Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Question

Want to see the full answer?

Answer 1

Question

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Students have asked these similar questions

Modern life has been impacted immensely by computers. Computers have penetrated every aspect of oursociety, either for better or for worse. From supermarket scanners calculating our shopping transactionswhile keeping store inventory; robots that handle highly specialized tasks or even simple human tasks,computers do much more than just computing. But where did all this technology come from and whereis it heading? Does the future look promising or should we worry about computers taking over theworld? Or are they just a necessary evil? Provide three references with your answer.

Two different options A and B with brake pads for disc brakes are connected to the rope drum. The diameter of the rope drum is 150 mm. What distance must the pads B be at from the center of rotation to cover the same distance as A?A B- Width 50 mm - Width 60 mm- Evidence center 120mm - Construction power 900 N from rotation center.- Maintains a weight of 200 kgwhen the installation force is 1.4kN (μ is missing from the data)M=μF(Ry-Ri)Right answer R=187 mm

Solve in detail please

Answer 2

Question

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 3

Question

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 4

Question

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Expert Solution & Answer

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 5

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Answer 6

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Answer 7

Chapter 11.17, Problem 21QP

(a)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Answer 8

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Answer 9

(b)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Answer 10

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Answer 11

(c)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Answer 12

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Answer 13

(d)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Answer 14

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Answer 15

(e)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Answer 16

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Answer 17

(f)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Answer 18

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Answer 19

(g)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Answer 20

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Answer 21

(h)

To determine

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Answer 22

Expert Solution & Answer

Answer 23

Expert Solution & Answer

Answer 24

Want to see the full answer?

Check out a sample textbook solution

See solution

Answer 25

Ch. 11.17 - Prob. 1QP Ch. 11.17 - Prob. 2QP Ch. 11.17 - Prob. 3QP Ch. 11.17 - Prob. 4QP Ch. 11.17 - Prob. 5QP Ch. 11.17 - Prob. 6QP Ch. 11.17 - Prob. 7QP Ch. 11.17 - Prob. 8QP Ch. 11.17 - Prob. 9QP Ch. 11.17 - Prob. 10QP

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure, Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.

Want to see the full answer?

Chapter 11 Solutions

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 775°C (1430°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 25 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 350°C (660°F), hold for 300 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 675°C (1250°F), hold for 7 s, then quench to room temperature.

Using the isothermal transformation diagram for a 1.13wt%C steel alloy, specify the nature of the final microstructure,

Rapidly cool to 600°C (1110°F), hold at this temperature for 7 s, rapidly cool to 450°C (840°F), hold at this temperature for 4 s, then quench to room temperature.