aluminum (K = 210 MPa, n = 0.13) is forged from a thickness of…

A: For aluminium K=210 MPa, n=0.13 The wide of billet is w=0.25 m The initial thickness is ti=30…

Q: A 300-mm-wide strip 25-mm thick is fed through a rolling mill with two powered rolls each of radius…

A: The answer has been attached in the form of images as follows:

Q: Please give me full explanation in 1hour do it fast A 4-in-thick aluminum slab is 10 in wide and 100…

A: Since we only answer up to 3 sub-parts, we’ll answer the first 3. Please resubmit the question and…

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: In a single pass rolling process using 410 mm diameter steel rollers, a strip width 140 mm and…

A: To find: The angle of bite in radians. Given: The diameter is d=410 mm. The width is b=140 mm. The…

Q: Fib the time period, if pure rolling is the condition

A: Given data: Roller connected to spring is released from the inclined plane To determine: Time…

Q: In a rolling operation using rolls of diameter 500 mm, if a 25 mm thick plate cannot be reduced to…

A: Given data: The diameter of roll is D = 500 mm. The thickness of the plate is t = 25 mm. The…

Q: A solid cylindrical slug made of 304 stainless steel is 150 mm in diameter and 100 mm high. It is…

A: Given:Initial diameter of cylinder, do=150 mmInitial height of the cylinder, ho=100 mmDiameter after…

Q: A 300 mm thick slab is being cold rolled using roll of 600 mm diameter. If the coefficient of…

A: Given, Thickness of slab=300mm Diameter of roller,D=600mm Radius of roller, R=300mm Coefficient of…

Q: An annealed 4340 steel strip of 300 mm width and 7 mm thickness is rolled to a thickness of 5 mm.…

Q: Drawing: A round rod of annealed 302 stainless steel (K = 1300 MPa and n = 0.3) is being drawn from…

A: Given:To find:

Q: A copper strip of 200 mm width and 300 mm thickness is to be rolled to a thickness of 295 mm The…

A: Given:Width of the copper strip=200 mmThickness of copper strip, hi=300 mmFinal thickness of copper…

Q: A 300-mm-wide strip 25-mm thick is fed (Bottom roll removed) through a rolling mill with two powered…

A: Given: The width of strip, b = 300 mm The thickness of strip, x = 25 mm The radius of rolls, R = 250…

Q: ti-pass cold rolling operation is to be used to red mill. The following data is provided for the ro…

Q: A blanking operation is to be performed on 2.0 mm thick cold-rolled steel (half hard). The part is…

A: Write the given data. t=2 mmD=45 mmA=0.075

Q: A strip with a cross section 120 mm x 6 mm is being rolled with 20% reduction area, using rolls of…

A: Given Strip = 120 mm X 6 mm Deduction = 20% Diameter = 400 mm Coefficient of friction = 0.1 To find…

Q: A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that…

Q: A low-carbon steel plate is 300 mm wide and 25 mm thick. It is reduced in one pass in a two-high…

A: The width of the steel plate is w=300 mm. The initial thickness of the steel plate is ti=25 mm. The…

Q: A hot rolling operation is being carried out on 250 mm wide and 25mm thick low carbon steel…

A: Calculate the final thickness. hf=1-0.2ho =0.8×25 =20 mm Calculate the strain. Strain ε=lnhohf…

Q: required at the moment of reaching the yield point (ℇ = 0.002) b) Force required when you have a…

Q: - 400 mm wide 25 mm thick strip is fed through a rolling mill with two powered olls each of radius…

Q: In rolling process, calculate the applied torque in (N.m) when w= 600mm, K = 275 MPa, n = 0.10, %3D…

A: Given Data W=600 mm K=275 MPa n=0.1 ho=35 mm hf=29 mm R=373.3 mm

Q: An aluminium strip with a cross section of 200 mm × 8 mm is being rolled with 25% reduction of…

A: Given Data: Aluminium strip cross sectional area A=200 mm×8 mm Diameter d=400 mm Tensile yield…

Q: plate material is 300 MPa. The power required for the rolling operation in kW is closest to

A: Given, In a single pass rolling operation:h1=20mmh2=18mmR=250 mmwidth=100mmσ0=300 MPa We have to…

Q: The minimum possible thickness

A: Given; A thick sheet having 4 mm is rolled with 300 mm diamaterOr, d=300 mm t=4 mmFriction…

Q: A annealed copper strip 300mm wide and 25mm thick is being rolled to a thickness of 10mm in one…

Q: A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a…

Q: Thickness of the sheet produced in a single pass.

