The reason fortitanium to be used as a material which is used in bio-medical implant even if it is most anodic material needs to be explained. Concept Introduction: Titanium is a chemical element having atomic number 22. Titanium is designated by the symbol Ti.Titanium is metal which is anodic in nature and which can be treated as the material used for the biomedical implants. Titanium was discovered by William Gregor in 1791 in Cornwall, Great Britain. The element has a number of mineral deposit and ilmenite. These are found in the Earth's Crust and lithosphere. Titanium is alloyed with different material such as aluminum, vanadium to produce lightweight alloys which then is used for jet engines and missiles. Titanium is corrosion resistance and is the highest element in strength to density ratio.

Question

Want to see the full answer?

Answer 1

Question

Chapter 18, Problem 18.22P

Interpretation Introduction

Interpretation:

The reason fortitanium to be used as a material which is used in bio-medical implant even if it is most anodic material needs to be explained.

Concept Introduction:

Titanium is a chemical element having atomic number 22. Titanium is designated by the symbol Ti.Titanium is metal which is anodic in nature and which can be treated as the material used for the biomedical implants. Titanium was discovered by William Gregor in 1791 in Cornwall, Great Britain. The element has a number of mineral deposit and ilmenite. These are found in the Earth's Crust and lithosphere. Titanium is alloyed with different material such as aluminum, vanadium to produce lightweight alloys which then is used for jet engines and missiles. Titanium is corrosion resistance and is the highest element in strength to density ratio.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

Steam flows steadily through a turbine at a rate of 45,000 lbm/h, entering at 1000 psia and 900°F and leaving at 5 psia as saturated vapor. If the power generated by the turbine is 4.1 MW, determine the rate of heat loss from the steam. The enthalpies are h1 = 1448.6 Btu/lbm and h2 = 1130.7 Btu/lbm. The rate of heat loss from the steam is Btu/s.

a. A silicon sample maintained at room temperature is uniformly doped with ND=10¹6/cm³ donors. Calculate the resistivity of the sample. b. The silicon sample of part (a) is "compensated" by adding NA=1016/cm³ acceptors. Calculate the resistivity of the compensated sample. c. Compute the resistivity of intrinsic silicon at room temperature. d. A 500 resistor is to be made from a bar-shaped piece of n-type Si. The bar has a cross sectional area of 102 cm² and a current-carrying length of 1 cm. Determine the doping required. μn or μp (cm²/V-sec) 1000 Electrons Holes NA or ND (cm³) 1x1014 Мет Mp (cm2V-sec) 1358 461 2 1357 460 100 5 1352 459 1 x 1015 1345 458 2 1332 455 5 1298 448 1 x 1016.... 1248 437 2 1165 419 5 986 378 1 x 1017 801 331 10 1014 1015 1016 NA or ND (cm-³) 1017 1018 Silicon T = 300 K

The A/D converter wit the specifications listed below is planned to be used in an environment in which the A/D converter temperature may change by ± 10 °C. Estimate the contributions of conversion and quantization errors to the uncertainty in the digital representation of an analog voltage by the converter. FSO N Linearity error Temperature drift error Analog to Digital (A/D) Converter 0-10 V 12 bits ± 3 bits 1 bit/5 °C