11-42 Cooling curves are obtained for a series of Cu-Ag alloys (Figure 11-33). Use this data to produce the Cu-Ag phase diagram. The maximum solubility of Ag in Cu is 7.9%, and the maximum solubility of Cu. in Ag is 8.8% The solubilities at room temperature are near zero. 1200 S0% Ag 71,9% Ag 1100 1000 100% Ag 900 J00% Cu 90% Ag 800 84 A 20% Ag 700 Time Figure 11-33 Cooling curves for a series of CurAg alloys (For Problem 11-42). Temperature (C)

11-42 Cooling curves are obtained for a series of Cu-Ag alloys (Figure 11-33). Use this data to produce the Cu-Ag phase diagram. The maximum solubility of Ag in Cu is 7.9%, and the maximum solubility of Cu. in Ag is 8.8% The solubilities at room temperature are near zero. 1200 S0% Ag 71,9% Ag 1100 1000 100% Ag 900 J00% Cu 90% Ag 800 84 A 20% Ag 700 Time Figure 11-33 Cooling curves for a series of CurAg alloys (For Problem 11-42). Temperature (C)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

rams A copper-nickel alloy of composition 75 wt% Ni-25 wt% Cu is slowly heated from a temperature of 1300°C (1573). (a) At what temperature does the first liquid phase form? (b) What is the composition of this liquid phase? T(°C) 1600 (c) At what temperature does complete melting of the alloy occur? (d) What is the composition of the last solid remaining prior to complete melting? 1500 1400 1300 1200 1100 1000 17 / 17 0 L (liquid) 20 liquidus + a solidus 100% 40 α (FCC solid solution) 60 80 100 wt% Ni 17
3) You see Al-Cu phase diagram below and two microstructures (A and B) having the same nominal composition of 3 percent Cu. In these microstructures, matrix is a and spheres refer to CuAl₂ particles. In A and B, the size of big particles are the same. a) For the same volume constant, if we heat treat the both microstructures at T₁ for a long time, is there any changes in both microstructures? If so, what is that? And is the changes the same for both A and B? Is the rate of changes the same for A and B? Draw the final microstructures of A and B if any changes occur you think so. Temperature a AI 2 I 4 a +CuAl2 1 6 Copper,% CuAl2 α
In Figure 1 (phase diagram), an alloy composition of 95 wt% Mg and 5 wt% Al is cooled from 700 C to 475 C. An analysis of the resulting ε solid-phase composition reveals that it has a higher Mg content than is anticipated by the phase diagram.a) Explain why this might be the case and how your reasoning results in the higher-than-expected Mg content.b) Provide a sketch showing the likely distribution of Mg content within the volume of ε solid-phase.
For an alloy containing 20 wt % Ag, refer to the Cu-Ag phase diagram given in the Figure: What is the melting point of Cu in °C? What are the relative amounts(in %) of the existing phases at 900°C? Define the Eutectic point in terms of °C and the composition % of Ag.
Figure 2 refers to the phase diagram for silver and tin. Label the regions (1) to (5) Temperature, 0/°C 1000 800 600 400 200 0 Liquid 2 Ag,Sn 60 a 20 40 80 Mass percentage Ag/% 100 Question 6: What will be observed when liquids of composition of 40% Ag are cooled to 200 K? When will it begin to precipitate? When will it become solid?
