A plate that is 250 mm wide and 25 mm thick is to be reduced in a single pass in a two-high rolling mill to a thickness of 20 mm. The roll has a radius = 500 mm, and its speed = 30 m/min. The work material has a strength coefficient = 240 MPa and a strain hardening exponent = 0.2. Determine (a)roll force, (b) roll torque, and (c) power required to accomplish this .operation 1365 N & 529865 N-m & 452 W O 500250 N & 12005 N-m & 2456 W O 71254632 N & 135674 N-m & 12053 W O 1851829 N & 46296 N-m & 92,591 W O

A plate that is 250 mm wide and 25 mm thick is to be reduced in a single pass in a two-high rolling mill to a thickness of 20 mm. The roll has a radius = 500 mm, and its speed = 30 m/min. The work material has a strength coefficient = 240 MPa and a strain hardening exponent = 0.2. Determine (a)roll force, (b) roll torque, and (c) power required to accomplish this .operation 1365 N & 529865 N-m & 452 W O 500250 N & 12005 N-m & 2456 W O 71254632 N & 135674 N-m & 12053 W O 1851829 N & 46296 N-m & 92,591 W O

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: 1) A upset forging operation is performed in an open die. The initial size of the workpart is: Do =…

A: Given, Initial size, Do=63 mmho=100 mm The final part diameter, D=70 mm Strength coefficient, K=600…

Q: c) A flat rolling operation is being carried out where the roll radius is 200 mm and the roll…

A: A rolling force is applied by rollers to the workpiece so as to reduce its thickness Maximum…

Q: coefficient of friction between the roll and the plate i

A: Given; In a rolling operation using rolls of;Diameter,D=400 mmThickness, t=35mmFor the given…

Q: If coefficient of friction µ in a rolling process is 0.5 and radius of roller is 1,000 mm, what is…

A: Given, Coefficient of friction = μ = 0.5 Radius of the roller = R = 1000 mm Maximum possible…

Q: A 3in long and 1in diameter billet is extruded in a direct extrusion operation with an rx = 4.0. The…

A: Write the extrusion ratio. rx=4 Write the length and diameter of the billet. L=3 inD=1 in…

Q: Please give me full explanation in 1hour do it fast A 4-in-thick aluminum slab is 10 in wide and 100…

A: Since we only answer up to 3 sub-parts, we’ll answer the first 3. Please resubmit the question and…

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: I need only part d) plz answer in 30min A 4-in-thick aluminum slab is 10 in wide and 100 in long. It…

A: You are asking for only d part so iam solving only that part

Q: A cylindrical part with 25 mm in diameter and 15 mm height is subjected to an open die forging…

A: Given data: Initial cylindrical diameter D=25 mm =0.025 m Initial height of cylinder hi=0.015 m Flow…

Q: A plate of 270 mm wide and 25 mm thick from carbon steel. A two-high rolling mill is used to reduce…

Q: A copper strip of 200 mm width and 300 mm thickness is to be rolled to a thickness of 295 mm The…

A: Given:Width of the copper strip=200 mmThickness of copper strip, hi=300 mmFinal thickness of copper…

Q: ti-pass cold rolling operation is to be used to red mill. The following data is provided for the ro…

Q: A cylindrical working part is subjected to a forging landfall operation. The blank is 3.0 in. high…

A: volume of workpiece=π4×22×3=9.4247 in3

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: single pass rolling process is used with 410 mm diameter steel rollers and a strip of width 140 mm…

A: Given:d=410 mmw=140 mmt=8 mm

Q: A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that…

Q: • A cylindrical billet that is 100 mm long and 40 mm in diameter is reduced by indirect (backward)…

Q: A hot rolling operation is being carried out on 250 mm wide and 25mm thick low carbon steel…

A: Calculate the final thickness. hf=1-0.2ho =0.8×25 =20 mm Calculate the strain. Strain ε=lnhohf…

Q: required at the moment of reaching the yield point (ℇ = 0.002) b) Force required when you have a…

Q: In rolling process, calculate the applied torque in (N.m) when w= 600mm, K = 275 MPa, n = 0.10, %3D…

