(a) Interpretation: Percent shrinkage during solidification of iron casting needs to be determined. Concept Introduction: Solidification is the process of forming a crystal structure form the molten metal. Shrinkage is the defect in cast product occurred during solidification Change in volume takes place due to Shrinkage The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as V Shrinkage = 4 3 π r 3 Where, r =radius of material

Question

Want to see the full answer?

Answer 1

Question

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

A flat-plate solar collector is used to heat water by having water flow through tubes attached at the back of the thin solar absorber plate. The absorber plate has emmisssivity and an absorptivity of 0.9. The top surface where x=0 temp of the absorber is T0=35 degrees C, and solar radiation is incident on the basorber at 500 W/m^2 with a surrounding temp of 0 degrees C. The convection heat transfer coefficient at the absorber surface is 5 W/m^2 K, while the ambient temp is 25 degrees C. Show that the variation of the temp in the basorber plate can be expressed as T(x)=-(q0/k)x+T0, and determine net heat flux, q, absorbed by solar collector.

Using properties of a saturated water, explain how you would determine the mole fraction of water vapor at the surface of a lake when the temp of the lake surface and the atmospheric pressure are specified.

Consider a glass of water in a room at 15 degrees C and 97 kPa. If the relative humidity in the room is 100 percent and the water and the air are in thermal and phase equilibrium, determine the mole fraction of the water vapor in the air and the mole fraction of air in the water.

Answer 2

Question

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 3

Question

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 4

Question

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 5

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Answer 6

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Answer 7

Chapter 9, Problem 9.78P

Interpretation Introduction

(a)

Interpretation:

Percent shrinkage during solidification of iron casting needs to be determined.

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Answer 8

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Answer 9

Interpretation Introduction

(b)

Interpretation:

Number of shrinkage pores in casting can be calculated as follows:

Concept Introduction:

Solidification is the process of forming a crystal structure form the molten metal.

Shrinkage is the defect in cast product occurred during solidification

Change in volume takes place due to Shrinkage

The material shrinks up to 7% during solidification volume of shrinkage material can be calculated as

VShrinkage=43πr3

Where,

r =radius of material

Answer 10

Expert Solution & Answer

Answer 11

Expert Solution & Answer

Answer 12

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 13

Ch. 9 - Prob. 9.1P Ch. 9 - Prob. 9.2P Ch. 9 - Prob. 9.3P Ch. 9 - Prob. 9.4P Ch. 9 - Prob. 9.5P Ch. 9 - Prob. 9.6P Ch. 9 - Prob. 9.7P Ch. 9 - Prob. 9.8P Ch. 9 - Prob. 9.9P Ch. 9 - Prob. 9.10P

Solution Summary: The author explains that the percentage of shrinkage during solidification of iron casting needs to be determined.

Want to see the full answer?

Chapter 9 Solutions