An alloy consisting of completely soluble cadmium (Cd) and zinc (Zn) in the liquid state, but neither of them dissolves in each other in the solid state. the table shown below shows the solidification temperatures for various alloys of cadmium and zinc. 1. Draw the equilibrium diagram according to the information given and data in the table and indicating all important temperature and phases. 2. Find the percentage of each phases and percentage of constituents of the alloy that contain 60 % Zn and at a temperature 300 °C. 3. Find the melting point for the following alloys 20 % Cd, 80% Cd 4. Draw the internal structure, noting the phases of the following alloys A) 30 % Cd at 290 °C b) 60 % Cd at room temperature. % of Zinc in alloy Start of solidification ("C) End of solidification ("C) 0 10 14 20 30 40 50 60 321 290 266 275 293 310 328 345 70 80 90 100 362 390 401 419 266 266 266 266 266 266 266 266 266 266 266 266
Is it possible to have a copper-nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and also an a phase of composition 37 wt% Ni-63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Temperature (°C) 1600 1500 1400 1300 1200 1100 1000 0 1085°C (Cu) 20 Liquid Liquidus line L B 40 a+L a A 60 Composition (wt% Ni) (a) 1455°C Solidus line 80 2800 2600 2400 2200 2000 100 (Ni) Temperature (°F) Temperature (°C) 1300 1200 20 Liquid Tie line. a + Liquid a 1 KR I 1 1 B ↑ Co a + Liquid -S 30 CL Composition (wt% Ni) (b) 40 1 Ca a 50
Consider the binary alloy phase diagram shown schematically below. The left-hand side denotes phase a, and the right-hand side the phase ß. The intermediate region is a coexistence regime with both a and ß phases. The three points 1, 2 and 3 in the coexistence region are at 22.8 wt% A, 28.2 wt% A, and 33.7 wt % A respectively. If the points on the phase boundaries L and R are at 20 wt% A and 39 wt % A, respectively, what is the fraction of a phase at 1, 2 and 3? (This question has only one correct answer) T(°C) A-B binary alloy 1400 Coexistence region 3 1 2 1100 B 20 % 40 % Weight % A
Q.4) For 30 wt% Sn - 70 wr% Pb alloy at 125 °C, (a) what phases are present? (b) What are the compositions of the phases? (c) Calculate the relative mass fraction of each phase present. Composition (at% Br 100 80 60 40 20 A 3270 Temperature (C) 300 200 100 0 0. (Pb) Solvus Solidu a+L B 18.3 20 liquidus Liquid 183 C 61.9 40 60 Composition (wt% Sn) 80 L 232 C G 97.8 1 600 500 P 400 (3) angesadway 300 200 H 100 100 (Sn)
Composition lat% N 40 60 100 1600 2800 1500 1453 C 2600 Liquid 1400 Solidus line Liquidua line 2400 1300 1200 2200 1100 1085 C 2000 1000 20 40 100 Composition (wt N (NO What is the amount for each phase in 1kg of a 50% Ni-50% Cu alloy at temperatures of 1400, 1300, or 1200 degrees C for point A and point B? Temperature ('C) Temperature ("F)
The isothermal transformation diagram for and iron- carbon alloy of eutectoid composition is given in figure. Specify the nature of the final microstructure (in terms of microconstituents present and approximate percentages of each) of a small specimen that has been subjected to the following time-temperature treatments. In each case, assume that the specimen begins at 760°C. Show your work on the diagram. a. Cool rapidly to 300°C, hold for 5 s. b. Cool rapidly to 600°C hold for 100 s, then quench to room temperature. C. Cool rapidly to 500°C, hold for 7 s, and then quench to room temperature. Temperature (°C) 800 700 600 500 400 300 200 100 0 -1 10 6 A A A M(start) M(50%) M(90%) 1 10 M-A Eutectoid temperature P 10² Time (s) B 50% 10³ 104 105
A 10 30 70 1) For an A-B alloy of composition 25 wt% B (i) Draw the microstructure at T (just above the eutectoid temperature) and calculate the fraction of each phase in the microstructure. (ii) Draw the microstructure at T (just below the eutectoid temperature) and determine the amount of each phase, i.e., fraction of proeutectoid alpha, eutectoid alpha and eutectoid beta. 2) Provide a brief summary of phase transformations which are often observed in the iron-carbon alloy system due to various heat treatment procedures carried out to tune the microstructure. Compare mechanical strength and ductility of the materials/microstructures that form as a result of such heat treatment processes.