A: Given Data W=600 mm K=275 MPa n=0.1 ho=35 mm hf=29 mm R=373.3 mm

Q: process, a 150 mmx15 nd rotational speed is nis reduction is the m=

Q: plate material is 300 MPa. The power required for the rolling operation in kW is closest to

A: Given, In a single pass rolling operation:h1=20mmh2=18mmR=250 mmwidth=100mmσ0=300 MPa We have to…

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

100%

A plate that is 250 mm wide and
25 mm thick is to be reduced in a
single pass in a two-high rolling
mill to a thickness of 20 mm. The
roll has a radius = 500 mm, and its
speed = 30 m/min. The work
material has a strength coefficient
= 240 MPa and a strain hardening
exponent = 0.2. Determine (a)roll
force, (b) roll torque, and (c)
power required to accomplish this
.operation
1365 N & 529865 N-m & 452 W O
500250 N & 12005 N-m & 2456 W O
71254632 N & 135674 N-m & 12053 W O
1851829 N & 46296 N-m & 92,591 W O

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

Step 2

Step 3

Step 4

Step 5

Step 6

Trending now

This is a popular solution!

Step by step

Solved in 6 steps with 6 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Solve it
A wire is drawn through a draw die with an entry angle = 15o. The starting diameter is 0.100 in. And the final diameter = 0.080 in. The coefficient of friction at the work-given interface = 0.07. The metal has a coefficient of resistance K = 30,000 psi and a strain hardening exponent of n = 0.20. Determine the stretching force and the stretching force in this operation.
A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. 5.1 Calculate the minimum coefficient of friction required, that will make the rolling operation possible. 5.2 Calculate the exit velocity of the plate. 5.3 Calculate the forward slip. 5.4 If the final width of the sheet is 200 mm, calculate the required roll force. 5.5 Explain what is roll flattening, its effects and how it can be reduced.
In a rolling operation using rolls of diameter 500 mm, if a 25 mm thick plate cannot be reduced to less than 20 mm in one Pass, the coefficient of friction between the roll and the plate is
A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. 5.1 Calculate the minimum coefficient of friction required, that will make the rolling operation possible. 5.2 Calculate the exit velocity of the plate. 5.3 Calculate the forward slip. 5.4 If the final width of the sheet is 200 mm, calculate the required roll force. 5.5 Explain what is roll flattening, its effects and how it can be reduced.
A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a rolling operation. As the thickness is reduced, the plate widens by 3%. The entrance speed of the plate is 13 m/min and the roll radius is 310 mm with a rotational speed of 30 rpm. To do 5.1 If the final width of the sheet is 200 mm, calculate the required roll force. 5.2. Explain what is roll flattening, its effects and how it can be reduced.
None
None
During a direct extrusion process for a billet with 5 in long and diameter 2.5 in to 1.6 in. For the work metal, strength coefficient is 75000 Ib/in, and strain hardening exponent is 0.4, also the die angle of extrusion is 90. In Johnson extrusion strain equation a = 0.8, and b= 1.5. Determine: (a) extrusion ratio (b) true strain (c) extrusion strain, and (d) ram pressure at length 5, 4.2, 2.3,1.5,and 0 in.
A upset forging operation is performed in an open die. The initial size of the workpart is: Do = 63 mm, and ho = 100 mm. The part is upset to a diameter = 70 mm. The work metal has a flow curve with strength coefficient = 600 MPa and strain hardening exponent= 0.22. Coefficient of friction at the die-work interface = 0.40. Determine (a) final height of the part, and (b) maximum force in the operation.
None
A sheet 300mm wide 25mm thick with two drives, each with a radius of 250mmit is passed through a rolling stand with rollers. Work is thickness in one layer at 50 rpm roll speed 22reduced to mm. The work material has a yield curve determined by K = 275 MPa and n = 0.15.The friction coefficient between the rollers and the work is considered to be 0.12. Successful rolling of frictionDetermine if it is sufficient to allow its operation. If it is sufficient;a) Rolling force,b) Momentc) Calculate the power.