Textbook Question
Chapter 11, Problem 44QTP
Estimate the clamping force for a die-casting machine in which the casting is rectangular with projected dimensions of 100 mm × 150 mm (4 in. × 6 in.). Would your answer depend on whether it is a hot-chamber or cold-chamber process? Explain.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Describe the die casting process in detail. Use neat sketches for clarity. Differentiate clearly between hot-chamber die casting and cold-chamber die casting processes.
What is the difference between true centrifugal and semi-centrifugal casting? Describe the centrifugal casting process in detail. Use neat sketches to elaborate your description.
A mould having dimensions 100 mm x 90 mm x 20 mm is filled with molten metal through a gate with height h and CS area A, the mould filling time is t1. The height is now quadrupled and the crosssectional area is halved. The corresponding filling time is t2 .
What is the ratio t2/t1 ?
For sand-casting a steel rectangular plate with dimensions 80mm×120mm×20mm, a cylindrical
riser has to be designed. The height of the riser is equal to its diameter. The total solidification
time for the casting is 2 minutes. In Chvorinov‟s law for the estimation of the total solidification
time, exponent is to be taken as 2. For a solidification time of 3 minutes in the riser, the diameter
(in mm) of the riser is ____
Chapter 11 Solutions
EBK MANUFACTURING ENGINEERING & TECHNOL
Ch. 11 - Describe the differences between expendable and...Ch. 11 - Name the important factors in selecting sand for...Ch. 11 - What are the major types of sand molds? What are...Ch. 11 - List important considerations when selecting...Ch. 11 - What is the function of a core?Ch. 11 - What is the difference between sand-mold and...Ch. 11 - What are composite molds? Why are they used?Ch. 11 - Describe the features of plaster-mold casting.Ch. 11 - Name the type of materials typically used for...Ch. 11 - What are the advantages of pressure casting over...
Ch. 11 - List the advantages and limitations of die...Ch. 11 - What is the purpose of a riser? What is a blind...Ch. 11 - Explain the purpose of a vent and a runner in a...Ch. 11 - How are shell molds produced?Ch. 11 - What keeps the mold together in vacuum casting?Ch. 11 - What is squeeze casting? What are its advantages?Ch. 11 - What are the advantages of the lost-foam casting...Ch. 11 - Prob. 18RQCh. 11 - What are the reasons for the large variety of...Ch. 11 - Why are risers not as useful in die casting as...Ch. 11 - Describe the drawbacks to having a riser that is...Ch. 11 - Why can blind risers be smaller than open-top...Ch. 11 - Why does die casting produce the smallest cast...Ch. 11 - Why is the investment-casting process capable of...Ch. 11 - What differences, if any, would you expect in the...Ch. 11 - Recently, cores for sand casting have been...Ch. 11 - Would you recommend preheating the molds used in...Ch. 11 - Give reasons for, and examples of, using die...Ch. 11 - Referring to Fig. 11.3, do you think it is...Ch. 11 - Explain why squeeze casting produces parts with...Ch. 11 - How are the individual wax patterns attached on a...Ch. 11 - Describe the measures that you would take to...Ch. 11 - You have seen that, even though die casting...Ch. 11 - How are hollow parts with various cavities made by...Ch. 11 - It was stated that the strength-to-weight ratio of...Ch. 11 - How are risers and sprues placed in sand molds?...Ch. 11 - In shell-mold casting, the curing process is...Ch. 11 - Why does the die-casting machine shown in Fig....Ch. 11 - Prob. 39QLPCh. 11 - What are the benefits to heating the mold in...Ch. 11 - The slushy state of alloys refers to that state...Ch. 11 - Can a chaplet also act as a chill? Explain.Ch. 11 - Rank the casting processes described in this...Ch. 11 - Estimate the clamping force for a die-casting...Ch. 11 - In sand casting, it is important that the...Ch. 11 - If an acceleration of 100 g is necessary to...Ch. 11 - A jeweler wishes to produce 24 gold rings in one...Ch. 11 - Describe the procedures that would be involved in...Ch. 11 - The optimum shape of a riser is spherical to...Ch. 11 - Sketch and describe a casting line consisting of...Ch. 11 - Outline the casting processes that would be most...Ch. 11 - Make a list of the mold and die materials used in...Ch. 11 - Write a brief paper on the permeability of molds...Ch. 11 - Light metals commonly are cast in vulcanized...Ch. 11 - It sometimes is desirable to cool metals more...Ch. 11 - The part shown in Fig. P11.59 is a hemispherical...Ch. 11 - Porosity that has developed in the boss of a...Ch. 11 - In Fig. II.1b the gemstones have been cast in...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- EX.3//A cylindrical riser must be designed for a sand-casting mold. The casting itself is a steel rectangular plate with dimensions 7.5 cm x 12.5 cm x 2.0 cm. Previous observations have indicated that the total solidification time (TTs) for this casting =1.6 min. The cylinder for the riser will have a diameter-to-height ratio=1.0. Determine the dimensions of the riser so that its TTS = 2.0 min.arrow_forwardI am in a hurry, I need the answer as soon as possible, please help.arrow_forwardFor a sand casting a steel rectangular plate with dimensions 80mm x 120mm x 20mm. Calculate shrinkage and draft allowance. And draw the designed pattern. Assume shrinkage of material as 0.1% for 12 inch, pattern material is wood and assume suitable draft anglesarrow_forward
- A riser in the shape of a sphere is to be designed for a sand casting mould at Simon Castings. The casting is a rectangular plate, with length = 400 mm, width = 250 mm, and thickness = 15 mm. If the total solidification time of the casting itself is known to be 7 min, determine the diameter of the riser so that it will take 30% longer for the riser to solidify.arrow_forwardTrue centrifugal casting is performed horizontally to make large diameter copper tube sections. The tubes have a length = 2.0 m, outside diameter = 0.4 m, and wall thickness = 30 mm. (a) If the rotational speed of the pipe = 600 rev/min, determine the G-factor on the molten metal. (b) Is the rotational speed sufficient to avoid "rain?" (c) What volume of molten metal must be poured into the mould to make the casting if solidification shrinkage and contraction after solidification are considered? Solidification shrinkage for copper = 3.5%, and solid thermal contraction = 6.5%.arrow_forwardYou were required to make 1000 simple small parts in aluminum. Would using a permanent mold be less expensive per part then preparing 1000 sand molds explain?arrow_forward
- 2. In the casting of steel under certain mould conditions, the mould constant in Chvorinov's rule is known to be 4.0 min/cm?, based on previous experience. The casting is a flat plate whose length is 25 cm, width is 8 cm, and thickness is 2.5 cm. Exponent n is taken to have a value of 2. Determine how long it will take for the casting to solidify.arrow_forwardcompute the diameter of the sphere (mm) that will freeze in the same time in same casting process with a 62.5mm x 150mm x 225mm plate. Assume that constant mold for this casting is 55 mm^2/sarrow_forwardCalculate the size of a cylindrical riser (Height and diameter equal ) necessary to feed slab casting 45 * 45 * 25 cm with a side riser , casting poured horizontally in to the mould.Use caine's equation and take constants in caine equation as a= 0.18; b = 0.05 and c= 1.0.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Casting Metal: the Basics; Author: Casting the Future;https://www.youtube.com/watch?v=2CIcvB72dmk;License: Standard youtube license