A: Given data; Thickness, t=6 mmDiameter,D=200 mmGiven is diameter rolls to reduce thickness without…

Q: Write a Brief Application of Pure Rolling Bodies in The Mechanical Systems?

A: Pure rolling refers to the rolling process in which no slide is seen. Pure rolling is a motion…

Q: I need the answer as soon as possible

A: Given data; hi=300 mmhf=295 mmR=300 mmN=100 rpmζavg=180 mpa

Q: A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a…

Q: A plate that is 260 mm wide and 27 mm thick is to be reduced in a single pass in a two‑high rolling…

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1: Disclaimer

VIEW

Step 2: Introduction

VIEW

Step 3: Calculation part

VIEW

Step 4: Conclusion

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 4 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Make your solutions as detailed solutions, clean, and clear. Draw the Figure.
A cold rolling operation is to be used to reduce a 50 mm thick and 200 mm wide copper plate. The entering velocity of the plate is 15 m/min and the exit velocity is 18 m/min. The coefficient of friction is 0.2 and assuming that the reduction in thickness during this process is the maximum draft permissible. If the plate widens by 5% after rolling, calculate the power required to drive the rolls. Assume average flow stress of the material as 180 MPa.
None
Derive the expression for roll separating force and power in rolling.
Bar stock of initial diameter = 90 mm is drawn with a draft = 15 mm. The draw die has an entrance angle = 18°, and the coefficient of friction at the work‑die interface = 0.08. The metal behaves as a perfectly plastic material with yield stress = 105 MPa. Determine (a) area reduction, (b) draw stress, (c) draw force required for the operation, and (d) power to perform the operation if exit velocity = 1.0 m/min
None
A sheet 300mm wide 25mm thick with two drives, each with a radius of 250mmit is passed through a rolling stand with rollers. Work is thickness in one layer at 50 rpm roll speed 22reduced to mm. The work material has a yield curve determined by K = 275 MPa and n = 0.15.The friction coefficient between the rollers and the work is considered to be 0.12. Successful rolling of frictionDetermine if it is sufficient to allow its operation. If it is sufficient;a) Rolling force,b) Momentc) Calculate the power.
A cold heading operation is performed to produce the head on a steel nail. The strength coefficient for this steel is 600 MPa, and the strain hardening exponent is 0.22. Coefficient of friction at the die‑work interface is 0.14. The wire stock out of which the nail is made is 5.00 mm in diameter. The head is to have a diameter of 9.5 mm and a thickness of 1.6 mm. The final length of the nail is 120 mm. (a) What length of stock must project out of the die in order to provide sufficient volume of material for this upsetting operation? (b) Compute the maximum force that the punch must apply to form the head in this open‑die operation.
4)
Briefly explain various methods available for breakdown passes in rolling. Explain their applications.
the work metal has a flow curve defined by K=300MPa and n=0.2, and the coefficient of friction between the rolls and the work is assumed to be 0.1. a 250mm wide strip 2.0cm thick is fed through a rolling mill with two powered rolls each of radius=300mm. the work thickness is to be reduced to 18mm in one pass at a roll speed of 50rev/min. what will be the power for this operation?
Calculate (1) die pressure distribution and (2) forging force for plane strain forging (open die forging). Assume yield strength of the material is Y, and yielding criterion is von Mises. ho 2Lo h Forged to 2L xdx L 'x+value Note: Assume Zo Constant Plane strain Die pressure distribution h L L Die pressure distribution h MATERIAL L dx -(-1) Friction Hill Y L When 0; =Y P=Y' = Calculate forging force X L dF elemental volume Average pressure