Thickness of the plate is reduced from 40mm to 20mm by succesive cold rolling passes using identical rolls of diameter 600 mm. Assume that there is no change in width. If the coefficient of friction b/w the rolls and the workpiece is 0.1. Determine the minimum number of passes required?

Thickness of the plate is reduced from 40mm to 20mm by succesive cold rolling passes using identical rolls of diameter 600 mm. Assume that there is no change in width. If the coefficient of friction b/w the rolls and the workpiece is 0.1. Determine the minimum number of passes required?

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Related questions

Q: A piece with a height of 120 mm and a diameter of 75 mm can be increased to 80 mm in height by…

A: Permissible stress is stress which produces due to pressure or forces which does not exceed the…

Q: In a rolling operation using a roll of diameter 1.5 m, if a 35 mm thick plate cannot be reduced to…

A: Given data: - The diameter of the roll is D = 1.5 m. The maximum possible reduction is t' = 12 mm.…

Q: A 300-mm-wide strip 25-mm thick is fed through a rolling mill with two powered rolls each of radius…

A: The answer has been attached in the form of images as follows:

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: Fib the time period, if pure rolling is the condition

A: Given data: Roller connected to spring is released from the inclined plane To determine: Time…

Q: A 300 mm thick slab is being cold rolled using roll of 600 mm diameter. If the coefficient of…

A: Given, Thickness of slab=300mm Diameter of roller,D=600mm Radius of roller, R=300mm Coefficient of…

Q: Drawing: A round rod of annealed 302 stainless steel (K = 1300 MPa and n = 0.3) is being drawn from…

A: Given:To find:

Q: A cylindrical working part is subjected to a forging landfall operation. The blank is 3.0 in. high…

A: volume of workpiece=π4×22×3=9.4247 in3

Q: A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that…

Q: Question 2. It is reduced to 80 mm with forging by stacking a part with a height of 120 mm and a…

Q: 1. What process is flexible and is widely used for bending plates for applications such as boilers,…

Q: - 400 mm wide 25 mm thick strip is fed through a rolling mill with two powered olls each of radius…

Q: In rolling process, calculate the applied torque in (N.m) when w= 600mm, K = 275 MPa, n = 0.10, %3D…

A: Given Data W=600 mm K=275 MPa n=0.1 ho=35 mm hf=29 mm R=373.3 mm

Q: A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a…

Q: Thickness of the sheet produced in a single pass.

A: Given data; Thickness, t=6 mmDiameter,D=200 mmGiven is diameter rolls to reduce thickness without…

Q: In a rolling operation using rolls of diameter 500 mm, if a 25 mm thick plate cannot be reduced to…

A: H=25-20 mm=5 mm R=250 mm Maximum draft for successful rolling per pass is given by, H=μ2R5 =…

Q: A 40 mm thick plate made from 410 grade stainless steel is to be reduced to 34 mm in one pass in a…

Q: Two parallel shafts 1 & 2, 11 cm. apart and rotating at 75 RPM and 200 RPM are connected by…

A: To Find : The diameter of the cylinder when they turn in opposite direction.Given : The distance…

Q: Compare the force required to draw (25mm×6mm) capper strip to 45% reduction of area with that…

Q: A cold rolling operation is to be used to reduce a 50 mm thick and 200 mm wide copper plate. The…

A: given; initial thickness(h1)=50mminitial width(w1)=200mmentry velocity(v1)=15m/minexi…

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: A solid cylinder of diameter 100 mm and height 50 mm is forged between two frictionless flat dies to…

A: Given:Diameter of solid cylinder, d1=100 mmHeight of solid cylinder, h1=50 mmFinal height of solid…

Q: Estimate the power for annealed low carbon steel strip 200 mm wide and 10 mm thick, rolled to a…

A: Rolling is a metal forming process in which a material is plastically deformed by passing it between…

Q: the work metal has a flow curve defined by K=300MPa and n=0.2, and the coefficient of friction…

Concept explainers

Forming and Shaping

Metal forming is a category of metalworking process through which the material can be given the desired shape and size by subjecting it to plastic deformation, where the component undergoes bulk deformation process upon application of loads. Unlike the shearing and machining process, the material does not undergo up to a failure point as indicated in the stress-strain curve. Hence, the stresses induced during the forming process are greater than yield strength but less than the failure strength of the material. The process does not lead to the loss of material, so it can be said to be an economical process. During forming, the material is subjected to tensile forces, compressive forces, bending, and shearing loading conditions. The material should possess the property of ductility to undergo the forming process.

Question

Thickness of the plate is reduced from 40mm to 20mm
by succesive cold rolling passes using identical rolls of
diameter 600 mm. Assume that there is no change in
width. If the coefficient of friction b/w the rolls and the
workpiece is 0.1.
Determine the minimum number of passes required?

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Step by step

Solved in 2 steps with 3 images

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Note:- • Do not provide handwritten solution. Maintain accuracy and quality in your answer. Take care of plagiarism. • Answer completely. • You will get up vote for sure.
In rolling process 40mm thick plate is rolled to 20mm in two high rolling mills. Roll diameter is 200mm the angle of contact is 15degree. Determine no of roll passes required to obtain final desires thickness
Would you kindly answer this question A rolling operation on a 250 mm wide, 8 mm thick, 1112 cold rolled steel takes place using hardened steel rolls with a surface finish of 0.03 μm. The rolls have a diameter of 350 mm and rotates at 115 rpm. The final thickness of the plate is 6 mm and the entry speed of the plate is 1.8 m/s. Calculate: 3.1 The minimum coefficient of friction required, that will make the rolling operation possible. 3.2 The required roll force. 3.3 The position of the neutral point, ?? 3.4 Indicate, using a sketch, the neutral point showing all relevant notation and dimensions.
A strip (300x30 mm) is fed through a rolling mill with two powered rolls (each with radius of 300 mm) rotating at the speed of 60 rpm. The flow stress of work material is 90 MPa, and the coefficient of friction between rolls and work is 0.12. For a single rolling operation performed at the contact angle of 6.28°, calculate the followings:a) Work thickness after rolling (in mm)
Maximum reduction in thickness for one pass in rolling process is Ahmas that can be expressed by Ah = u'R, where u is coefficient between contact surfaces and R is roller radius. Then, angle subtended by the deformation zone for u =0.1 (in degree) is friction max
A circular shape blank will be cut of 105 mm diameter from a strip of 3.3 mm with a clearance value of 0.25 mm. Take the shear strength as 400 MPa. Determine The appropriate punch diameter. Blanking force. Blanking force when the blade angle is 5.5
I need the answer as soon as possible
Note:- • Do not provide handwritten solution. Maintain accuracy and quality in your answer. Take care of plagiarism. • Answer completely. • You will get up vote for sure.
Second problem only. Read and Solve carefully, make sure readable if it is in hand written form, include the units in every step and draw the diagram. Your work will be appreaciated much. Thanks! See attached figure for the problem.