ti-pass cold rolling operation is to be used to red mill. The following data is provided for the ro cm, h=2.5 cm, R = 350 mm, μ = 0.16. If the draft er of passes required is.

Q: An annealed copper strip 9 in wide having. K=80,000 psi, N=0.60, and a height of 1 in _was flat…

A:

Q: c) A flat rolling operation is being carried out where the roll radius is 200 mm and the roll…

A: A rolling force is applied by rollers to the workpiece so as to reduce its thickness Maximum…

Q: A 3in long and 1in diameter billet is extruded in a direct extrusion operation with an rx = 4.0. The…

A: Write the extrusion ratio.   rx=4   Write the length and diameter of the billet.   L=3 inD=1 in…

Q: Please give me full explanation in 1hour do it fast A 4-in-thick aluminum slab is 10 in wide and 100…

A: Since we only answer up to 3 sub-parts, we’ll answer the first 3. Please resubmit the question and…

Q: A steel rotor of a gas turbine of 400mm outside diameter, 150mm inside diameter and 25mm thick is…

A: INTRODUCTION: Shrinkage can also result in problems in cast goods, including failure and leaking.…

Q: A hot rolling operation is being carried out on 250 mm wide and 25mm thick low carbon steel…

A: Calculate the final thickness. hf=1-0.2ho   =0.8×25   =20 mm Calculate the strain. Strain ε=lnhohf…

Q: required at the moment of reaching the yield point (ℇ = 0.002) b) Force required when you have a…

A:

Q: In a 'tandem' rolling process, a wide metal strip passes continuously between four sets of rolls,…

A:

Q: A round disk of 200-mm diameter is blanked from a strip of 3.0-mm, half-hard cold-rolled steel whose…

A: Given data: d=200 mmt=3 mmτ=300 MPaAc=0.075 Need to determine the punch, die diameters and blanking…

Q: A flat-rolling operation of 250 mm wide alloy stee Calculate roll torque

A: GIVEN: **Width (Wt)=250mm **Diameter of rollers (D)=600mm **Height before rolling (ho)=30mm**Height…

Q: te the maximum bending force requires for a 3 mm thick and 300 mm long Ti-6Al-4V titanium alloy…

A: Given data as per question Thickness, t=3 mm=3×10-3 m Length, L=300 mm=0.3 m And Sy=925 MPa, S_UT =…

Q: Less of 3-0 mm is to be reduced n and wall thickness 2-0 mm. D = 0-1 and draft = 3.1. Compare t…

A:

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.